US4137216A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Post bulk polymerization process for polyvinyl halide and composition thereof
Assignee: Occidental Chemical Corp
•
Filing: 1977-06-29
•
Granted: 1979-01-30
•
Expires: 1997-06-29
Abstract
Abstract An improved polyvinyl halide or a vinyl halide copolymer containing up to 50 percent of a comonomer can be obtained by post polymerizing in a single stage or two-stage bulk process in contact with a base polymer, the same or different monomer as the monomer used to form the base polymer. Compositions produced by the process of the invention are useful in making films, coated fabrics and molded objects. The liquid phase post polymerization process of the invention is applicable to base polymers in powder form prepared by emulsion, suspension and bulk polymerization processes. The base polymer can be present in a polymerization mixture in which only a partial amount of monomer has been converted to base polymer such as in a two-stage polymerization process or the base polymer can be used in dry, solid form. Polymers of the invention have improved bulk density and reduced plasticizer uptake and can be used to prepare fabric coatings. Copolymers prepared by the novel post-polymerization process of the invention which show increased impact strength in addition to improved bulk density and reduced plasticizer uptake are useful in the preparation of molding compounds. In the bulk polymerization process of the invention, the addition of the same monomer or monomers or a different monomer or monomers subsequent to the partial conversion by a two-stage bulk process of polymerization of the vinyl halide monomer or monomers or vinyl halide monomer and comonomer, results in higher yield than can be obtained in the same reaction vessel as compared with a usual two-stage bulk polymerization process. In the two-stage bulk polymerization process of the invention, optional addition of small amounts of a hydrocarbon rubber dissolved or dispersed in the monomer to the second reaction stage effectively prevents reactor fouling during polymerization. Optional second stage addition of a small amount of a surfactant beneficially diminishes the porosity of the polymer product. A small particle size product can be obtained by incorporating in the first stage of a two-stage bulk polymerization process either an inert finely divided additive, a surfactant, a mixture thereof, or a polyolefin.
Inventors
- 👤 Anthony L. Lemper
- 👤 Gilbert Witschard
- 👤 Victor A. Pattison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:25
CPC Classifications
C; C08; C08F; C08F285/00; C08F255/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
434 words
The process for the preparation of small particle size polymer of vinyl halide by bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising a vinyl halide monomer or a mixture of a vinyl halide monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free particle size control additive selected from the group consisting of: (a) an inorganic or organic, inert, fine particle size material which is solid at least at the reaction temperature and insoluble in said monomer, said material having an average particle size in the range of about 0.001 to about 50 microns and said material being present in the amount of 0.001 to 5 percent by weight based upon said monomer composition present in said first stage; (b) a surface active agent in an amount of 0.01 to 5 percent by weight based upon said monomer present in said first stage; (c) a mixture of said inert, fine particle size material and said surface active agent; and (d) a polyolefin in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage; until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage comprising at least one vinyl halide monomer or at least one comonomer which copolymerizes therewith or mixtures thereof and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of a surface active agent added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
Claim 2
Dependent Claim
434 words
The process for the preparation of small particle size polymer of vinyl halide by bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising a vinyl halide monomer or a mixture of a vinyl halide monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free particle size control additive selected from the group consisting of: (a) an inorganic or organic, inert, fine particle size material which is solid at least at the reaction temperature and insoluble in said monomer, said material having an average particle size in the range of about 0.001 to about 50 microns and said material being present in the amount of 0.001 to 5 percent by weight based upon said monomer composition present in said first stage; (b) a surface active agent in an amount of 0.01 to 5 percent by weight based upon said monomer present in said first stage; (c) a mixture of said inert, fine particle size material and said surface active agent; and (d) a polyolefin in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage; until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage comprising at least one vinyl halide monomer or at least one comonomer which copolymerizes therewith or mixtures thereof and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of a surface active agent added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
Claim 3
Dependent Claim
47 words
The process of claim 1 wherein the additive in the first stage is selected from the group consisting of (a) the inert fine particle size material, (b) the surface active agent, and (c) the mixture of said inert, fine particle size material and said surface active agent.
Claim 4
Dependent Claim
16 words
The process of claim 2 wherein said inert, fine particle size material is a fumed silica.
Claim 5
Dependent Claim
17 words
The process of claim 2 wherein the first stage surface active agent additive is octylphenoxy polyethoxy ethanol.
Claim 6
Dependent Claim
15 words
The process of claim 1 wherein the additive in the first stage is the polyolefin.
Claim 7
Dependent Claim
44 words
The process of claim 5 wherein the monomer composition polymerized in the first stage is vinyl chloride and the monomer composition polymerized in the second stage until about 30 to about 95% by weight of monomer composition is converted to polymer is vinyl chloride.
Claim 8
Dependent Claim
21 words
The process of claim 6 wherein the polyolefin additive has a weight average molecular weight of about 50,000 to about 1,000,000.
Claim 9
Dependent Claim
13 words
The process of claim 7 wherein the polyolefin additive is ethylene-propylene-ethylidene norbornene terpolymer.
