US4139591A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Reinforced plastic molding material
Assignee: Individual
•
Filing: 1975-01-17
•
Granted: 1979-02-13
•
Expires: 1995-01-17
Abstract
Abstract A laminating material such as a fibrous glass formed as a woven fabric or chopped strand mat which has been coated with a plastic resin on both sides thereof. The plastic resin is applied so that it does not permeate the fibers of the reinforcing material but is only adhered on the surfaces thereof. The resin coating is maintained intact on the reinforcing material by incorporation of a fine light mat, referred to as a carrier, in the resin coating. The reinforcing material can be made by initially laying down a resin coating on release film, together with the carrier. After processing of the resin to its final tackiness required for laminating, the resin sheet is adhered to one or preferably both surfaces of the laminating fabric.
Inventors
- 👤 Peter L. Jurisich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:37
CPC Classifications
B; B29; B29B; B29B15/00; B29B15/08; B29B15/10; B32; B32B; B32B5/00; B32B5/02; B32B5/024; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/28; B29C70/30; B29C70/34; B32B27/00; B32B27/12; B32B7/00; B32B7/04; B32B7/06; B29C33/00; B29C33/56; B29C33/68; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0854; B32B2262/00; B32B2262/10; B32B2262/101; B32B2305/00; B32B2305/10; B32B2305/20; B32B2305/72; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1028; Y10T442/00; Y10T442/30; Y10T442/3707; Y10T442/378
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
234 words
The process of manufacturing a laminating material for use in the forming of a cured composite fibrous glass and resin product comprising: supplying a reinforcing fibrous glass mat or fabric; supplying a release paper; placing a plastic resin in a partially cured stage compatible with the fibrous glass on said release paper in a partially adhered manner wherein said resin can form a cured composite product with the reinforcing fibrous glass mat or fabric; applying a thin web or strands of material into the resin to help to maintain it from flaking off the mat or fabric during any bending or movement thereof prior to forming the product to be formed; and, impressing the combination of said release paper with said resin and thin web or strand of material therein against the surface of said fibrous glass fabric or mat whereby said release paper is exposed with said resin and reinforcing web thereunder so that said resin extends into the interstices of said fibrous glass fabric or mat sufficiently to cause it to bind to the reinforcing mat or fabric strands so that at least a portion of the fibers are secured together to allow the resin to flow in sufficient quantity substantially between all fibers to cause the resin to extend substantially into the interstices throughout the cross section of said fabric to form a product having resin content through its cross section.
Claim 2
Dependent Claim
234 words
The process of manufacturing a laminating material for use in the forming of a cured composite fibrous glass and resin product comprising: supplying a reinforcing fibrous glass mat or fabric; supplying a release paper; placing a plastic resin in a partially cured stage compatible with the fibrous glass on said release paper in a partially adhered manner wherein said resin can form a cured composite product with the reinforcing fibrous glass mat or fabric; applying a thin web or strands of material into the resin to help to maintain it from flaking off the mat or fabric during any bending or movement thereof prior to forming the product to be formed; and, impressing the combination of said release paper with said resin and thin web or strand of material therein against the surface of said fibrous glass fabric or mat whereby said release paper is exposed with said resin and reinforcing web thereunder so that said resin extends into the interstices of said fibrous glass fabric or mat sufficiently to cause it to bind to the reinforcing mat or fabric strands so that at least a portion of the fibers are secured together to allow the resin to flow in sufficient quantity substantially between all fibers to cause the resin to extend substantially into the interstices throughout the cross section of said fabric to form a product having resin content through its cross section.
Claim 3
Dependent Claim
27 words
The process as claimed in claim 1 further comprising: pressing the combination of said resin, web and release paper on both surfaces of said fabric or mat.
Claim 4
Dependent Claim
15 words
The process as claimed in claim 1 further comprising: utilization of a chopped strand mat.
Claim 5
Dependent Claim
16 words
The process as claimed in claim 1 further comprising: utilization of a woven fibrous glass mat.
Claim 6
Dependent Claim
207 words
The process of manufacturing a finished composite product of fibrous glass reinforced plastic comprising: supplying a reinforcing mat or fabric; supplying a release paper against said reinforcing mat or fabric; placing a plastic resin compatible with said fibrous glass that has not been brought to its final cure to form the plastic of the end product with the reinforcing fabric or mat against said release paper in a partially adhered manner; applying a thin web or strands of material to the resin to maintain the resin from flaking off the mat or fabric during movement or subsequent conformation in forming the fibrous glass reinforced plastic; impressing the combination of resin with the reinforcing web into the surface of said fabric or mat sufficiently into the interstices so that they are bound at least to a limited degree at the surface thereof; applying said combination against a form of the final end product to which the combination is to be conformed; removing said release paper from said combination; forming said combination with respect to said form so as to cause the resin to flow and extend substantially through the cross section of the mat or fabric; and, curing said resin to form the fibrous glass reinforced plastic product.
Claim 7
Dependent Claim
207 words
The process of manufacturing a finished composite product of fibrous glass reinforced plastic comprising: supplying a reinforcing mat or fabric; supplying a release paper against said reinforcing mat or fabric; placing a plastic resin compatible with said fibrous glass that has not been brought to its final cure to form the plastic of the end product with the reinforcing fabric or mat against said release paper in a partially adhered manner; applying a thin web or strands of material to the resin to maintain the resin from flaking off the mat or fabric during movement or subsequent conformation in forming the fibrous glass reinforced plastic; impressing the combination of resin with the reinforcing web into the surface of said fabric or mat sufficiently into the interstices so that they are bound at least to a limited degree at the surface thereof; applying said combination against a form of the final end product to which the combination is to be conformed; removing said release paper from said combination; forming said combination with respect to said form so as to cause the resin to flow and extend substantially through the cross section of the mat or fabric; and, curing said resin to form the fibrous glass reinforced plastic product.
Claim 8
Dependent Claim
18 words
The process of claim 5 further comprising: Applying said combination to both surfaces of said fabric or mat.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |