Products obtained by molding ligneous materials and their method of manufacture
Assignee: Individual
•
Filing: 1976-10-07
•
Granted: 1979-02-13
•
Expires: 1996-10-07
Abstract
Abstract A process for producing a heat-resistant object comprises drying fibrils of a ligneous material previously immersed in a boiling aqueous salt solution, said drying being continued until the moisture content thereof is about 10 percent, impregnating said dried fibrils with a solution of a polymerizable resin and pressure molding the resulting impregnated fibrils so as to polymerize said resin thereby producing said heat-resistant object.
Inventors
- 👤 Pierre Sorbier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 01:37
CPC Classifications
D; D21; D21J; D21J1/00; D21J1/16; C; C08; C08K; C08K3/00; C08K3/16; C08L; C08L97/00; C08L97/02; C08L2201/00; C08L2201/08; C08L61/00; C08L61/20; C08L61/26; C08L61/28
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
67 words
A process for producing a heat-resistant object comprising (a) immersing a ligneous material in an aqueous salt solution, (b) drying the said ligneous material, in the form of fibrils until the moisture content thereof is about 10 percent, (c) impregnating said fibrils with a solution of a polymerizable resin, and (d) molding said resin impregnated fibrils under pressure to polymerize said resin thereby producing said heat-resistant object.
Claim 2
Dependent Claim
67 words
A process for producing a heat-resistant object comprising (a) immersing a ligneous material in an aqueous salt solution, (b) drying the said ligneous material, in the form of fibrils until the moisture content thereof is about 10 percent, (c) impregnating said fibrils with a solution of a polymerizable resin, and (d) molding said resin impregnated fibrils under pressure to polymerize said resin thereby producing said heat-resistant object.
Claim 3
Dependent Claim
16 words
The process of claim 1 wherein said fibrils are impregnated with a hydroalcoholic solution of melamine.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein said ligneous material is immersed in an aqueous solution of sodium chloride.
Claim 5
Dependent Claim
15 words
The process of claim 3 wherein said aqueous solution of sodium chloride also includes kaolin.
Claim 6
Dependent Claim
17 words
The process of claim 1 wherein the aqueous salt solution in step (a) is at the boil.
Claim 7
Dependent Claim
101 words
The process of claim 1 which also includes subsequent to molding said resin impregnated fibrils in step (d), the steps of (e) spraying on the surface of the resulting molded object a catalyst-containing solution of a polymerizable resin and simultaneously with said spraying, projecting onto said surface bleached wood wool or bleached and dried paper pulp or a mixture thereof, and (f) molding said object resulting from step (e) under pressure and at a temperature of about 100° to 150° C. for a time sufficient to polymerize said resin, whereby said object is provided with the appearance of faience or porcelain.
Claim 8
Dependent Claim
11 words
The process of claim 6 wherein said catalyst is ammonium chloride.
Claim 9
Dependent Claim
77 words
A process for producing a molded object from ligneous material fibrils, said object having the appearance of faience or porcelain consisting essentially of (a) preparing an admixture consisting essentially of said ligneous material fibrils, a polymerizable resin in an amount effective to impregnate said ligneous material and an effective amount of bleached wood wool or bleached paper pulp or a mixture thereof and (b) molding the mixture resulting from step (a) so as to polymerize said resin.
Claim 10
Dependent Claim
77 words
A process for producing a molded object from ligneous material fibrils, said object having the appearance of faience or porcelain consisting essentially of (a) preparing an admixture consisting essentially of said ligneous material fibrils, a polymerizable resin in an amount effective to impregnate said ligneous material and an effective amount of bleached wood wool or bleached paper pulp or a mixture thereof and (b) molding the mixture resulting from step (a) so as to polymerize said resin.
Claim 11
Dependent Claim
10 words
The process of claim 8 wherein said resin is melamine.
Claim 12
Dependent Claim
26 words
The process of claim 8 wherein said ligneous material fibrils prior to being admixed in step (a) are immersed in an aqueous solution of sodium chloride.
Claim 13
Dependent Claim
16 words
The process of claim 10 wherein said aqueous solution of sodium chloride is at the boil.
Claim 14
Dependent Claim
13 words
The process of claim 8 which includes adding kaolin powder in step (a).
Claim 15
Dependent Claim
41 words
The process of claim 8 wherein the ligneous material fibrils in step (a) are in the form of ligneous bundles having a length between 5 and 20 mm, a thickness less than 0.1 mm and a width less than 0.5 mm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |