Water soluble or water dispersible hot-melt adhesive compositions based on polyvinyl alcohol with residual acetate groups and process for producing the same

Claim 2

Water soluble or water dispersible hot-melt adhesive compositions which consist essentially of: (a) polyvinyl alcohol having about a 30 to about a 60 mol% residual acetate group content which is prepared by dissolving polyvinyl acetate having an average degree of polymerization (p) of about 60 to about 200 in absolute methanol, the amount of the absolute methanol being from about the stoichiometric amount necessary to obtain polyvinyl alcohol having a degree of hydrolysis of about a 40 to about a 70 mol% to about 2 times as much as the above-defined stoichiometric amount, and carrying out alkaline hydrolysis; (b) one or more plasticizers in an amount of above about (0.08 p - 10)% by weight (but above 0% by weight) and below about (0.08 p + 25)% by weight based on the polyvinyl alcohol; and (c) an ethylene-vinyl acetate copolymer in an amount of 0 to about 50% by weight based on the polyvinyl alcohol.

Claim 3

Adhesive compositions as set forth in claim 1 wherein the polyvinyl acetate is produced by polymerizing vinyl acetate in one or more alcohols having a chain transfer constant above about 20 × 10 -4 at the polymerization temperature.

Claim 4

Adhesive compositions as set forth in claim 2 wherein the one or more alcohols include ethanol.

Claim 5

Adhesive compositions as set forth in claim 2 wherein the one or more alcohols include isopropanol.

Claim 6

Adhesive compositions as set forth in claim 1 wherein the one or more plasticizers include polyethylene glycol having a weight average molecular weight of about 400 to about 1,000.

Claim 7

Adhesive compositions as set forth in claim 1 wherein the one or more plasticizers are a mixture of one or more plasticizers which are liquid at room temperature and one or more plasticizers which are solid at room temperature.

Claim 8

Adhesive compositions as set forth in claim 1 wherein the ethylene-vinyl acetate copolymer has a melt index of about 150 to about 400.

Claim 9

Adhesive compositions as set forth in claim 1 wherein one or more acid compounds selected from the group consisting of phosphorus acid, phosphoric acid and pyrophosphoric acid is present.

Claim 10

Adhesive compositions as set forth in claim 8 wherein an amount of the one or more acid compounds is from about 0.1 to about 3% by weight based on the polyvinyl alcohol.

Claim 11

Adhesive compositions as set forth in claim 8 wherein the one or more acid compounds is phosphorous acid.

Claim 12

Adhesive compositions as set forth in claim 8 wherein the one or more acid compounds is pyrophosphoric acid.

Claim 13

A process for producing water soluble or dispersible hot-melt type adhesive compositions comprising (a) polyvinyl alcohol having a residual acetate group content of about 30 to about 60 mol%, (b) a plasticizer in an amount of above about (0.08 p - 10)% by weight (but above 0% by weight) and below about (0.08 p + 25)% by weight based on said polyvinyl alcohol, and (c) an ethylene-vinyl acetate copolymer in an amount of 0 to about 50% by weight based on said polyvinyl alcohol, which consists essentially of the following steps: (A) preparing polyvinyl acetate having an average degree of polymerization of about 60 to about 200 (p) by polymerizing vinyl acetate in a solvent; (B) dissolving the resultant polyvinyl acetate in absolute methanol, the amount of the absolute methanol being from about the stoichiometric amount necessary to obtain polyvinyl alcohol having a degree of hydrolysis of about 40 to about 70 mol% to about 2 times as much as the above-defined stoichiometric amount; (C) adding an alkali to the resultant solution to carry out alkaline hydrolysis of the polyvinyl acetate; and (D) mixing the resultant polyvinyl alcohol with the plasticizer in the above described amount and the ethylene-vinyl acetate copolymer in the above described amount upon melting.

Claim 14

A process for producing water soluble or dispersible hot-melt type adhesive compositions comprising (a) polyvinyl alcohol having a residual acetate group content of about 30 to about 60 mol%, (b) a plasticizer in an amount of above about (0.08 p - 10)% by weight (but above 0% by weight) and below about (0.08 p + 25)% by weight based on said polyvinyl alcohol, and (c) an ethylene-vinyl acetate copolymer in an amount of 0 to about 50% by weight based on said polyvinyl alcohol, which consists essentially of the following steps: (A) preparing polyvinyl acetate having an average degree of polymerization of about 60 to about 200 (p) by polymerizing vinyl acetate in a solvent; (B) dissolving the resultant polyvinyl acetate in absolute methanol, the amount of the absolute methanol being from about the stoichiometric amount necessary to obtain polyvinyl alcohol having a degree of hydrolysis of about 40 to about 70 mol% to about 2 times as much as the above-defined stoichiometric amount; (C) adding an alkali to the resultant solution to carry out alkaline hydrolysis of the polyvinyl acetate; and (D) mixing the resultant polyvinyl alcohol with the plasticizer in the above described amount and the ethylene-vinyl acetate copolymer in the above described amount upon melting.

Claim 15

A process for producing adhesive compositions as set forth in claim 12 wherein the solvent used for polymerization of the vinyl acetate is one or more alcohols having a chain transfer constant above about 20 × 10 -4 at the polymerization temperature.

Claim 16

A process for producing adhesive compositions as set forth in claim 13 wherein the one or more alcohols include ethanol.

Claim 17

A process for producing adhesive compositions as set forth in claim 13 wherein the one or more alcohols include isopropanol.

Claim 18

A process for producing adhesive compositions as set forth in claim 12 wherein the plasticizer is polyethylene glycol having a weight average molecular weight of about 400 to about 1000.

Claim 19

A process for producing adhesive compositions as set forth in claim 12 wherein the one or more plasticizers are a mixture of one or more plasticizers which are liquid at room temperature and one or more plasticizers which are solid at room temperature.

Claim 20

A process for producing adhesive compositions as set forth in claim 12 wherein the ethylene-vinyl acetate copolymer has a melt index of about 150 to about 400.

Claim 21

A process for producing adhesive compositions as set forth in claim 12 wherein the polyvinyl alcohol mixed with the plasticizer and the ethylene-vinyl acetate copolymer by melting is that produced by alkaline hydrolysis of polyvinyl acetate and drying the resultant product by melting by means of a vent type extruder.

Claim 22

A process for producing adhesive compositions as set forth in claim 12 wherein the step of mixing the polyvinyl alcohol with the plasticizer and the ethylene-vinyl acetate copolymer by melting is carried out by mixing the polyvinyl alcohol still containing the methanol with the plasticizer and the ethylene-vinyl acetate copolymer by melting and removing the solvent at a temperature above the melting point of the polyvinyl alcohol.

Claim 23

A process for producing adhesive compositions as set forth in claim 20 wherein mixing by melting is carried out by means of a vent type extruder.

Claim 24

A process for producing water soluble or dispersible hot-melt type adhesive compositions comprising (a) polyvinyl alcohol having a residual acetate group content of about 30 to about 60 mol%, (b) a plasticizer in an amount of above about (0.08 p - 10)% by weight (but above 0% by weight) and below about (0.08 p + 25)% by weight based on said polyvinyl alcohol, (c) an ethylene-vinyl acetate copolymer in an amount of 0 to about 50% by weight based on said polyvinyl alcohol and (d) an acid compound selected from the group consisting of phosphorus acid, phosphoric acid and pyrophosphoric acid in an amount of about 0.5 to about 3% by weight, which consists essentially of the following steps: (A) preparing polyvinyl acetate having an average degree of polymerization (p) of about 60 to about 200 by polymerizing vinyl acetate in a solvent; (B) dissolving the resultant polyvinyl acetate in absolute methanol, the amount of the absolute methanol being from about the stoichiometric amount necessary to obtain polyvinyl alcohol having a degree of hydrolysis of about 40 to about 70 mol% to about 2 times as much as the above-defined stoichiometric amount; (C) adding an alkali to the resultant solution to carry out alkaline hydrolysis of the polyvinyl acetate; and (D) mixing the resultant polyvinyl alcohol with the plasticizer in the above described amount, the ethylene-vinyl acetate copolymer in the above described amount and the acid compound in the amount of the above-described amount by melting.

Claim 25

A process for producing water soluble or dispersible hot-melt type adhesive compositions comprising (a) polyvinyl alcohol having a residual acetate group content of about 30 to about 60 mol%, (b) a plasticizer in an amount of above about (0.08 p - 10)% by weight (but above 0% by weight) and below about (0.08 p + 25)% by weight based on said polyvinyl alcohol, (c) an ethylene-vinyl acetate copolymer in an amount of 0 to about 50% by weight based on said polyvinyl alcohol and (d) an acid compound selected from the group consisting of phosphorus acid, phosphoric acid and pyrophosphoric acid in an amount of about 0.5 to about 3% by weight, which consists essentially of the following steps: (A) preparing polyvinyl acetate having an average degree of polymerization (p) of about 60 to about 200 by polymerizing vinyl acetate in a solvent; (B) dissolving the resultant polyvinyl acetate in absolute methanol, the amount of the absolute methanol being from about the stoichiometric amount necessary to obtain polyvinyl alcohol having a degree of hydrolysis of about 40 to about 70 mol% to about 2 times as much as the above-defined stoichiometric amount; (C) adding an alkali to the resultant solution to carry out alkaline hydrolysis of the polyvinyl acetate; and (D) mixing the resultant polyvinyl alcohol with the plasticizer in the above described amount, the ethylene-vinyl acetate copolymer in the above described amount and the acid compound in the amount of the above-described amount by melting.

Claim 26

A proces for producing adhesive compositions as set forth in claim 22 wherein the acid compound is phosphorous acid.

Claim 27

A process for producing adhesive compositions as set forth in claim 22 wherein the acid compound is pyrophosphoric acid.