US4142006A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a high power laser mirror
Assignee: Westinghouse Electric Corp
•
Filing: 1976-02-27
•
Granted: 1979-02-27
•
Expires: 1996-02-27
Abstract
Abstract Method of making a high power laser mirror. Essentially the mirror consists of a refractory composition substrate which is polished to an optical finish and overcoated with a high reflectivity metal and a dielectric film disposed to cover the high reflectivity metal. The method includes the hot pressing of the refractory composition, especially silicon carbide, to form a substrate following which an optical finish is polished on one surface thereof. Thereafter, a metal film with a high reflectivity is applied to cover the optical surface and then a dielectric film is deposited over the high reflectivity metal film. Both films are deposited employing process of vacuum evaporation for deposition on the substrate. As thus combined, the mirror exhibits low optical absorptivity, high thermal conductivity, low weight, and low coefficient of thermal expansion. Since the substrate is formed of a hard refractory composition, an excellent optical finish can be polished on the surface thereof.
Inventors
- 👤 Wolfgang J. Choyke
- 👤 Richard A. Hoffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:20
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/08; G02B5/0816; G02B5/085; G02B5/0858; G02B5/0891; G02B7/00; G02B7/18; G02B7/181; G02B7/1815; H; H01; H01S; H01S3/00; H01S3/02; H01S3/04; H01S3/0401; H01S3/0407; Y; Y10; Y10S; Y10S359/00; Y10S359/90
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
126 words
The method for producing a high power laser mirror, the steps comprising forming a substrate of a refractory composition having a thermal conductivity of at least 2 watts/cm° K., a thermal expansion coefficient of less than 5 × 10 -6 /° C., a hardness of at least 9 MOH and a density of less than 4 gm/cm 3 , said material having a density in excess of about 99% of theoretical density, polishing an optical surface on at least one surface of the substrate, depositing a film of a high reflectivity metal on the optical surface, said film having a thickness not in excess of 8,000 angstroms, and depositing a transparent dielectric film of less than 2,000 angstroms in thickness over the metal of high reflectivity.
Claim 2
Independent Claim
126 words
The method for producing a high power laser mirror, the steps comprising forming a substrate of a refractory composition having a thermal conductivity of at least 2 watts/cm° K., a thermal expansion coefficient of less than 5 × 10 -6 /° C., a hardness of at least 9 MOH and a density of less than 4 gm/cm 3 , said material having a density in excess of about 99% of theoretical density, polishing an optical surface on at least one surface of the substrate, depositing a film of a high reflectivity metal on the optical surface, said film having a thickness not in excess of 8,000 angstroms, and depositing a transparent dielectric film of less than 2,000 angstroms in thickness over the metal of high reflectivity.
Claim 3
Dependent Claim
43 words
The method of claim 1 in which the polishing is interrupted, a metallic layer of up to 1,000 angstroms in thickness is placed on the surface of the refractory composition undergoing polishing, and thereafter the polishing is continued for producing an optical surface.
Claim 4
Dependent Claim
14 words
The method of claim 1 in which the films are deposited by vacuum evaporation.
Claim 5
Dependent Claim
25 words
The method of claim 1 in which the refractory composition substrate is selected from the group consisting of silicon carbide, silicon nitride and mixtures thereof.
Claim 6
Dependent Claim
23 words
The method of claim 1 in which the metal of high reflectivity is selected from the group consisting of silver, gold, and copper.
Claim 7
Dependent Claim
13 words
The method of claim 1 in which the dielectric film is lanthanum fluoride.
Claim 8
Dependent Claim
26 words
The method of claim 1 in which the deposition rate is within the range between about 200 angstroms per second and about 3,000 angstroms per second.
Claim 9
Independent Claim
142 words
The method of producing a high power laser mirror, the steps comprising hot pressing a silicon carbide substrate to achieve a density in the substrate in excess of 99% of the theoretical density of silicon carbide, said silicon carbide having a thermal conductivity of at least two watts per centimeter degrees K., a thermal expansion of less than 5 × 10 -6 /° C. and a hardness of at least 9 MOH, polishing an optical surface on at least one surface of the substrate by lapping the same while employing a 1/4 micron diamond abrasive, applying to the optical surface a layer of silver having a thickness of between 1,500 angstroms and 5,000 angstroms, and applying to the silver film thus deposited a dielectric film of lanthanum fluoride having a thickness within the range between about 500 angstroms and about 1,500 angstroms.
Claim 10
Independent Claim
142 words
The method of producing a high power laser mirror, the steps comprising hot pressing a silicon carbide substrate to achieve a density in the substrate in excess of 99% of the theoretical density of silicon carbide, said silicon carbide having a thermal conductivity of at least two watts per centimeter degrees K., a thermal expansion of less than 5 × 10 -6 /° C. and a hardness of at least 9 MOH, polishing an optical surface on at least one surface of the substrate by lapping the same while employing a 1/4 micron diamond abrasive, applying to the optical surface a layer of silver having a thickness of between 1,500 angstroms and 5,000 angstroms, and applying to the silver film thus deposited a dielectric film of lanthanum fluoride having a thickness within the range between about 500 angstroms and about 1,500 angstroms.
Claim 11
Dependent Claim
28 words
The method of claim 8 in which a chromium film having a thickness between about 100 angstroms and 500 angstroms is deposited between the substrate and silver film.
Claim 12
Dependent Claim
47 words
The method of claim 1 in which the substrate consists essentially of a base having a chemically vapor deposited coating of substantially pure silicon carbide having a thickness of up to about 1/8 inch, which coating is optically polished to a roughness of less than 10A RMS.
Claim 13
Independent Claim
107 words
The method of making a mirror suitable for use in the 500A to 1000A wavelength comprising forming a base of the desired configuration from a material selected from the group consisting of silicon carbide, silicon nitride, mixtures thereof and with additives such as silicon, aluminum or magnesium, said form base having a density of not less than 90% of theoretical chemically vapor depositing a layer of silicon carbide having a thickness of up to 1/8 inch on said base of the desired configuration, and thereafter polishing an optical surface on the chemically vapor deposited silicon carbide, said optical surface having a roughness of less than 10A R.M.S.
Claim 14
Independent Claim
107 words
The method of making a mirror suitable for use in the 500A to 1000A wavelength comprising forming a base of the desired configuration from a material selected from the group consisting of silicon carbide, silicon nitride, mixtures thereof and with additives such as silicon, aluminum or magnesium, said form base having a density of not less than 90% of theoretical chemically vapor depositing a layer of silicon carbide having a thickness of up to 1/8 inch on said base of the desired configuration, and thereafter polishing an optical surface on the chemically vapor deposited silicon carbide, said optical surface having a roughness of less than 10A R.M.S.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |