Method of producing partially hydrolyzed acrylamide polymers
Assignee: Kyoritsu Yuki Co Ltd
•
Filing: 1977-06-29
•
Granted: 1979-03-27
•
Expires: 1997-06-29
Abstract
Abstract Acrylamide polymers or copolymers are partially hydrolyzed by mixing the particles of hydrous gel of the polymer in an apparatus which has a mixing mechanism comprising of blades having a blank space and the face of the apparatus where the polymer is contacted with is made of or coated with synthetic resin.
Inventors
- 👤 Atsuo Tago
- 👤 Hiroyuki Kudomi
- 👤 Yasuyuki Nakanishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:03
CPC Classifications
B; B01; B01J; B01J19/00; B01J19/0053; B01J19/0066; B01F; B01F27/00; B01F27/05; B01F27/07; B01F27/072; B01F27/0727; B01F27/11; B01F27/114; B01J19/02; B01J19/18; B01J19/20; C; C08; C08F; C08F8/00; C08F8/44; B01J2219/00; B01J2219/02; B01J2219/0204; B01J2219/0245; C08F2800/00; C08F2800/20
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
145 words
A method of partially and uniformly hydrolyzing acrylamide polymer in gel form having a water content of from 65 to 90 wt.% which comprises: (a) dividing said acrylamide polymer to particle size of less than 10 mm; and (b) subsequently admixing said finely divided acrylamide polymer with an alkaline material in a mixing apparatus wherein: (i) the surfaces in contact with said acrylamide polymer particles are formed of or coated with a synthetic resin; (ii) the mixing mechanism comprises blades or flights having a blank space; (iii) the clearance between the apparatus body wall and the blade is 2 to 5 times the polymer particle size; (iv) the width of blade is 3 to 8 times the polymer particle size; and (v) the space ratio of the blade ##EQU2## is greater than 5%, to hydrolyze a portion of the amide groups on said acrylamide polymer.
Claim 2
Independent Claim
145 words
A method of partially and uniformly hydrolyzing acrylamide polymer in gel form having a water content of from 65 to 90 wt.% which comprises: (a) dividing said acrylamide polymer to particle size of less than 10 mm; and (b) subsequently admixing said finely divided acrylamide polymer with an alkaline material in a mixing apparatus wherein: (i) the surfaces in contact with said acrylamide polymer particles are formed of or coated with a synthetic resin; (ii) the mixing mechanism comprises blades or flights having a blank space; (iii) the clearance between the apparatus body wall and the blade is 2 to 5 times the polymer particle size; (iv) the width of blade is 3 to 8 times the polymer particle size; and (v) the space ratio of the blade ##EQU2## is greater than 5%, to hydrolyze a portion of the amide groups on said acrylamide polymer.
Claim 3
Dependent Claim
30 words
The method as set forth in claim 1, wherein the synthetic resin forming or coating the surface of the apparatus to be contacted with the polymer particles is fluorocarbon resin.
Claim 4
Dependent Claim
18 words
The method as set forth in claim 1, wherein the mixing mechanism is a double helical ribbon blade.
Claim 5
Dependent Claim
22 words
The method as set forth in claim 1, wherein the polymer particle size is within the range of 2 to 5 mm.
Claim 6
Dependent Claim
15 words
The method as set forth in claim 1, wherein the alkaline material is caustic soda.
Claim 7
Dependent Claim
52 words
The method as set forth in claim 1, wherein the mixing apparatus is of a horizontal type and so constructed that the polymer particles are transferred from one end thereof to the other and that an aqueous solution of an alkaline material is sprayed to the polymer particles during said transfer thereof.
Claim 8
Dependent Claim
19 words
The method as set forth in claim 1, wherein the obtained partially hydrolyzed polymer particles are dried under heating.
Claim 9
Dependent Claim
29 words
The method as set forth in claim 7, wherein drying under heating is accomplished under normal pressure or reduced pressure and at a temperature of 40° to 100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-26 | 1982-09-25 | 1983-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-26 | 1986-09-25 | 1987-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-26 | 1990-09-25 | 1991-03-27 | $7700.00 | Window Closed / Lapsed |