Abstract In a process for polymerization of tetrafluoroethylene with a copolymerizable modifier in an aqueous medium containing a polymerization initiator and a dispersant to produce a modified tetrafluoroethylene polymer containing 0.001 to 2 wt.% of the copolymerizable modifier based on the weight of the polymer, a process for producing the modified tetrafluoroethylene polymer characterized in that: (1) chlorotrifluoroethylene is used as said copolymerizable modifier, (2) at least 50 wt.% of the copolymerizable modifier to be incorporated into the polymer is introduced into the polymerization system after 70 wt.% of the polymer to be finally formed has been formed, and (3) after 90 wt.% of the polymer to be finally formed has been formed, the concentration of said copolymerizable modifier is maintained at at least 0.01 mol.% based on the total amount of tetrafluoroethylene and the modifier in the polymerization system.
In a process for polymerization of tetrafluoroethylene with a copolymerizable modifier in an aqueous medium containing a polymerization initiator and a dispersant to produce a modified tetrafluoroethylene polymer containing 0.001 to 2 wt.% of the copolymerizable modifier based on the weight of the polymer, a process for producing the modifier tetrafluoroethylene polymer characterized in that: (1) chlorotrifluoroethylene is used as said copolymerizable modifier, (2) at least 50 wt.% of the copolymerizable modifier to be incorporated into the polymer is introduced into the polymerization system after 70 wt.% of the polymer to be finally formed has been formed, at least 50 wt.% of the copolymerizable modifier to be incorporated into the polymer thus being contained in the shell portion of the particles of the polymer, and (3) after 90 wt.% of the polymer to be finally formed has been formed, the concentration of said copolymerizable modifier is maintained at at least 0.01 mol.% based on the total amount of tetrafluoroethylene and the modifier in the polymerization system, the outer most portion of particles, corresponding to at most 10 wt.% of the polymer to be finally obtained, thus containing the copolymerizable modifier in an amount of at least 0.01 mol.%.
Claim 2
Dependent Claim
198 words
In a process for polymerization of tetrafluoroethylene with a copolymerizable modifier in an aqueous medium containing a polymerization initiator and a dispersant to produce a modified tetrafluoroethylene polymer containing 0.001 to 2 wt.% of the copolymerizable modifier based on the weight of the polymer, a process for producing the modifier tetrafluoroethylene polymer characterized in that: (1) chlorotrifluoroethylene is used as said copolymerizable modifier, (2) at least 50 wt.% of the copolymerizable modifier to be incorporated into the polymer is introduced into the polymerization system after 70 wt.% of the polymer to be finally formed has been formed, at least 50 wt.% of the copolymerizable modifier to be incorporated into the polymer thus being contained in the shell portion of the particles of the polymer, and (3) after 90 wt.% of the polymer to be finally formed has been formed, the concentration of said copolymerizable modifier is maintained at at least 0.01 mol.% based on the total amount of tetrafluoroethylene and the modifier in the polymerization system, the outer most portion of particles, corresponding to at most 10 wt.% of the polymer to be finally obtained, thus containing the copolymerizable modifier in an amount of at least 0.01 mol.%.
Claim 3
Dependent Claim
12 words
A modified tetrafluoroethylene polymer produced by the process claimed in claim 1.