Process for producing catalyst components for olefin polymerization
Assignee: Mitsubishi Chemical Corp
•
Filing: 1977-10-06
•
Granted: 1979-03-27
•
Expires: 1997-10-06
Abstract
Abstract A catalyst component, which is to be combined with an organoaluminum component to form a Ziegler catalyst for olefin polymerization, is produced by treating (1) a solid composition resulting from a process of combining a magnesium halide such as magnesium chloride, an electron donor compound such as ethyl benzoate and a titanium halogen compound such as titanium tetrachloride with (2) an interhalogen compound or a halogen such as iodine trichloride.
Inventors
- 👤 Masuzo Yokoyama
- 👤 Shoichi Masukawa
- 👤 Tsunenori Takahashi
- 👤 Hideo Sakurai
- 👤 Makoto Kouno
- 👤 Shozo Ohkosi
- 👤 Satosi Ohtaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:31
CPC Classifications
C; C08; C08F; C08F4/00; C08F4/02; C08F4/022; C08F10/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
79 words
In a process for producing a catalyst component for polymerization of olefins in which a solid composition for said catalyst component is prepared by combining a magnesium halide, an electron donor compound, and a titanium halogen compound, the improvement which comprises contacting said solid composition with a member selected from the group consisting of interhalogen compounds and halogens in a mole ratio of about 0.001 to 20:1 of said interhalogen compound or halogen relative to said titanium halogen compound.
Claim 2
Dependent Claim
79 words
In a process for producing a catalyst component for polymerization of olefins in which a solid composition for said catalyst component is prepared by combining a magnesium halide, an electron donor compound, and a titanium halogen compound, the improvement which comprises contacting said solid composition with a member selected from the group consisting of interhalogen compounds and halogens in a mole ratio of about 0.001 to 20:1 of said interhalogen compound or halogen relative to said titanium halogen compound.
Claim 3
Dependent Claim
27 words
A process as claimed in claim 1 in which the solid composition, after being thus contacted with said selected member, is washed with an inactive organic solvent.
Claim 4
Dependent Claim
37 words
A process as claimed in claim 1 in which the contact of the solid composition with said selected member comprises causing the solid composition and said selected member to contact each other in an inactive organic solvent.
Claim 5
Dependent Claim
16 words
A process as claimed in claim 2 in which the inactive organic solvent is a halohydrocarbon.
Claim 6
Dependent Claim
16 words
A process as claimed in claim 3 in which the inactive organic solvent is a halohydrocarbon.
Claim 7
Dependent Claim
38 words
A process as claimed in claim 1 in which said process of combining a magnesium halide, an electron donor compound, and a titanium halogen compound includes a step of grinding together at least two of the stated components.
Claim 8
Dependent Claim
37 words
A process as claimed in claim 1 in which the electron donor compound is an ester of a carboxylic acid having from 1 to 12 carbon atoms and an alcohol having from 1 to 12 carbon atoms.
Claim 9
Dependent Claim
28 words
A process as claimed in claim 7 in which the ester is an ester of benzoic acid and a monohydric alcohol having from 1 to 12 carbon atoms.
Claim 10
Dependent Claim
57 words
A process as claimed in claim 1 in which the titanium halogen compound is defined by the formula Ti (OR) m X n-m wherein R is an alkyl group; X is a halogen; n is 3 or 4; m is zero or an integer from 1 to 4; and n is equal to or greater than m.
Claim 11
Dependent Claim
27 words
A process as claimed in claim 9 in which the titanium halogen compound is a member selected from the group consisting of titanium tetrachloride and titanium trichloride.
Claim 12
Dependent Claim
49 words
A process as claimed in claim 1 in which the mole ratio of the magnesium halide to the electron donor compound to the titanium halogen compound to the interhalogen compound or halogen is (from 1,000 to 3) to (from 10 to 0.1) to 1 to (from 0.001 to 20).
Claim 13
Dependent Claim
114 words
A process as claimed in claim 1 in which the solid composition is prepared by the process steps of: (1) contacting the magnesium halide with the electron donor compound thereby to produce a first composition containing the magnesium halide; (2) grinding said first composition together with the titanium halogen compound in liquid substantially in the absence of a solvent thereby to produce a ground second composition containing the magnesium halide; (3) contacting said second composition with said member selected from the group consisting of interhalogen compounds and halogens; and (4) washing the second composition containing the magnesium halide with an inactive organic solvent at the same time as or after the above step (3).
Claim 14
Dependent Claim
28 words
A process as claimed in claim 12 in which the step (1) comprises grinding the magnesium halide and the electron donor compound in the absence of a solvent.
Claim 15
Dependent Claim
34 words
A process as claimed in claim 12 in which the step (1) comprises heating the magnesium halide and the electron donor compound in an inactive solvent at a temperature of 60° to 150° C.
Claim 16
Dependent Claim
25 words
A process as claimed in claim 12 in which the washing of the step (4) comprises extracting of the titanium content of the second composition.
Claim 17
Dependent Claim
14 words
A catalyst component for polymerization of olefins obtained by the process of claim 1.
References Cited (Backward Citations)
US3206447A
Cited
US3223694A
Cited
US3524840A
Cited
US3953414A
Cited
US3859231A
Cited
US3972862A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-26 | 1982-09-25 | 1983-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-26 | 1986-09-25 | 1987-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-26 | 1990-09-25 | 1991-03-27 | $7700.00 | Window Closed / Lapsed |