Method and apparatus for treating aluminous metal skim material and by-products of said method
Assignee: Reynolds Metals Co
•
Filing: 1977-02-24
•
Granted: 1979-01-30
•
Expires: 1997-02-24
Abstract
Abstract A method for treating hot skim material to separate, recover, and prepare for use both aluminum and non-aluminous constituents contained in the hot skim materials involves a centrifuge having a rotatable bowl to receive a charge of skim material. The centrifuge then both consolidates the non-aluminous constituents thereof into a semi-porous cake and separates and discharges molten aluminum as the bowl is rotated. The semi-porous cake is cooled and found to be friable. Thereafter, the friable cake is crushed and screened to be used as a foaming and extending agent.
Inventors
- 👤 Ogle R. Singleton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:29
CPC Classifications
C; C22; C22B; C22B21/00; C22B21/0038; C22B21/0069; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
178 words
A method of treating hot skim material after its removal from a body of molten aluminum to separate and recover aluminum contained therein without adding a salt flux to the skim material, which comprises the steps of: rotating a charge of said skim material in a rotatable container having at least one peripheral gap therein, said gap having a width in the range of from 1/8 to 1 inch at a temperature of at least above the liquidus under conditions effective substantially to avoid thermiting, and at a speed of rotation sufficient to separate molten aluminum from residual portions of the charge; consolidating with centrifugal force residual portions of said charge into a porous filter cake as the charge is being rotated at said peripheral opening, said container having a wall against which centrigugal force drives said residual portions for consolidating said residual portions at said at least one gap, into said porous filter cake at said gap without substantially passing therethrough; discharging separated aluminum radially outwardly around and through said porous filter cake and through said gap.
Claim 2
Independent Claim
178 words
A method of treating hot skim material after its removal from a body of molten aluminum to separate and recover aluminum contained therein without adding a salt flux to the skim material, which comprises the steps of: rotating a charge of said skim material in a rotatable container having at least one peripheral gap therein, said gap having a width in the range of from 1/8 to 1 inch at a temperature of at least above the liquidus under conditions effective substantially to avoid thermiting, and at a speed of rotation sufficient to separate molten aluminum from residual portions of the charge; consolidating with centrifugal force residual portions of said charge into a porous filter cake as the charge is being rotated at said peripheral opening, said container having a wall against which centrigugal force drives said residual portions for consolidating said residual portions at said at least one gap, into said porous filter cake at said gap without substantially passing therethrough; discharging separated aluminum radially outwardly around and through said porous filter cake and through said gap.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said at least one peripheral gap has a width within the range of from 3/16 to 1/2 inch.
Claim 4
Dependent Claim
33 words
The method of claim 2 including stopping rotation of said rotatable container, cooling residual portions of the charge in said container to a temperature below 1000° F., and removing the caked, cooled material.
Claim 5
Dependent Claim
35 words
The method of claim 1 wherein said at least one peripheral gap has a width of around 3/16 inch and some of the aluminum discharged radially outwardly is first filtered through said porous filter cake.
Claim 6
Independent Claim
77 words
A method of processing molten aluminum skim to obtain a foaming and extending agent therefrom comprising the steps of: gathering skim from molten aluminum; centrifuging said skim to separate an aluminum portion of said skim from a residual portion of said skim; crushing said residual portion of said skim and sorting particles therefrom to be used as a foaming and extending agent in plastic construction materials, said sorted particles being smaller than around 0.0058 inch (0.147 mm).
Claim 7
Independent Claim
77 words
A method of processing molten aluminum skim to obtain a foaming and extending agent therefrom comprising the steps of: gathering skim from molten aluminum; centrifuging said skim to separate an aluminum portion of said skim from a residual portion of said skim; crushing said residual portion of said skim and sorting particles therefrom to be used as a foaming and extending agent in plastic construction materials, said sorted particles being smaller than around 0.0058 inch (0.147 mm).
Claim 8
Dependent Claim
78 words
A method as in claim 5 wherein said centrifuging step is carried out in a centrifuge bowl having a peripheral gap therein, with a width in the range of from 1/8 to 1 inch, said centrifuge bowl having a wall which consolidates a non-aluminous portion of said skim into a porous cake at said gap to filter some aluminum passing through said gap, said aluminum portion of said skim being driven through said porous cake and said gap.
Claim 9
Dependent Claim
70 words
Method as in claim 5 wherein the sorting of said particles is accomplished with a screening assembly having at least two screens in series each successive screen having a smaller mesh size than the previous screen, the residual portion remaining on the larger mesh screen being further processed to obtain an aluminum fraction therefrom and the residual material passing through the finer mesh screen being used as a foaming/extending agent.
Claim 10
Dependent Claim
73 words
A method as in claim 7 wherein there are at least three screens and wherein the largest-mesh screen has a hole size of approximately 0.185 inches (4.699 mm), the second-largest mesh screen has an opening size of approximately 0.0232 inch (0.589 mm), and the finest mesh screen has an opening size of approximately 0.0058 inch (0.147 mm), and wherein the residual material caught by said finest mesh screen is again crushed and screened.
Claim 11
Independent Claim
135 words
A method of reclaiming aluminous metal, metallic oxides and metallic nitrides and carbides from molten aluminum skim material comprising the steps of: gathering skim from molten aluminum; centrifuging said skim to separate an aluminum portion of said skim from a residual portion of said skim, said centrifuging being accomplished in a centrifuge bowl having at least one peripheral gap with a width in the range of from 1/8 inch to 1 inch and a wall for consolidating said residual portion of said skim into a porous cake at said gap; crushing said residual portion of said skim to form crushed particles; sorting said crushed particles according to size into a small-particle fraction containing metallic nitrides and carbides and into at least one large-particle fraction; further treating said large particle fraction to extract aluminous metal therefrom.
Claim 12
Dependent Claim
22 words
A method as in claim 9 wherein said small-particle fraction has a particle size of less than approximately 0.0058 inch (0.147 mm).
Claim 13
Dependent Claim
86 words
A method as in claim 10 wherein said large particle fraction is separated into at least two other subfractions, a first having a particle size less than approximately 0.0232 inch (0.589 mm) and a second having a particle size greater than approximately 0.0232 inch (0.589 mm), and wherein the further step is included of further crushing and sorting said first subfraction to obtain additional particles having a size less than approximately 0.0058 inch (0.147 mm) to add to said small-particle fraction containing metallic nitrides and carbides.
Claim 14
Dependent Claim
19 words
A method as in claim 9 wherein said gap is in the range of from 3/16 to 1/2 inch.
Claim 15
Dependent Claim
13 words
A method as in claim 9 wherein said gap is around 3/16 inch.
References Cited (Backward Citations)
US3374089A
Cited
US3999980A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-29 | 1982-07-31 | 1983-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-29 | 1986-07-31 | 1987-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-29 | 1990-07-31 | 1991-01-30 | $7700.00 | Window Closed / Lapsed |