Process for making a precursor of a solution of cellulose
Assignee: Akzona Inc
•
Filing: 1977-07-26
•
Granted: 1979-03-06
•
Expires: 1997-07-26
Abstract
Abstract A process is provided for making a solid precursor of a solution of cellulose in a tertiary amine oxide by suspending cellulose in a mixture containing a tertiary amine oxide and water under conditions where the amine oxide will dissolve the cellulose and cooling the resulting product to ambient temperature to provide a solid solution of cellulose in amine oxide. The product may be comminuted to form chips which are adapted to be fed to an extruder or other apparatus for shaping it into a cellulosic article. An organic liquid which is miscible with the tertiary amine oxide and is a non-solvent for the cellulose may be included with the amine oxide-water mixture to improve the up-take of the tertiary amine oxide by the cellulose.
Inventors
- 👤 Clarence C. McCorsley, III
- 👤 Julianna K. Varga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:36
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/091; C08J3/096; C08B; C08B1/00; C08B1/003; C08J2301/00; C08J2301/02
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
69 words
A process for making a solid precursor of a solution of cellulose in a tertiary amine oxide which comprises dissolving cellulose in a tertiary amine oxide solvent for cellulose containing a non-solvent for the cellulose compatible with said amine oxide solvent at a temperature where a liquid solution is obtained and cooling the solution until it solidifies to form a solid cellulosic product containing absorbed amine oxide and non-solvent.
Claim 2
Dependent Claim
69 words
A process for making a solid precursor of a solution of cellulose in a tertiary amine oxide which comprises dissolving cellulose in a tertiary amine oxide solvent for cellulose containing a non-solvent for the cellulose compatible with said amine oxide solvent at a temperature where a liquid solution is obtained and cooling the solution until it solidifies to form a solid cellulosic product containing absorbed amine oxide and non-solvent.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein the said solid solution is comminuted to form cellulose chips adapted to be fed to an extruder.
Claim 4
Dependent Claim
10 words
The process of claim 1 wherein the non-solvent is water.
Claim 5
Dependent Claim
13 words
The process of claim 1 wherein the non-solvent is a water-organic non-solvent mixture.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein the tertiary amine oxide is N-methylmorpholine oxide.
Claim 7
Dependent Claim
13 words
The process of claim 1 wherein the tertiary amine oxide is dimethylcyclohexylamine oxide.
Claim 8
Dependent Claim
13 words
The process of claim 1 wherein the tertiary amine oxide is dimethylethanolamine oxide.
Claim 9
Dependent Claim
38 words
The process of claim 1 wherein the product contains from about 90% to about 50% by weight tertiary amine oxide, from 2% to 15% percent by weight water and from about 10% to about 35% by weight cellulose.
Claim 10
Dependent Claim
103 words
A process for making a precursor of a solution of cellulose in a tertiary amine oxide which comprises suspending cellulose in a mixture containing an amine oxide, water, and an organic liquid, which is miscible with the amine oxide and water and is non-solvent for cellulose at a temperature at which the cellulose dissolves, until a solution of cellulose is obtained, removing the organic liquid therefrom, and thereafter cooling the solution to provide a solid solution containing cellulose and absorbed amine oxide and water which is capable of becoming a solution of cellulose when heated without further addition of solvent for the cellulose.
Claim 11
Dependent Claim
103 words
A process for making a precursor of a solution of cellulose in a tertiary amine oxide which comprises suspending cellulose in a mixture containing an amine oxide, water, and an organic liquid, which is miscible with the amine oxide and water and is non-solvent for cellulose at a temperature at which the cellulose dissolves, until a solution of cellulose is obtained, removing the organic liquid therefrom, and thereafter cooling the solution to provide a solid solution containing cellulose and absorbed amine oxide and water which is capable of becoming a solution of cellulose when heated without further addition of solvent for the cellulose.
Claim 12
Independent Claim
111 words
A method for making a solid chip containing cellulose adapted to be melted and shaped comprising preparing a slurry containing cellulose and a mixture of a tertiary amine oxide solvent for the cellulose and a non-solvent for the cellulose containing water in an amount which improves the intimate association of the tertiary amine oxide and cellulose fibers, heating the slurry to dissolve the cellulose in the tertiary amine oxide and applying vacuum to remove any non-aqueous non-solvent, thereafter cooling the solution to form a solid solution of cellulose in tertiary amine oxide and water, and comminuting the product to form chips adapted for feeding to an extruder or similar processing equipment.
Claim 13
Independent Claim
111 words
A method for making a solid chip containing cellulose adapted to be melted and shaped comprising preparing a slurry containing cellulose and a mixture of a tertiary amine oxide solvent for the cellulose and a non-solvent for the cellulose containing water in an amount which improves the intimate association of the tertiary amine oxide and cellulose fibers, heating the slurry to dissolve the cellulose in the tertiary amine oxide and applying vacuum to remove any non-aqueous non-solvent, thereafter cooling the solution to form a solid solution of cellulose in tertiary amine oxide and water, and comminuting the product to form chips adapted for feeding to an extruder or similar processing equipment.
Claim 14
Dependent Claim
32 words
The method of claim 10 wherein the non-solvent is a mixture of an organic non-solvent and water and the organic non-solvent is removed as the cellulose dissolves in the tertiary amine oxide.
Claim 15
Dependent Claim
98 words
A process for making a solid cellulose product which is adapted to form a solution of cellulose by heating the said product alone, said process comprising dispersing cellulose in a liquid containing a tertiary amine oxide solvent for cellulose and a non-solvent for cellulose, dissolving the cellulose in said liquid mixture, and cooling the resulting solution until solidification to form a solid cellulosic product containing absorbed tertiary amine oxide solvent and water in an amount which will not dissolve the cellulose at ambient temperatures but is adapted to dissolve the cellulose when heated to form a shapeable solution.
Claim 16
Dependent Claim
98 words
A process for making a solid cellulose product which is adapted to form a solution of cellulose by heating the said product alone, said process comprising dispersing cellulose in a liquid containing a tertiary amine oxide solvent for cellulose and a non-solvent for cellulose, dissolving the cellulose in said liquid mixture, and cooling the resulting solution until solidification to form a solid cellulosic product containing absorbed tertiary amine oxide solvent and water in an amount which will not dissolve the cellulose at ambient temperatures but is adapted to dissolve the cellulose when heated to form a shapeable solution.
Claim 17
Dependent Claim
8 words
The product of the process of claim 10.
Claim 18
Dependent Claim
8 words
The product of the process of claim 12.
References Cited (Backward Citations)
US3447956A
Cited
US3508941A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-05 | 1982-09-04 | 1983-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-05 | 1986-09-04 | 1987-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-05 | 1990-09-04 | 1991-03-06 | $7700.00 | Window Closed / Lapsed |