Cellular inorganic resin cements, and process and compositions for forming them
Assignee: PLASKOLITE Inc A CORP OF OHIO
•
Filing: 1977-12-05
•
Granted: 1979-02-27
•
Expires: 1997-12-05
Abstract
Abstract Process and composition for forming cellular inorganic plastic cements of magnesium oxychlorides and magnesium oxysulfates. A water slurry containing a magnesium salt, magnesium oxide and a water-soluble phosphate is formed and to it are added an anionic water-repellent surfactant and a blowing agent capable of providing a gaseous component in the strongly alkaline environment either through decomposition or reaction or through vaporization. Inorganic filler material may be added to impart strength, the maximum flexural strength being attained when at least about one-half of the filler comprises microfibers. The resulting cellular product is nonflammable and exhibits essentially zero flame spread, zero smoke density and zero fuel contribution. The cellular products are further characterized as being formed of substantially uniformly sized cells and having densities over a wide range.
Inventors
- 👤 William L. Prior
- 👤 Richard S. Lindstrom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:37
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/30; C04B28/32; C04B2111/00; C04B2111/20; C04B2111/27; C04B2111/275
Claims Analysis
Total Claims: 85
Claim 1
Independent Claim
187 words
A process for forming a cellular inorganic resin cement, comprising the steps of (a) forming a reactant water slurry of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate, a water-soluble phosphate and reactive magnesium oxide, the amount of said magnesium salt ranging from about 50% to about 75% by weight of the total weight of said water and said magnesium salt, said slurry having a viscosity ranging between about 700 and 15,000 centipoises; (b) blending into said slurry at least 0.5% by slurry weight of an anionic water-repellent surfactant; (c) uniformly dispersing throughout said slurry a blowing agent, capable of providing a gaseous component either through decomposition or reaction or through vaporization at a temperature below that at which said inorganic resin cement is cured, in an amount required to form said cellular inorganic resin cement with a predetermined density, thereby to provide a foaming composition capable of attaining said predetermined density and final cell structure before said foaming composition gels to form said inorganic resin cement; and (d) curing said foaming composition under conditions to retain essentially all of its water content.
Claim 2
Dependent Claim
187 words
A process for forming a cellular inorganic resin cement, comprising the steps of (a) forming a reactant water slurry of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate, a water-soluble phosphate and reactive magnesium oxide, the amount of said magnesium salt ranging from about 50% to about 75% by weight of the total weight of said water and said magnesium salt, said slurry having a viscosity ranging between about 700 and 15,000 centipoises; (b) blending into said slurry at least 0.5% by slurry weight of an anionic water-repellent surfactant; (c) uniformly dispersing throughout said slurry a blowing agent, capable of providing a gaseous component either through decomposition or reaction or through vaporization at a temperature below that at which said inorganic resin cement is cured, in an amount required to form said cellular inorganic resin cement with a predetermined density, thereby to provide a foaming composition capable of attaining said predetermined density and final cell structure before said foaming composition gels to form said inorganic resin cement; and (d) curing said foaming composition under conditions to retain essentially all of its water content.
Claim 3
Dependent Claim
52 words
A process in accordance with claim 1 wherein the molar ratio of said magnesium chloride hexahydrate to said magnesium oxide is between about 1 to 3 and about 1 to 8 and of said magnesium sulfate heptahydrate to said magnesium oxide is between about 1 to 3 and about 1 to 14.
Claim 4
Dependent Claim
37 words
A process in accordance with claim 1 wherein the amount of said magnesium salt in said slurry ranges from about 60% to about 75% by weight of the total weight of said water and said magnesium salt.
Claim 5
Dependent Claim
32 words
A process in accordance with claim 1 wherein said magnesium salt is magnesium chloride hexahydrate and the molar ratio of said magnesium salt to said magnesium oxide is about 1 to 5.
Claim 6
Dependent Claim
20 words
A process in accordance with claim 1 wherein the viscosity of said slurry is between about 700 and 2500 centipoises.
Claim 7
Dependent Claim
23 words
A process in accordance with claim 1 wherein the amount of said surfactant ranges between about 0.5% and about 3% by slurry weight.
Claim 8
Dependent Claim
18 words
A process in accordance with claim 5 wherein said surfactant is stearic acid or an inorganic salt thereof.
Claim 9
Dependent Claim
22 words
A process in accordance with claim 1 wherein said blowing agent decomposes in the strongly alkaline slurry to provide said gaseous component.
Claim 10
Dependent Claim
28 words
A process in accordance with claim 8 wherein said blowing agent is hydrogen peroxide in an amount up to about 2.5% (100% concentration basis) by said slurry weight.
Claim 11
Dependent Claim
32 words
A process in accordance with claim 9 including the step of blending into said slurry, prior to the addition of said hydrogen peroxide, a catalyst for the decomposition of said hydrogen peroxide.
Claim 12
Dependent Claim
24 words
A process in accordance with claim 1 wherein said blowing agent is a liquid which vaporizes above ambient temperature to provide said gaseous component.
Claim 13
Dependent Claim
25 words
A process in accordance with claim 11 wherein said liquid blowing agent is trichlorofluoromethane in an amount up to about 8% by said slurry weight.
Claim 14
Dependent Claim
26 words
A process in accordance with claim 1 wherein said curing of said foaming composition is carried out at a temperature between ambient and about 250° C.
Claim 15
Dependent Claim
29 words
A process in accordance with claim 1 including the step of adding to said slurry a nucleating agent in an amount up to about 0.5% by said slurry weight.
Claim 16
Dependent Claim
23 words
A process in accordance with claim 1 including the step of forming said foaming composition into a predetermined configuration prior to said curing.
Claim 17
Dependent Claim
23 words
A process in accordance with claim 1 wherein said forming comprises molding with or without added heat and with or without added pressure.
Claim 18
Dependent Claim
56 words
A process in accordance with claim 1 including the step of incorporating a filler component into said cellular inorganic resin prior to said curing, the amount of said filler component being up to about 40% by weight of said cellular inorganic resin and less than that which will cause the collapse of said cellular inorganic resin.
Claim 19
Dependent Claim
24 words
A process in accordance with claim 17 wherein said filler component comprises at least in part microfibers up to about one-fourth inch in length.
Claim 20
Dependent Claim
14 words
A process in accordance with claim 18 wherein said microfibers comprise milled glass fibers.
Claim 21
Dependent Claim
14 words
A process in accordance with claim 18 wherein said microfibers comprise asbestos mine tailings.
Claim 22
Dependent Claim
13 words
A process in accordance with claim 18 wherein said microfibers comprise wollastonite fibers.
Claim 23
Dependent Claim
22 words
A process in accordance with claim 17 wherein said filler component comprises at least in part glass fibers longer than one-fourth inch.
Claim 24
Dependent Claim
20 words
A process in accordance with claim 22 wherein said glass fibers are in the form of a glass fiber mat.
Claim 25
Dependent Claim
21 words
A process in accordance with claim 17 wherein said filler component comprises at least in part a finely divided particulate material.
Claim 26
Dependent Claim
25 words
A process in accordance with claim 24 wherein said finely divided particulate material comprises mica, talc, perlite, vermiculite, polystyrene beads, glass microballoons or mixtures thereof.
Claim 27
Dependent Claim
54 words
A process in accordance with claim 17 wherein said step of incorporating said filler component comprises adding at least a portion of said filler component to said slurry, the amount of said filler component added to said slurry being no greater than that which raises the viscosity of said slurry to about 100,000 centipoises.
Claim 28
Dependent Claim
25 words
A process in accordance with claim 26 wherein said filler component is added to said slurry prior to dispersing said blowing agent throughout said slurry.
Claim 29
Dependent Claim
20 words
A process in accordance with claim 26 wherein said filler component is dispersed throughout said slurry with said blowing agent.
Claim 30
Dependent Claim
29 words
A process in accordance with claim 26 wherein said filler component comprises at least 50% by weight of microfibers ranging in length between about 1/32 inch and 1/4 inch.
Claim 31
Dependent Claim
24 words
A process in accordance with claim 26 wherein said filler component comprises at least in part fibers longer than one-fourth inch or particulate material.