Claim 10
Dependent Claim
32 words
The process of claim 7 wherein 1 to 200% by weight of said additional monomer based upon the weight of the resultant converted based polymer or copolymer is added all at once.
Claim 11
Dependent Claim
17 words
The process of claim 9 wherein the additional monomer added in said second stage is vinyl chloride.
Claim 12
Dependent Claim
32 words
The process of claim 10 wherein the polymerization in step (2) is continued until about 30 to about 80 percent by weight of the monomer composition has been converted to base polymer.
Claim 13
Dependent Claim
19 words
The process of claim 11 wherein the surface active agent added in the second stage is octylphenoxy polyethoxy ethanol.
Claim 14
Dependent Claim
430 words
A small particle size polymer of vinyl halide by a bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising a vinyl halide monomer or a mixture of a vinyl halide monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free particle size control additive selected from the group consisting of: (a) an inorganic or organic, inert, fine particle size material which is solid at least at the reaction temperature and insoluble in said monomer, said material having an average particle size in the range of about 0.001 to about 50 microns and said material being present in the amount of 0.001 to 5 percent by weight based upon said monomer composition present in said first stage; (b) a surface active agent in an amount of 0.01 to 5 percent by weight based upon said monomer present in said first stage; (c) a mixture of said inert, fine particle size material and said surface active agent; and (d) a polyolefin in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage; until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage comprising at least one vinyl halide monomer or at least one comonomer which copolymerizes therewith or mixtures thereof, and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of a surface active agent added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
Claim 15
Dependent Claim
430 words
A small particle size polymer of vinyl halide by a bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising a vinyl halide monomer or a mixture of a vinyl halide monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free particle size control additive selected from the group consisting of: (a) an inorganic or organic, inert, fine particle size material which is solid at least at the reaction temperature and insoluble in said monomer, said material having an average particle size in the range of about 0.001 to about 50 microns and said material being present in the amount of 0.001 to 5 percent by weight based upon said monomer composition present in said first stage; (b) a surface active agent in an amount of 0.01 to 5 percent by weight based upon said monomer present in said first stage; (c) a mixture of said inert, fine particle size material and said surface active agent; and (d) a polyolefin in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage; until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage comprising at least one vinyl halide monomer or at least one comonomer which copolymerizes therewith or mixtures thereof, and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of a surface active agent added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
Claim 16
Dependent Claim
341 words
A small particle size polymer of vinyl halide by a bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising viny chloride monomer or a mixture of vinyl chloride monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free polyolefin particle size control additive of weight average molecular weight of about 50,000 to about 1,000,000 in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage, until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the vinyl chloride monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage consisting of vinyl chloride monomer, the proportion of said additional monomer being 1 to 200% based upon the weight of the resultant converted base polymer, said additional monomer being added all at once, and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of octylphenoxy polyethoxy ethanol added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
Claim 17
Dependent Claim
341 words
A small particle size polymer of vinyl halide by a bulk liquid phase polymerization comprising the steps of: (1) polymerization of a monomer composition comprising viny chloride monomer or a mixture of vinyl chloride monomer with an ethylenically unsaturated comonomer copolymerizable therewith, in a first stage using high speed agitation at a temperature of from about 30 to about 70 degrees centigrade in the presence of a water-free polyolefin particle size control additive of weight average molecular weight of about 50,000 to about 1,000,000 in an amount of about 0.05 to about 4 percent by weight based upon said monomer composition present in said first stage, until about 3 to about 20 percent by weight of said monomer composition has been converted to polymer particles, (2) continuing the preparation of small particle size polymers by polymerization in a second stage during which the reaction mixture is subjected to low speed agitation, until about 30 to about 95 percent by weight of the vinyl chloride monomer composition has been converted to base polymer, (3) introducing additional monomer into said second stage consisting of vinyl chloride monomer, the proportion of said additional monomer being 1 to 200% based upon the weight of the resultant converted base polymer, said additional monomer being added all at once, and (4) carrying out the polymerization of said additional monomer in said second stage to provide non-porous polymer particles by increasing the second stage polymerization temperature after about 30 to about 80 percent by weight of said reaction mixture has been converted to polymer, from a range of about 30 to about 70 degrees centigrade to a range of about 60 to 80 degrees centigrade, said increase in polymerization temperature being about 10 to about 50 degrees centigrade, said second stage polymerization being carried out in the presence of octylphenoxy polyethoxy ethanol added to said second stage polymerization reaction in an amount of about 0.01 to about 0.2 percent by weight based upon the weight of monomer composition added up to said point of surface active agent addition.
References Cited (Backward Citations)
US3725367A
Cited
US3875130A
Cited
US3891720A
Cited
US3816565A
Cited
US4003962A
Cited
US4028329A
Cited
US4048260A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-29 | 1982-07-31 | 1983-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-29 | 1986-07-31 | 1987-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-29 | 1990-07-31 | 1991-01-30 | $7700.00 | Window Closed / Lapsed |