Process for the electrolytic formation of lead dioxide solar absorption coating

Claim 2

In the method of forming lead dioxide solar energy collector coatings by electrodeposition, the improvement comprising two stage electrodeposition, from a bath suitable therefor, by first depositing the lead dioxide at a relatively high overpotential to form nuclei at a multiplicity of random locations on the surface of the substrate followed by deposition at a reduced overpotential for a longer period of time to cause crystal growths outward from said preformed nuclei, said crystal growths comprising a multiplicity of upwardly pointing pyramidal shapes adapted to trap incident radiation to enhance the absorption thereof.

Claim 3

An improved process, as recited in claim 1, wherein said first nuclei-forming stage is maintained for a time period on the order of 1-5 seconds and said second crystal growth stage continues for a duration on the order of 1-15 minutes.

Claim 4

An improved process, as recited in claim 1, wherein said bath is essentially free of contaminants or additives and is maintained at a temperature below 30° C.

Claim 5

An improved process, as recited in claim 1, wherein the initial potential applies about 6 milliamps per square centimeter and the subsequent potential produces about 3 milliamps per square centimeter anodic current densities.

Claim 6

An improved process, as recited in claim 1, wherein the substrate used in said process is copper and a corrosion-resistant coating is first applied to said copper substrate.

Claim 7

An improved process, as recited in claim 1, wherein said staged electrodeposition process produces oriented upwardly extending, randomly shaped and disposed crystals up to 1.0 micrometers in height and with a surface density on the order of 2-10 crystals per square micrometer.

Claim 8

An improved process, as recited in claim 1, wherein said high overpotential is 400-1000 millivolts per square centimeter and said reduced overpotential is 100-400 millivolts per square centimeter.

Claim 9

An improved process for forming lead dioxide solar energy collector coatings by two stages electrodeposition from a bath suitable therefor comprising first depositing the lead dioxide at a relatively high overpotential to form nuclei at a multiplicity of random locations on the surface of the substrate followed by deposition at a reduced overpotential for a longer period of time to cause crystal growths outward from said preformed nuclei said crystal growths comprising a multiplicity of upwardly pointing pyramidal shapes adapted to trap incident radiation to enhance the absorption thereof, wherein said electrodeposition bath consists of sodium hydroxide and lead monoxide and the current density in the first nuclei-forming stage is on the order of 4-8 milliamps per square centimeter and the current density for said subsequent crystal growth stage is on the order of 1-4 milliamps per square centimeter.

Claim 10

An improved process for forming lead dioxide solar energy collector coatings by two stages electrodeposition from a bath suitable therefor comprising first depositing the lead dioxide at a relatively high overpotential to form nuclei at a multiplicity of random locations on the surface of the substrate followed by deposition at a reduced overpotential for a longer period of time to cause crystal growths outward from said preformed nuclei said crystal growths comprising a multiplicity of upwardly pointing pyramidal shapes adapted to trap incident radiation to enhance the absorption thereof, wherein said electrodeposition bath consists of sodium hydroxide and lead monoxide and the current density in the first nuclei-forming stage is on the order of 4-8 milliamps per square centimeter and the current density for said subsequent crystal growth stage is on the order of 1-4 milliamps per square centimeter.

Claim 11

An improved process, as recited in claim 8, wherein said high overpotential is 400-1000 millivolts per square centimeter and said reduced overpotential is 100-400 millivolts per square centimeter.

Claim 12

An improved process, as recited in claim 9, wherein said high overpotential is 400-1000 millivolts per square centimeter and said reduced overpotential is 100-400 millivolts per square centimeter.