Claim 32
Dependent Claim
40 words
A process in accordance with claim 26 including the steps of forming said foaming composition into a predetermined configuration and adding at least a portion of said filler component to said foaming composition during said forming of said predetermined configuration.
Claim 33
Dependent Claim
27 words
A process in accordance with claim 31 wherein said filler component added during said forming comprises microfibers ranging in length between about 1/32 inch and 1/4 inch.
Claim 34
Dependent Claim
24 words
A process in accordance with claim 31 wherein said filler component added during said forming comprises fibers longer than one-fourth inch or particulate material.
Claim 35
Dependent Claim
40 words
A process in accordance with claim 33 wherein said fibers added during said forming are glass and are provided as a glass fiber mat and said forming said predetermined configuration includes laminating said glass fiber mat with said foaming composition.
Claim 36
Dependent Claim
39 words
A process in accordance with claim 31 wherein said step of forming said predetermined configuration comprises molding said foaming composition within a mold cavity, said molding being performed with or without added heat and with or without added pressure.
Claim 37
Dependent Claim
30 words
A process in accordance with claim 35 including the step of lining said mold cavity with a mixture of a filler component and said reactant slurry without a blowing agent.
Claim 38
Dependent Claim
26 words
A process in accordance with claim 36 wherein said filler component in said mixture lining said mold cavity comprises fibers greater than one-fourth inch in length.
Claim 39
Dependent Claim
27 words
A process in accordance with claim 31 including the step of applying a surface finish to said predetermined configuration subsequent to curing said cellular inorganic resin cement.
Claim 40
Dependent Claim
193 words
A composition for forming a cellular inorganic resin cement, comprising in combination (a) a reactant water slurry of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate, reactive magnesium oxide and at least one water-soluble phosphate, said slurry having a viscosity ranging between about 700 and 15,000 centipoises and being one in which the solids concentration of said magnesium salt ranges between about 50% and about 70% by weight of the total weight of water of said slurry and said magnesium salt; (b) an anionic, water-repellent surfactant present in said slurry in an amount between about 0.5% and about 3% by slurry weight; and (c) a blowing agent, capable of providing a gaseous component either through decomposition or reaction or through vaporization in the strongly alkaline environment of said slurry, uniformly dispersed throughout said slurry and present in an amount required to form said cellular inorganic resin cement with a predetermined density, thereby to provide a foaming composition capable of attaining said predetermined density and final cell structure before said foaming composition gels to form said cellular inorganic resin cement and from which essentially no water is removed upon curing.
Claim 41
Dependent Claim
193 words
A composition for forming a cellular inorganic resin cement, comprising in combination (a) a reactant water slurry of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate, reactive magnesium oxide and at least one water-soluble phosphate, said slurry having a viscosity ranging between about 700 and 15,000 centipoises and being one in which the solids concentration of said magnesium salt ranges between about 50% and about 70% by weight of the total weight of water of said slurry and said magnesium salt; (b) an anionic, water-repellent surfactant present in said slurry in an amount between about 0.5% and about 3% by slurry weight; and (c) a blowing agent, capable of providing a gaseous component either through decomposition or reaction or through vaporization in the strongly alkaline environment of said slurry, uniformly dispersed throughout said slurry and present in an amount required to form said cellular inorganic resin cement with a predetermined density, thereby to provide a foaming composition capable of attaining said predetermined density and final cell structure before said foaming composition gels to form said cellular inorganic resin cement and from which essentially no water is removed upon curing.
Claim 42
Dependent Claim
51 words
A composition in accordance with claim 39 wherein the molar ratio of said magnesium chloride hexahydrate to said magnesium oxide ranges between about 1 to 3 and about 1 to 8 and of said magnesium sulfate heptahydrate to said magnesium oxide between about 1 to 3 and about 1 to 14.
Claim 43
Dependent Claim
37 words
A composition in accordance with claim 39 wherein the amount of said magnesium salt in said slurry ranges from about 60% to about 75% by weight of the total weight of said water and said magnesium salt.
Claim 44
Dependent Claim
32 words
A composition in accordance with claim 39 wherein said magnesium salt is magnesium chloride hexahydrate and the molar ratio of said magnesium salt to said magnesium oxide is about 1 to 5.
Claim 45
Dependent Claim
20 words
A composition in accordance with claim 39 wherein the viscosity of said slurry is between about 700 and 2500 centipoises.
Claim 46
Dependent Claim
23 words
A composition in accordance with claim 39 wherein the amount of said surfactant ranges between about 0.5% and about 3% by slurry weight.
Claim 47
Dependent Claim
18 words
A composition in accordance with claim 44 wherein said surfactant is stearic acid or an inorganic salt thereof.
Claim 48
Dependent Claim
22 words
A composition in accordance with claim 39 wherein said blowing agent decomposes in the strongly alkaline slurry to provide said gaseous component.
Claim 49
Dependent Claim
28 words
A composition in accordance with claim 46 wherein said blowing agent is hydrogen peroxide in an amount up to about 2.5% (100% concentration basis) by said slurry weight.
Claim 50
Dependent Claim
17 words
A composition in accordance with claim 47 including a catalyst for the decomposition of said hydrogen peroxide.
Claim 51
Dependent Claim
25 words
A composition in accordance with claim 48 wherein said decomposition catalyst is potassium permanganate in an amount up to about 0.5% by said slurry weight.
Claim 52
Dependent Claim
24 words
A composition in accordance with claim 39 wherein said blowing agent is a liquid which vaporizes above ambient temperature to provide said gaseous component.
Claim 53
Dependent Claim
25 words
A composition in accordance with claim 50 wherein said liquid blowing agent is trichlorofluoromethane in an amount up to about 8% by said slurry weight.
Claim 54
Dependent Claim
22 words
A composition in accordance with claim 39 including a nucleating agent in an amount up to about 0.5% by said slurry weight.
Claim 55
Dependent Claim
56 words
A composition in accordance with claim 39 including a filler component present in an amount up to about 40% by said slurry weight, and less than that which will cause the collapse of the cellular inorganic resin formed from said composition, said composition being further characterized as having a viscosity no greater than about 100,000 centipoises.
Claim 56
Dependent Claim
29 words
A composition in accordance with claim 53 wherein said filler component comprises at least 50% by weight of microfibers ranging in length between about 1/32 inch and 1/4 inch.
Claim 57
Dependent Claim
14 words
A composition in accordance with claim 54 wherein said microfibers comprise milled glass fibers.
Claim 58
Dependent Claim
14 words
A composition in accordance with claim 55 wherein said milled glass fibers are water-bonded.
Claim 59
Dependent Claim
13 words
A composition in accordance with claim 54 wherein said microfibers comprise mineral fibers.
Claim 60
Dependent Claim
15 words
A composition in accordance with claim 57 wherein said mineral fibers are asbestos mine tailings.
Claim 61
Dependent Claim
14 words
A composition in accordance with claim 57 wherein said mineral fibers are wollastonite fibers.
Claim 62
Dependent Claim
23 words
A composition in accordance with claim 53 wherein said filler component comprises at least in part fibers greater than one-fourth inch in length.
Claim 63
Dependent Claim
17 words
A composition in accordance with claim 53 wherein said filler component comprises a finely divided particulate material.
Claim 64
Dependent Claim
25 words
A composition in accordance with claim 61 wherein said finely divided particulate material comprises mica, talc, perlite, vermiculite, polystyrene beads, glass microballoons or mixtures thereof.
Claim 65
Dependent Claim
132 words
A cured cellular inorganic resin cement having essentially uniformly sized cells, a density ranging between about 5 and about 100 pounds per cubic foot and being further characterized as exhibiting essentially zero flame spread, zero smoke density and zero fuel contribution, said inorganic resin cement being the reaction product of reactive magnesium oxide and an aqueous, soluble phosphate-containing gaging solution of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate and having a concentration of said magnesium salt ranging between about 50% and about 75% by weight of said gaging solution, said reaction product being further characterized in that essentially all of the water of said gaging solution and the water of hydration of said magnesium salt are consumed in the reaction and contained in said inorganic resin cement.
