Assignee: Novartis Corp
•
Filing: 1977-05-16
•
Granted: 1979-02-27
•
Expires: 1997-05-16
Abstract
Abstract This invention relates to a process for the thermal decomposition of metal nitrates which decompose below a temperature of about 400° C. to form the corresponding metal oxide as well as oxides of nitrogen, said process involving distributing said nitrate over previously formed oxide and conducting said decomposition under "muffle" conditions such that said decomposition occurs in an atmosphere predominantly comprised of the vapors evolved during the thermal decomposition.
Inventors
- 👤 Ralph Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:06
CPC Classifications
C; C01; C01C; C01C3/00; C01C3/004; C01B; C01B13/00; C01B13/14; C01B13/18; C01B21/00; C01B21/20; C01B21/36; C01B21/38; C01B21/42; C01B7/00; C01B7/01; C01B7/03
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
145 words
A method for thermally decomposing a metal nitrate in a liquid phase to the corresponding metal oxide and a nitrogen dioxide-containing gaseous mixture, said metal nitrate having a decomposition temperature of less than about 400° C., said process comprising the steps of (1) introducing solid metal oxide particles coated with said metal nitrate liquid phase into a decomposition reactor, the metal of said oxide corresponding to the metal in the liquid phase; (2) raising the temperature of said coated particles above the decomposition temperature of said nitrate; (3) maintaining said coated patricles at a temperature above said decomposition temperature and in an atmosphere formed by the vapors evolved during said decomposition for a period of time sufficient to decompose said nitrate, the metal oxide decomposition product forming on and adhering to said particles; and (4) removing said metal oxide and said nitrogen dioxide-containing gaseous mixture.
Claim 2
Independent Claim
145 words
A method for thermally decomposing a metal nitrate in a liquid phase to the corresponding metal oxide and a nitrogen dioxide-containing gaseous mixture, said metal nitrate having a decomposition temperature of less than about 400° C., said process comprising the steps of (1) introducing solid metal oxide particles coated with said metal nitrate liquid phase into a decomposition reactor, the metal of said oxide corresponding to the metal in the liquid phase; (2) raising the temperature of said coated particles above the decomposition temperature of said nitrate; (3) maintaining said coated patricles at a temperature above said decomposition temperature and in an atmosphere formed by the vapors evolved during said decomposition for a period of time sufficient to decompose said nitrate, the metal oxide decomposition product forming on and adhering to said particles; and (4) removing said metal oxide and said nitrogen dioxide-containing gaseous mixture.
Claim 3
Dependent Claim
21 words
The method of claim 1, wherein said liquid phase of metal nitrate contains at least about 50%, by weight, of nitrate.
Claim 4
Dependent Claim
23 words
The method of claim 1, wherein the weight ratio of solids to liquid phase in said coated particles is at least about 3:1.
Claim 5
Dependent Claim
37 words
The method of claim 1, wherein said decomposition reactor is a fluidized bed of said oxide particles and at least a portion of said gaseous mixture is recycled to the decomposition reactor and comprises the fluidizing means.
Claim 6
Dependent Claim
78 words
The method of claim 1, wherein said decomposition reactor is a fluidized bed of said coated metal oxide particles, a portion of said nitrogen dioxide-containing gaseous mixture is the fluidizing means and the temperature of the particles in said bed is maintained above said decomposition temperature by immersing in said bed an extended area of heat transfer surface containing inner passages through which a heat transfer fluid is circulated at a temperature in excess of said decomposition temperature.
Claim 7
Independent Claim
117 words
A method for thermally decomposing manganous nitrate contained in a liquid phase to manganese dioxide and a nitrogen dioxide-containing gaseous mixture which comprises the steps of (1) introducing solid manganese dioxide particles coated with said manganous nitrate liquid phase into a decomposition reactor; (2) raising the temperature of said coated particles above about 180° C.; (3) maintaining said coated particles at said temperature in excess of about 180° C. and in an atmosphere formed by the vapors evolved during said decomposition for a period of time sufficient to decompose said manganous nitrate, the manganese dioxide decomposition product forming on and adhering to said manganese dioxide particles, and (4) removing manganese dioxide and said nitrogen dioxide-containing gaseous mixture.
Claim 8
Independent Claim
117 words
A method for thermally decomposing manganous nitrate contained in a liquid phase to manganese dioxide and a nitrogen dioxide-containing gaseous mixture which comprises the steps of (1) introducing solid manganese dioxide particles coated with said manganous nitrate liquid phase into a decomposition reactor; (2) raising the temperature of said coated particles above about 180° C.; (3) maintaining said coated particles at said temperature in excess of about 180° C. and in an atmosphere formed by the vapors evolved during said decomposition for a period of time sufficient to decompose said manganous nitrate, the manganese dioxide decomposition product forming on and adhering to said manganese dioxide particles, and (4) removing manganese dioxide and said nitrogen dioxide-containing gaseous mixture.
Claim 9
Dependent Claim
21 words
The method of claim 6, wherein said liquid phase of manganous nitrate contains at least about 50%, by weight, of nitrate.
Claim 10
Dependent Claim
23 words
The method of claim 6, wherein the weight ratio of solids to liquid phase in said coated particles is at least about 3:1.
Claim 11
Dependent Claim
40 words
The method of claim 6, wherein said decomposition reactor is a fluidized bed of said dioxide particles and at least a portion of said nitrogen dioxide-containing gaseous mixture of step (4) is recycled to the bed as the fluidizing means.
Claim 12
Dependent Claim
37 words
The method of claim 6, wherein the temperature of said coated particles is raised above about 180° C. by contacting said coated particles with manganese dioxide particles whose temperature is above the decomposition temperature of manganous nitrate.
Claim 13
Dependent Claim
21 words
The method of claim 10, wherein said liquid phase of manganous nitrate contains at least about 50%, by weight, of nitrate.
Claim 14
Dependent Claim
23 words
The method of claim 10, wherein the weight ratio of solids to liquid phase in said coated particles is at least about 3:1.
Claim 15
Dependent Claim
32 words
The method of claim 10, wherein at least a portion of the manganese dioxide removed in step (4) is heated and recycled to contact said coated particles and raise the temperature thereof.
Claim 16
Dependent Claim
13 words
The method of claim 10, wherein said decomposition reactor is a rotary kiln.
Claim 17
Dependent Claim
40 words
The method of claim 10, wherein said decomposition reactor is a fluidized bed of said dioxide particles and at least a portion of said nitrogen dioxide-containing gaseous mixture of step (4) is recycled to the bed as the fluidizing means.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |