Staple fiber, finish therefor and process for use of same
Assignee: HOECHST FIBERS INDUSTRIES
•
Filing: 1977-07-22
•
Granted: 1979-01-30
•
Expires: 1997-07-22
Abstract
Abstract A composition for short cut, synthetic polymeric staple fibers that are used in a wet lay application for the production of nonwovens is disclosed and claimed herein along with a fiber having the finish thereon and the process for dispersing the fiber in an aqueous medium. Synthetic polymeric filaments are cut into staple lengths, generally in a range of from about 1/4 to about 3 inches in length, and are dispersed in an aqueous medium in conjunction with a composition that includes as an essential ingredient, an ethoxylated primary emulsifier that contains at least five moles of ethylene oxide, and exhibits a surface tension of at least 30 dynes per centimeter in a 0.10 weight percent aqueous solution a 25 DEG C. plus or minus 2 DEG C. Optionally, a lubricant may be added to the finish composition to improve processability of the fiber during manufacture. The lubricant should be compatible with the primary emulsifier. A secondary emulsifier may also be added to emulsify the lubricant, and may additionally assist in dispersing the fiber. The composition may be added to the fiber during the manufacture of same or may be added to the aqueous medium. A preferred composition for addition to the fiber at the time of manufacture includes 50 parts of an ethoxylated castor oil, 25 parts of an ethoxylated sorbitol hexoleate and 25 parts of n-octyl, n-decyl adipate. The composition should further be characterized by a low foaming propensity and as not adversely affecting bondability of the fibers.
Inventors
- 👤 Roland L. Hawkins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:07
CPC Classifications
D; D21; D21H; D21H5/00; D21H5/12; D21H5/1254; D06; D06M; D06M13/00; D06M13/10; D06M13/165; D06M15/00; D06M15/19; D06M15/37; D06M15/53; D06M7/00; D21H13/00; D21H17/00; D21H17/71; D06M2200/00; D06M2200/40; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2904; Y10T428/2907; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
96 words
A finish composition for promoting dispersion of staple fibers in an aqueous medium comprising as an essential ingredient a primary emulsifier, said emulsifier being ethoxylated and containing at least five moles of ethylene oxide, said emulsifier further being characterized by a surface tension of at least 30 dynes per centimeter in a 0.10 weight percent aqueous solution of same at about 25° C., and said composition being further characterized by a low foaming propensity, and not adversely affecting bondability of the fibers with which it is used in the presence of a chemical bonding agent therefor.
Claim 2
Dependent Claim
96 words
A finish composition for promoting dispersion of staple fibers in an aqueous medium comprising as an essential ingredient a primary emulsifier, said emulsifier being ethoxylated and containing at least five moles of ethylene oxide, said emulsifier further being characterized by a surface tension of at least 30 dynes per centimeter in a 0.10 weight percent aqueous solution of same at about 25° C., and said composition being further characterized by a low foaming propensity, and not adversely affecting bondability of the fibers with which it is used in the presence of a chemical bonding agent therefor.
Claim 3
Dependent Claim
38 words
The finish composition as defined in claim 1 further comprising a lubricant for said fiber, said lubricant being compatible with said primary emulsifier to avoid adversely affecting dispersion of fibers having the finish thereon in an aqueous medium.
Claim 4
Dependent Claim
60 words
The finish composition as defined in claim 2 further comprising a secondary emulsifier, said secondary emulsifier emulsifying said lubricant in water and being compatible with said primary emulsifier, said primary and secondary emulsifiers representing at least a majority of said composition on a weight basis, and said secondary emulsifier being present in an amount of not more than said lubricant.
Claim 5
Dependent Claim
27 words
The finish composition as defined in claim 1 wherein said composition is present in an aqueous formulation in a range from about 1 to 10 weight percent.
Claim 6
Dependent Claim
36 words
The finish composition as defined in claim 1 wherein the primary emulsifier is selected from a group consisting of ethoxylated castor oils, ethoxylated hydrogenated castor oils, ethoxylated sorbitol esters, ethoxylated coconut oils and mixtures of same.
Claim 7
Dependent Claim
47 words
The finish composition as defined in claim 3 wherein the primary emulsifier is present in an amount of about 50 weight percent, the lubricant is present in an amount of about 25 weight percent and the secondary emulsifier is present in an amount of about 25 percent.
Claim 8
Dependent Claim
28 words
The finish composition as defined in claim 6 wherein the primary emulsifier is an ethoxylated castor oil having from about five to about 40 moles of ethylene oxide.
Claim 9
Dependent Claim
31 words
The finish composition as defined in claim 2 wherein the lubricant is a member selected from the group consisting of pentaerythritol tetrapelargonate, ethoxylated coconut oil, mineral oil, and n-octyl, n-decyl adipate.
Claim 10
Dependent Claim
26 words
The finish composition as defined in claim 6 wherein the secondary emulsifier is an ethoxylated sorbitol oleate having at least about 20 moles of ethylene oxide.
Claim 11
Dependent Claim
142 words
A finish formulation for polymeric staple fibers comprising: (a) about 1 to about 10 weight percent of a composition comprising an ethoxylated primary emulsifier, said primary emulsifier having at least five moles of ethylene oxide and a surface tension of at least about 30 dynes per centimeter in a 0.10 weight percent aqueous solution of same at about 25° C.; a lubricant for said fiber, said lubricant being compatible with said primary emulsifier so as not to adversely affect an aqueous dispersion of fiber with said composition thereon, and a secondary emulsifier being compatible with said primary emulsifier; and (b) the balance being an aqueous phase, said formulation being further characterized as promoting dispersion of said fibers in an aqueous medium, having a low foaming propensity, and not adversely affecting bondability of said fibers in the presence of a chemical binder therefor.
Claim 12
Dependent Claim
142 words
A finish formulation for polymeric staple fibers comprising: (a) about 1 to about 10 weight percent of a composition comprising an ethoxylated primary emulsifier, said primary emulsifier having at least five moles of ethylene oxide and a surface tension of at least about 30 dynes per centimeter in a 0.10 weight percent aqueous solution of same at about 25° C.; a lubricant for said fiber, said lubricant being compatible with said primary emulsifier so as not to adversely affect an aqueous dispersion of fiber with said composition thereon, and a secondary emulsifier being compatible with said primary emulsifier; and (b) the balance being an aqueous phase, said formulation being further characterized as promoting dispersion of said fibers in an aqueous medium, having a low foaming propensity, and not adversely affecting bondability of said fibers in the presence of a chemical binder therefor.
Claim 13
Dependent Claim
38 words
The finish formulation as defined in claim 10 wherein the primary emulsifier is a member selected from the group consisting of ethoxylated castor oils, ethoxylated hydrogenated castor oils, ethoxylated sorbitol esters, ethoxylated coconut oils, and mixtures of same.
Claim 14
Dependent Claim
31 words
The finish formulation as defined in claim 10 wherein the lubricant is a member selected from the group consisting of pentaerythritol tetrapelargonate, ethoxylated coconut oil, mineral oil, and n-octyl, n-decyl adipate.
Claim 15
Dependent Claim
17 words
The finish formulation as defined in claim 12 wherein said secondary emulsifier is an ethoxylated sorbitol hexoleate.
Claim 16
Dependent Claim
39 words
The finish formulation as defined in claim 10 wherein the primary emulsifier is POE(16) castor oil, the lubricant is n-octyl, n-decyl adipate, and the secondary emulsifier is POE (50) sorbitol hexoleate, and further said composition contains potassium hexyl phosphate.
References Cited (Backward Citations)
US3113369A
Cited
US3170876A
Cited
US3140198A
Cited
US3248258A
Cited
US3341452A
Cited
US3421935A
Cited
US3470095A
Cited
US3575856A
Cited
US3951825A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-29 | 1982-07-31 | 1983-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-29 | 1986-07-31 | 1987-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-29 | 1990-07-31 | 1991-01-30 | $7700.00 | Window Closed / Lapsed |