Claim 66
Dependent Claim
132 words
A cured cellular inorganic resin cement having essentially uniformly sized cells, a density ranging between about 5 and about 100 pounds per cubic foot and being further characterized as exhibiting essentially zero flame spread, zero smoke density and zero fuel contribution, said inorganic resin cement being the reaction product of reactive magnesium oxide and an aqueous, soluble phosphate-containing gaging solution of a magnesium salt selected from magnesium chloride hexahydrate and magnesium sulfate heptahydrate and having a concentration of said magnesium salt ranging between about 50% and about 75% by weight of said gaging solution, said reaction product being further characterized in that essentially all of the water of said gaging solution and the water of hydration of said magnesium salt are consumed in the reaction and contained in said inorganic resin cement.
Claim 67
Dependent Claim
19 words
A cellular inorganic resin cement in accordance with claim 63 wherein said cells have diameters up to about 3mm.
Claim 68
Dependent Claim
54 words
A cellular inorganic resin cement in accordance with claim 63 wherein the molar ratio of said magnesium chloride hexahydrate to said magnesium oxide ranges between about 1 to 3 and about 1 to 8 and of said magnesium sulfate heptahydrate to said magnesium oxide between about 1 to 3 and about 1 to 14.
Claim 69
Dependent Claim
27 words
A cellular inorganic resin cement in accordance with claim 63 including a filler component present in an amount up to about 40% by weight of said cement.
Claim 70
Dependent Claim
26 words
A cellular inorganic resin cement in accordance with claim 66 wherein said filler component comprises at least 50% by weight microfibers up to one-fourth inch long.
Claim 71
Dependent Claim
15 words
A cellular inorganic resin cement in accordance with claim 67 wherein said microfibers are glass.
Claim 72
Dependent Claim
17 words
A cellular inorganic resin cement in accordance with claim 67 wherein said microfibers are milled glass fibers.
Claim 73
Dependent Claim
17 words
A cellular inorganic resin cement in accordance with claim 69 wherein said milled glass fibers are water-bonded.
Claim 74
Dependent Claim
16 words
A cellular inorganic resin cement in accordance with claim 67 wherein said microfibers comprise mineral fibers.
Claim 75
Dependent Claim
18 words
A cellular inorganic resin cement in accordance with claim 71 wherein said mineral fibers are asbestos mine tailings.
Claim 76
Dependent Claim
17 words
A cellular inorganic resin cement in accordance with claim 61 wherein said mineral fibers are wollastonite fibers.
Claim 77
Dependent Claim
27 words
A cellular inorganic resin cement in accordance with claim 66 wherein said filler component comprises at least in part long fibers greater than one-fourth inch in length.
Claim 78
Dependent Claim
25 words
A cellular inorganic resin cement in accordance with claim 74 wherein said long fibers are glass in the form of a woven or nonwoven mat.
Claim 79
Dependent Claim
24 words
A cellular inorganic resin cement in accordance with claim 75 wherein said cellular inorganic resin cement is formed as a cellular cement/glass fiber laminate.
Claim 80
Dependent Claim
21 words
A cellular inorganic resin cement in accordance with claim 76 wherein said cellular cement of said laminate contains microfibers distributed therethrough.
Claim 81
Dependent Claim
19 words
A cellular inorganic resin cement in accordance with claim 66 further characterized as being formed into a predetermined configuration.
Claim 82
Dependent Claim
27 words
A cellular inorganic resin cement in accordance with claim 78 wherein selected surfaces of said predetermined configuration have bonded thereto said inorganic resin cement in noncellular form.
Claim 83
Dependent Claim
22 words
A cellular inorganic resin cement in accordance with claim 79 wherein said noncellular inorganic resin cement has a filler component incorporated therein.
Claim 84
Dependent Claim
22 words
A cellular inorganic resin cement in accordance with claim 80 wherein said filler component comprises fibers greater than one-fourth inch in length.
Claim 85
Dependent Claim
14 words
A cellular inorganic resin cement in accordance with claim 78 including a surface finish.
References Cited (Backward Citations)
US1946077A
Cited
US3320077A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |