US4145263A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Steel sheet useful in forming foodstuff and beverage cans
Assignee: Toyo Kohan Co Ltd
•
Filing: 1977-08-12
•
Granted: 1979-03-20
•
Expires: 1997-08-12
Abstract
Abstract A steel sheet is provided herein which has been treated to form thereon a first very thin layer of tin and a second layer of hydrated chromium oxide. This treated steel sheet can effectively be coated with an organic coating, and can be used for producing cans for foodstuffs and carbonated beverages.
Inventors
- 👤 Nobuyuki Tsutsui
- 👤 Tsuneo Inui
- 👤 Hiroaki Kawamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 00:17
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/38; C25D3/00; C25D3/02; C25D3/30
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
160 words
A process for producing a steel sheet containing a first layer of tin and a second layer of hydrated chromium oxide, which consists essentially of electrolytically tin plating a substantially clean steel sheet base in an electrolyte containing stannous sulfate, stannous chloride, stannous fluoborate, sodium stannate or potassium stannate, to obtain a tin plated steel sheet in which the amount of plated tin is 0.05-0.60 g/m 2 , subjecting the resultant steel sheet to an electrolytic treatment at 5-20 coulombs/dm 2 under 5-50 A/dm 2 of current density in an electrolyte containing chromic acid and at least one member selected from the group consisting of sulfuric acid, a fluorine compound, an aromatic disulfonic acid and thiourea, to form a second layer consisting essentially of hydrated chromium oxide in an amount of 0.005 to 0.05 g/m 2 calculated as chromium, any metallic chromium deposited between said first and second layers being present in an amount less than 0.005 g/m 2 .
Claim 2
Dependent Claim
160 words
A process for producing a steel sheet containing a first layer of tin and a second layer of hydrated chromium oxide, which consists essentially of electrolytically tin plating a substantially clean steel sheet base in an electrolyte containing stannous sulfate, stannous chloride, stannous fluoborate, sodium stannate or potassium stannate, to obtain a tin plated steel sheet in which the amount of plated tin is 0.05-0.60 g/m 2 , subjecting the resultant steel sheet to an electrolytic treatment at 5-20 coulombs/dm 2 under 5-50 A/dm 2 of current density in an electrolyte containing chromic acid and at least one member selected from the group consisting of sulfuric acid, a fluorine compound, an aromatic disulfonic acid and thiourea, to form a second layer consisting essentially of hydrated chromium oxide in an amount of 0.005 to 0.05 g/m 2 calculated as chromium, any metallic chromium deposited between said first and second layers being present in an amount less than 0.005 g/m 2 .
Claim 3
Dependent Claim
32 words
A process for producing a steel sheet according to claim 1, wherein the electrolytic tin plating step is performed in an acidic electrolyte at a current density of 5-50 A/dm 2 .
Claim 4
Dependent Claim
34 words
A process for producing a steel sheet according to claim 1, wherein the electrolytic tin plating step is performed by use of an alkaline electrolyte at a current density of 1-10 A/dm 2 .
Claim 5
Dependent Claim
138 words
A process for producing a steel sheet containing a first layer of tin and a second layer of hydrated chromium oxide, which consists essentially of electrolytically tin plating a substantially clean steel sheet base in an electrolyte containing stannous sulfate, stannous chloride, stannous fluoborate, sodium stannate or potassium stannate, to obtain a tin plated steel sheet in which the amount of plated tin is 0.05-0.60 g/m 2 , and subjecting the resultant steel sheet to an electrolytic treatment at 8-140 coulombs/dm 2 under 5-40 A/dm 2 of current density in an electrolyte containing sodium dichromate, to form a second layer consisting of hydrated chromium oxide in an amount of 0.005 to 0.05 g/m 2 calculated as chromium, any metallic chromium deposited between said first and second layers being present in an amount less than 0.005 g/m 2 .
Claim 6
Dependent Claim
138 words
A process for producing a steel sheet containing a first layer of tin and a second layer of hydrated chromium oxide, which consists essentially of electrolytically tin plating a substantially clean steel sheet base in an electrolyte containing stannous sulfate, stannous chloride, stannous fluoborate, sodium stannate or potassium stannate, to obtain a tin plated steel sheet in which the amount of plated tin is 0.05-0.60 g/m 2 , and subjecting the resultant steel sheet to an electrolytic treatment at 8-140 coulombs/dm 2 under 5-40 A/dm 2 of current density in an electrolyte containing sodium dichromate, to form a second layer consisting of hydrated chromium oxide in an amount of 0.005 to 0.05 g/m 2 calculated as chromium, any metallic chromium deposited between said first and second layers being present in an amount less than 0.005 g/m 2 .
Claim 7
Dependent Claim
32 words
A process for producing a steel sheet according to claim 4, wherein the electrolytic tin plating step is performed in an acidic electrolyte at a current density of 5-50 A/dm 2 .
Claim 8
Dependent Claim
32 words
A process for producing a steel sheet according to claim 4, wherein the electrolytic tin plating step is performed in an alkaline electrolyte at a current density of 1-10 A/dm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-19 | 1982-09-18 | 1983-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-19 | 1986-09-18 | 1987-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-19 | 1990-09-18 | 1991-03-20 | $7700.00 | Window Closed / Lapsed |