US4141727A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrical contact material and method of making the same
Assignee: Panasonic Holdings Corp
•
Filing: 1977-11-29
•
Granted: 1979-02-27
•
Expires: 1997-11-29
Abstract
Abstract An electrical contact material comprising silver, bismuth oxide and tin oxide with or without tin metal, wherein the amounts of the bismuth and the tin on the basis of the sum weight of the metals in both the metal component and in the metal oxide component are 1.5 to 6 weight percent and 0.1 to 6 weight percent, respectively. This electrical contact material has high resistance to both welding and arc erosion. An advantageous method of making the electrical contact material comprises preparing a metal alloy composed of all the above metals in the above weight ratio and internally oxidizing the bismuth completely in the alloy after shaping the alloy to a desired electrical contact material shape or after crushing the alloy to scaly flakes.
Inventors
- 👤 Sankichi Shida
- 👤 Shinji Okuma
- 👤 Mashiro Oita
- 👤 Hyogo Hirohata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:10
CPC Classifications
H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/023; H01H1/0237; H01H1/02372; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/929
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
110 words
An electrical contact material comprising a metal component as a major ingredient and the remainder being a metal oxide component as a minor ingredient, said metal component consisting essentially of silver with or without tin, and said metal oxide component consisting essentially of bismuth oxide and tin oxide, wherein the amount of the bismuth of said bismuth oxide is 1.5 to 6 weight percent, and the total amount of the tin of said metal component and the tin of said metal oxide component is 0.1 to 6 weight percent, respectively, both on the basis of the sum of said metal component and all the metals of said metal oxide component.
Claim 2
Dependent Claim
110 words
An electrical contact material comprising a metal component as a major ingredient and the remainder being a metal oxide component as a minor ingredient, said metal component consisting essentially of silver with or without tin, and said metal oxide component consisting essentially of bismuth oxide and tin oxide, wherein the amount of the bismuth of said bismuth oxide is 1.5 to 6 weight percent, and the total amount of the tin of said metal component and the tin of said metal oxide component is 0.1 to 6 weight percent, respectively, both on the basis of the sum of said metal component and all the metals of said metal oxide component.
Claim 3
Dependent Claim
53 words
An electrical contact material according to claim 1, wherein said metal component is present in the form of a silver-tin matrix, and said metal oxide component is present in the form of bismuth oxide particles (Bi 2 O 3 ) and tin oxide particles (SnO 2 ) uniformly dispersed in said silver-tin matrix.
Claim 4
Dependent Claim
65 words
An electrical contact material according to claim 1, wherein said metal component is present in the form of silver matrix, and said metal oxide component is present in the form of bismuth-tin oxide particles (Bi 2 Sn 2 O 7 ) and particles of one of bismuth oxide (Bi 2 O 3 ) or tin oxide (SnO 2 ) uniformly dispersed in said silver matrix.
Claim 5
Dependent Claim
57 words
An electrical contact material according to claim 3, wherein said electrical contact material is made by compressing and sintering a starting mixture consisting essentially of 1.6 to 6.5 weight percent of bismuth oxide (Bi 2 O 3 ), 0.1 to 7.5 weight percent of tin oxide (SnO 2 ) and the remainder of a fine silver powder.
Claim 6
Dependent Claim
48 words
An electrical contact material according to claim 1, wherein said metal component is present in the form of a silver matrix, and said metal oxide component is present in the form of bismuth-tin oxide particles (Bi 2 Sn 2 O 7 ) uniformly dispersed in said silver matrix.
Claim 7
Dependent Claim
43 words
An electrical contact material according to claim 1, wherein said electrical contact material is made by internally oxidizing a starting alloy consisting essentially of 1.5 to 6 weight percent of bismuth, 0.1 to 6 weight percent of tin, and the remainder of silver.
Claim 8
Dependent Claim
60 words
An electrical contact material according to claim 1, wherein said metal oxide component contains an additive oxide of one of copper oxide and zinc oxide, wherein the amount of the metal of said additive oxide is 0.016 to 1.2 weight percent on the basis of the sum of said metal component and all the metals of said metal oxide component.
Claim 9
Dependent Claim
79 words
An electrical contact material according to claim 7, wherein said metal component is present in the form of a silver matrix, and said metal oxide component is present in the form of bismuth-tin oxide particles (Bi 2 Sn 2 O 7 ), and one of bismuth oxide particles (Bi 2 O 3 ) or tin oxide particles (SnO 2 ), and one of copper oxide particles (CuO) or zinc oxide particles (ZnO), all uniformly dispersed in said silver matrix.
Claim 10
Dependent Claim
86 words
An electrical contact material according to claim 7, wherein said metal oxide component is present in the form of a silver matrix, and said metal oxide component is present in the form of bismuth-tin oxide particles (Bi 2 Sn 2 O 7 ), and one of bismuth oxide particles (Bi 2 O 3 ) or tin oxide particles, and one of copper oxide particles (CuO) or zinc oxide particles (ZnO), and one of copper-bismuth oxide particles or zinc-bismuth oxide particles uniformly dispersed in said silver matrix.
Claim 11
Dependent Claim
63 words
An electrical contact material according to claim 9, wherein said copper-bismuth oxide particles and said zinc-bismuth oxide particles have the formulae CuBi x O y and ZnBi x O y , respectively, where said x is the integer 2, 4 or 48, and said y is the integer 4, 7 or 73 when said x is the integer 2, 4 or 48, respectively.
Claim 12
Dependent Claim
39 words
An electrical contact material according to claim 10, wherein said copper-bismuth oxide particles has the formula CuBi 2 O 4 , and said zinc-bismuth oxide particles has the formula ZnBi 4 O 7 or ZnBi 48 O 78 .
Claim 13
Dependent Claim
54 words
An electrical contact material according to claim 7, wherein said electrical contact material is made by internally oxidizing a starting alloy consisting essentially of 1.5 to 6 weight percent of bismuth, 0.1 to 6 weight percent of tin, 0.016 to 1.2 weight percent of one of copper and zinc, and the remainder being silver.
Claim 14
Dependent Claim
72 words
An electrical contact material according to claim 7, wherein said electrical contact material is made by compressing and sintering a starting mixture consisting essentially of 1.6 to 6.5 weight percent of bismuth oxide (Bi 2 O 3 ), 0.1 to 7.5 weight percent of tin oxide (SnO 2 ), 0.02 to 1.5 weight percent of one of copper oxide (CuO) and zinc oxide (ZnO), and the remainder being a fine silver powder.
Claim 15
Independent Claim
69 words
A method of making an electrical contact material, comprising: melting a starting metal mixture to a molten alloy, said starting metal mixture consisting essentially of 1.5 to 6 weight percent of bismuth, 0.1 to 6 weight percent of tin, and the remainder of silver; cooling said molten alloy to an alloy ingot; and internally oxidizing bismuth in said alloy ingot to bismuth oxide by heating in an oxidizing atmosphere.
Claim 16
Independent Claim
69 words
A method of making an electrical contact material, comprising: melting a starting metal mixture to a molten alloy, said starting metal mixture consisting essentially of 1.5 to 6 weight percent of bismuth, 0.1 to 6 weight percent of tin, and the remainder of silver; cooling said molten alloy to an alloy ingot; and internally oxidizing bismuth in said alloy ingot to bismuth oxide by heating in an oxidizing atmosphere.
Claim 17
Dependent Claim
112 words
A method according to claim 14, wherein said internal oxidizing step comprises: first heating said alloy ingot in an oxidizing atmosphere at a temperature between 600° C. and the melting temperature of bismuth oxide so as to internally oxidize the bismuth in a surface layer of said alloy ingot to bismuth oxide; shaping the thus treated alloy ingot to a desired shape for the electrical contact material; and second, heating the thus shaped alloy ingot in an oxidizing atmosphere at a temperature between 600° C. and 850° C. so as to internally oxidize the bismuth, still remaining as metal bismuth in said alloy ingot after said first heating step, to bismuth oxide.
Claim 18
Dependent Claim
49 words
A method according to claim 15, wherein a cross-sectional area of said alloy ingot, wherein said alloy ingot is oxidized by said first heating step to such a depth that at least 25% of the cross sectional area of said alloy ingot is oxidized by said first heating step.
Claim 19
Dependent Claim
39 words
A method according to claim 15, wherein said alloy ingot, after said second heating step, is further subjected to a third heating step at a temperature between 870° C. and the melting temperature of silver, and is then quenched.
Claim 20
Dependent Claim
154 words
A method according to claim 14, wherein prior to said internal oxidizing step, said alloy ingot is crushed to scaly flakes each having a thickness of 0.1 to 1 mm, and the thus made flakes are compressed to a green billet having a porosity of about 5 to about 10 percent, and said internal oxidizing step comprising heating said gree billet in an oxidizing atmosphere at a temperature between 600° C. and the melting temperature of bismuth oxide so as to completely oxidize the bismuth in said flakes to bismuth oxide, wherein the thus heated flakes are further compressed to a compact body having a porosity less than 2 percent, and then reheating the thus made compact body in an oxidizing atmosphere at a temperature between 600° C. and the melting temperature of silver, to form a sintered body which is ready for shaping to a desired shape to form the electrical contact material.
Claim 21
Dependent Claim
44 words
A method according to claim 18, wherein said reheating step is carried out at a temperature higher than 870° C., and said sintered body is quenched, then annealed at a temperature between 870° C. and the melting temperature of silver, and then further quenched.
References Cited (Backward Citations)
CA564548A
Cited
US2486341A
Cited
US2890315A
Cited
US3205565A
Cited
US3489531A
Cited
DE2102996A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |