Method for lead crystal storage cells and storage devices made therefrom
Assignee: Solargen Electronics Ltd
•
Filing: 1977-12-01
•
Granted: 1979-02-20
•
Expires: 1997-12-01
Abstract
Abstract A unique storage cell is provided in which the active mass on the positive electrode is a mixture of crystalline and polycrystalline lead superoxide (PbO2). These cells are characterized, inter alia, by their remarkably lower internal resistance, higher activity, better charging and discharging characteristics, lower sulphatization, higher storage capacity and greater ability to draw larger amounts of electric current in a considerably shorter period of time as compared with conventional lead-acid storage cells. Storage devices (e.g., a battery) made from such cells also exhibit superior performance characteristics as compared with storage devices made from the conventional lead-acid cells. Batteries made from such cells will be referred to as "lead-crystal" batteries.
Inventors
- 👤 Rudolf R. Hradcovsky
- 👤 Otto R. Kozak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:09
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/14; H01M4/16; H01M4/36; H01M4/48; H01M4/56; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
166 words
A method of making a solid state conductor for use in storage cells which comprises: (a) forming a uniform and adherent layer of lead and cadmium on a carrier plate selected from the group consisting of lead, an alloy of lead with antimony and an inert, non-conductive material coated with lead or an alloy of lead with antimony, (b) immersing the resulting carrier plate in a container containing a dilute solution of sulfuric acid and a lead plate, (c) connecting said carrier plate to the positive terminal of an emf source and connecting lead plate to the negative terminal of said emf source, thereby causing electric current to flow through said plates, and (d) causing said cadmium in said lead-cadmium layer to react with sulfuric acid to form cadmium sulfate which is deposited on said lead plate, and simultaneously oxidizing said lead in said lead-cadmium layer thereby forming a mixture of crystalline and polycrystalline lead superoxide, in which lead is at its maximum valence of four.
Claim 2
Independent Claim
166 words
A method of making a solid state conductor for use in storage cells which comprises: (a) forming a uniform and adherent layer of lead and cadmium on a carrier plate selected from the group consisting of lead, an alloy of lead with antimony and an inert, non-conductive material coated with lead or an alloy of lead with antimony, (b) immersing the resulting carrier plate in a container containing a dilute solution of sulfuric acid and a lead plate, (c) connecting said carrier plate to the positive terminal of an emf source and connecting lead plate to the negative terminal of said emf source, thereby causing electric current to flow through said plates, and (d) causing said cadmium in said lead-cadmium layer to react with sulfuric acid to form cadmium sulfate which is deposited on said lead plate, and simultaneously oxidizing said lead in said lead-cadmium layer thereby forming a mixture of crystalline and polycrystalline lead superoxide, in which lead is at its maximum valence of four.
Claim 3
Dependent Claim
70 words
A method of making a solid state conductor as in claim 1 wherein, in step (a), said uniform and adherent layer lead and cadmium is formed by spraying a hot melt mixture of lead and cadmium on the surface of the carrier plate under a reducing atmosphere, and causing said hot melt mixture to sinterize on the surface of the carrier plate without forming an alloy of lead and cadmium.
Claim 4
Dependent Claim
22 words
A method as in claim 2 wherein said hot melt mixture consists of from about 30 to about 70 weight percent lead.
Claim 5
Dependent Claim
22 words
A method as in claim 2 wherein said hot melt mixture consists of from about 45 to about 55 weight percent lead.
Claim 6
Dependent Claim
22 words
A method as in claim 2 wherein said hot melt mixture is an approximately 1:1 ratio by weight, of lead to cadmium.
Claim 7
Dependent Claim
57 words
A method of making a solid state conductor as in claim 1 wherein, in step (a) said uniform and adherent layer of lead and cadmium is formed by making a relatively thin paste of lead and cadmium mixture in a reducing organic liquid, depositing said paste on said carrier plate and evaporating said solvent from the paste.
Claim 8
Dependent Claim
13 words
A method as in claim 6 wherein said reducing organic liquid is methanol.
Claim 9
Dependent Claim
24 words
A method as in claim 7 wherein said layer of lead and cadmium consists of from about 30 to about 70 weight percent lead.
Claim 10
Dependent Claim
24 words
A method as in claim 7 wherein said layer of lead and cadmium consists of from about 45 to about 55 weight percent lead.
Claim 11
Dependent Claim
24 words
A method as in claim 7 wherein said layer of lead and cadmium is an approximately 1:1 ratio by weight, of lead to cadmium.
Claim 12
Dependent Claim
13 words
A method as in claim 6 wherein said reducing organic liquid is ethanol.
Claim 13
Dependent Claim
24 words
A method as in claim 11 wherein said layer of lead and cadmium consists of from about 30 to about 70 weight percent lead.
Claim 14
Dependent Claim
24 words
A method as in claim 11 wherein said layer of lead and cadmium consists of from about 45 to about 55 weight percent lead.
Claim 15
Dependent Claim
24 words
A method as in claim 11 wherein said layer of lead and cadmium is an approximately 1:1 ratio by weight, of lead to cadmium.
Claim 16
Dependent Claim
24 words
A method as in claim 6 wherein said layer of lead and cadmium consists of from about 30 to about 70 weight percent lead.
Claim 17
Dependent Claim
24 words
A method as in claim 6 wherein said layer of lead and cadmium consists of from about 45 to about 55 weight percent lead.
Claim 18
Dependent Claim
24 words
A method as in claim 6 wherein said layer of lead and cadmium is an approximately 1:1 ratio by weight, of lead to cadmium.
Claim 19
Dependent Claim
113 words
A method of making a solid state conductor as in claim 1 wherein, in step (a), said uniform and adherent layer of lead and cadmium is formed on the surface of said carrier plate by an electroplating process which comprises immersing, in an electrolytic bath, two conductors, a cathode made from an alloy of lead and antimony and an anode made from lead and cadmium, wherein said electrolytic bath comprises lead fluoroborate, metallic lead, fluoroboric acid, boric acid, cadmium fluoroborate, metallic cadmium, ammonium fluoroborate and water, connecting said cathode and said anode, respectively, to the negative and positive terminals of an emf source, and causing an electric current to flow through said electrodes.
Claim 20
Dependent Claim
20 words
A method as in claim 18 wherein said anode consists of from about 30 to about 70 weight percent lead.
Claim 21
Dependent Claim
20 words
A method as in claim 18 wherein said anode consists of from about 45 to about 55 weight percent lead.
Claim 22
Dependent Claim
21 words
A method as in claim 18 wherein said anode consists of an approximately 1:1 ratio by weight, of lead to cadmium.
References Cited (Backward Citations)
US4008144A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-19 | 1982-08-21 | 1983-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-19 | 1986-08-21 | 1987-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-19 | 1990-08-21 | 1991-02-20 | $7700.00 | Window Closed / Lapsed |