Corrosion preventive, coated metal pipe
Assignee: Nippon Steel Corp
•
Filing: 1977-11-15
•
Granted: 1979-03-06
•
Expires: 1997-11-15
Abstract
Abstract There are applied in layers on the surface of a metal pipe, a rapid hardening and cure type corrosion preventive material consisting essentially of isocyanate terminated polyurethane prepolymer, amine base hardener and petroleum resin, and a reinforcing material consisting of silica sand, blast furnace slag or the like. Thus there are provided a plurality of coatings or layers on the metal pipe, which are excellent in impact resisting and corrosion preventive properties.
Inventors
- 👤 Jiro Satake
- 👤 Tetsuzo Arai
- 👤 Yoshifumi Miyamoto
- 👤 Hiroo Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 00:10
CPC Classifications
F; F16; F16L; F16L58/00; F16L58/02; F16L58/04; F16L58/10; F16L58/1054; F16L58/1072; Y; Y10; Y10S; Y10S138/00; Y10S138/06; Y10S138/07
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
126 words
In metal pipes coated with layers of corrosion preventive material and reinforcing material selected from the group consisting of silica sand, blast furnace slag, and synthetic or natural resin of a solid particle type, wherein the improvement comprises a corrosion preventive material containing: (1) a first ingredient consisting essentially of isocyanate terminated polyurethane prepolymer formed from the reaction of polyether polyol with poly-isocyanate, and (2) a second ingredient consisting essentially of (i) amine base hardener and (ii) petroleum resin formed by heating and polymerizing the fraction of distillate of an unsaturated petroleum base hydrocarbon in the presence of a suitable catalyst, the carbon number of said hydrocarbon being essentially C 4 to C 5 , said first ingredient and second ingredient being mixed prior to coating.
Claim 2
Dependent Claim
126 words
In metal pipes coated with layers of corrosion preventive material and reinforcing material selected from the group consisting of silica sand, blast furnace slag, and synthetic or natural resin of a solid particle type, wherein the improvement comprises a corrosion preventive material containing: (1) a first ingredient consisting essentially of isocyanate terminated polyurethane prepolymer formed from the reaction of polyether polyol with poly-isocyanate, and (2) a second ingredient consisting essentially of (i) amine base hardener and (ii) petroleum resin formed by heating and polymerizing the fraction of distillate of an unsaturated petroleum base hydrocarbon in the presence of a suitable catalyst, the carbon number of said hydrocarbon being essentially C 4 to C 5 , said first ingredient and second ingredient being mixed prior to coating.
Claim 3
Dependent Claim
24 words
A corrosion preventive, coated metal pipe as set forth in claim 1, wherein the lowermost layer of said coating is a corrosion preventive material.
Claim 4
Dependent Claim
33 words
A corrosion preventive, coated metal pipe as set forth in claim 1, wherein the lowermost layer of said coatings is a corrosion preventive material and the layer thereabove is a reinforcing material layer.
Claim 5
Dependent Claim
42 words
A corrosion preventive coated metal pipe, as set forth in claim 1, wherein the lowermost layer of said coatings is a corrosion preventive material, the layer thereabove is a reinforcing material layer, and the layer still thereabove is a corrosion preventive material.
Claim 6
Dependent Claim
29 words
A corrosion preventive coated metal pipe as set forth in claim 1, wherein primer coating is present between the surface of said metal pipe and a coating applied thereto.
Claim 7
Dependent Claim
39 words
A corrosion preventive coated metal pipe as set forth in claim 1, wherein said isocyanate terminated polyurethane prepolymer contains isocyanate radical in an amount of 3 to 10 weight % and has the molecular weight of 800 to 1700.
Claim 8
Dependent Claim
44 words
A corrosion preventive coated metal pipe as set forth in claim 1, wherein said second ingredient 25 to 38 weight parts of amine base hardener, and 25 to 40 weight parts of petroleum resin, per 100 parts by weight of isocyanate terminated polyurethane prepolymer.
Claim 9
Dependent Claim
45 words
A corrosion preventive, coated metal pipe as set forth in claim 1, wherein said second ingredient contains 1 to 15 parts by weight of pigment, and 20 to 45 parts by weight of filler material, per 100 parts by weight of isocyanate terminated polyurethane prepolymer.
Claim 10
Dependent Claim
39 words
A corrosion preventive coated metal pipe as set forth in claim 1, wherein said powdered blast furnace slag is made by cooling, solidifying slag from a blast furnace and crushing same into 10 to 150 meshes in a crusher.
Claim 11
Dependent Claim
30 words
A corrosion preventive, coated metal pipe as set forth in claim 1, wherein scales on a metal pipe are removed, and/or the surface of said metal pipe are shot-blasted, beforehand.
Claim 12
Dependent Claim
37 words
A corrosion preventive coated metal pipe, as set forth in claim 1, wherein the uppermost layer of coatings is a cloth impregnated with said corrosion preventive material for protection of the outer surface of the metal pipe.
Claim 13
Dependent Claim
21 words
A corrosion preventive, coated metal pipe as set forth in claim 11, wherein said cloth is a glass cloth or jute.
Claim 14
Dependent Claim
35 words
A corrosion preventive coated metal pipe as set forth in claim 1, wherein the uppermost layer of said coatings consists of a sheet or tape for protection of the outer surface of the metal pipe.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-05 | 1982-09-04 | 1983-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-05 | 1986-09-04 | 1987-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-05 | 1990-09-04 | 1991-03-06 | $7700.00 | Window Closed / Lapsed |