Abstract Styrene is copolymerized with maleic anhydride by mixing maleic anhydride with styrene under mass polymerization conditions in a ratio of styrene to maleic anhydride of at least 5:1, continuing to add maleic anhydride throughout a mass polymerization stage until about 25% to about 40% of the styrene monomer is reacted to produce a reaction mass in which the polymerized maleic anhydride is about 1% to about 10% of the total reaction mass. The polymerization is then completed in a pH-adjusted free-radical initiated suspension stage, which generates homopolymer of styrene. During the suspension stage about 10% to about 20% of the bound maleic anhydride is hydrolyzed. The acid component of the bound maleic acid may be converted back to the anhydride through the use of a vented extruder.
Method of making a mixture of polystyrene and a copolymer of styrene and maleic anhydride comprising (a) mixing together under mass polymerization conditions styrene and maleic anhydride in a ratio of at least 5:1 and at rates such that maleic anhydride is not added at a rate greater than the rate at which the styrene polymerizes under the current polymerization conditions, until about 25% to about 40% of the monomers are polymerized, to produce a reaction mass containing polymerized maleic anhydride in an amount comprising from about 1% to about 10% of the total reaction mass, (b) suspending the reaction mass in water, adjusting the pH of the suspension to between about 4.5 and about 7.0, and carrying the styrene polymerization reaction to completion with the aid of a free-radical initiator to form beads of polymer product.
Claim 2
Dependent Claim
137 words
Method of making a mixture of polystyrene and a copolymer of styrene and maleic anhydride comprising (a) mixing together under mass polymerization conditions styrene and maleic anhydride in a ratio of at least 5:1 and at rates such that maleic anhydride is not added at a rate greater than the rate at which the styrene polymerizes under the current polymerization conditions, until about 25% to about 40% of the monomers are polymerized, to produce a reaction mass containing polymerized maleic anhydride in an amount comprising from about 1% to about 10% of the total reaction mass, (b) suspending the reaction mass in water, adjusting the pH of the suspension to between about 4.5 and about 7.0, and carrying the styrene polymerization reaction to completion with the aid of a free-radical initiator to form beads of polymer product.
Claim 3
Dependent Claim
14 words
Method of claim 1 including the step of separating the beads from the water.
Claim 4
Dependent Claim
21 words
Method of claim 1 followed by passing the beads through a vented extruder to convert acid groups to the anhydride form.