Catalyst manufacture
Assignee: BASF Catalysts LLC
•
Filing: 1977-04-29
•
Granted: 1979-01-16
•
Expires: 1997-04-29
Abstract
Abstract Catalysts are made which have a catalytically-active composite containing a catalytically-promoting metal component and a high surface area, refractory oxide support, deposited on a macrosize carrier. The catalytically-active composite is made by combining a solution of a water-soluble, catalytically-promoting metal component with a finely divided, high area, refractory oxide which is sufficiently dry to absorb essentially all of said solution. The catalytically-promoting metal component of the resulting composite is converted to water-insoluble form while the composite is essentially devoid of unabsorbed solution. The composite is comminuted in the presence of an aqueous medium which is preferably acidic. The resulting slurry is used to deposit the catalytically-promoting metal-containing solids on the macrosize carrier, and the resulting material is dried and may be calcined.
Inventors
- 👤 Saul G. Hindin
- 👤 Joseph C. Dettling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:59
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J37/00; B01J37/02; B01J37/0215
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
90 words
A method of manufacturing a composition having a water insoluble catalytically promoting component thereon, which method consists essentially of mixing a solution of a water-soluble, catalytically-promoting metal component and finely-divided, high surface area, refractory oxide which is sufficiently dry to absorb essentially all of said solution, converting said catalytically-promoting metal component in the resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, comminuting said water-insoluble, catalytically-promoting metal-refractory oxide material as a slurry, depositing the slurry on a solid, macrosize carrier, and drying the resulting composite.
Claim 2
Independent Claim
90 words
A method of manufacturing a composition having a water insoluble catalytically promoting component thereon, which method consists essentially of mixing a solution of a water-soluble, catalytically-promoting metal component and finely-divided, high surface area, refractory oxide which is sufficiently dry to absorb essentially all of said solution, converting said catalytically-promoting metal component in the resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, comminuting said water-insoluble, catalytically-promoting metal-refractory oxide material as a slurry, depositing the slurry on a solid, macrosize carrier, and drying the resulting composite.
Claim 3
Dependent Claim
11 words
The method of claim 1 in which said slurry is acidic.
Claim 4
Dependent Claim
17 words
The method of claim 1 in which the catalytically-promoting metal component is comprised of platinum group metal.
Claim 5
Dependent Claim
26 words
The method of claim 3 wherein said refractory oxide comprises an activated alumina having a surface area of at least about 75 square meters per gram.
Claim 6
Dependent Claim
26 words
The method of claim 4 wherein said comminuting provides a slurry in which most of the solids have particle sizes of less than about 10 microns.
Claim 7
Dependent Claim
15 words
The method of claim 5 wherein said platinum group metal component is comprised of platinum.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein said slurry contains acetic acid.
Claim 9
Dependent Claim
22 words
The method of claim 1 wherein said carrier comprises a monolithic ceramic or metallic structure having a plurality of flow channels therethrough.
Claim 10
Dependent Claim
21 words
The method of claim 8 wherein the water-insoluble catalytically-promoting metal component is comprised of platinum group metal and base metal oxide.
Claim 11
Dependent Claim
14 words
The method of claim 9 wherein the platinum group metal is comprised of platinum.
Claim 12
Dependent Claim
15 words
The method of claim 10 wherein the base metal oxide is comprised of nickel oxide.
Claim 13
Independent Claim
128 words
A method of manufacturing a composition having a water insoluble catalytically promoting component thereon, which method consists essentially of mixing an aqueous solution of a water-soluble, platinum group metal component and finely-divided, high surface area, calcined alumina which is sufficiently dry to absorb essentially all of said solution, converting said platinum group metal component of resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, comminuting said water-insoluble, platinum group metal-alumina composite in an aqueous, acidic slurry to provide a slurry in which most of the solids have a particle size of less than about 10 microns, depositing the slurry on a solid, macrosize carrier having a total surface area of less than about 1 square meter per gram, and drying the resulting composite.
Claim 14
Independent Claim
128 words
A method of manufacturing a composition having a water insoluble catalytically promoting component thereon, which method consists essentially of mixing an aqueous solution of a water-soluble, platinum group metal component and finely-divided, high surface area, calcined alumina which is sufficiently dry to absorb essentially all of said solution, converting said platinum group metal component of resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, comminuting said water-insoluble, platinum group metal-alumina composite in an aqueous, acidic slurry to provide a slurry in which most of the solids have a particle size of less than about 10 microns, depositing the slurry on a solid, macrosize carrier having a total surface area of less than about 1 square meter per gram, and drying the resulting composite.
Claim 15
Dependent Claim
22 words
The method of claim 12 wherein said carrier is a monolithic ceramic or metallic structure having a plurality of flow channels therethrough.
Claim 16
Dependent Claim
15 words
The method of claim 13 wherein said platinum group metal component is comprised of platinum.
Claim 17
Dependent Claim
14 words
The method of claim 14 wherein said slurry contains a base metal oxide component.
Claim 18
Dependent Claim
16 words
The method of claim 15 wherein said base metal oxide component is comprised of nickel oxide.
Claim 19
Dependent Claim
22 words
The method of claim 13 wherein said water-soluble platinum group metal component comprises an acidic rhodium compound and a basic platinum compound.
Claim 20
Dependent Claim
14 words
The method of claim 13 wherein said slurry contains acetic acid during said comminution.
Claim 21
Independent Claim
132 words
A method of manufacturing a composition having a water-insoluble catalytically-promoting component thereon, which method consists essentially of the steps of (a) mixing an aqueous solution of a water-soluble, catalytically-promoting metal component and finely-divided, high surface area, refractory oxide which is sufficiently dry to absorb essentially all of said solution, (b) converting said catalytically-promoting metal component in the resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, (c) repeating steps (a) and (b) while using a different catalytically-promoting metal and a separate portion of a finely-divided, high surface area, refractory oxide than used in steps (a) and (b), comminuting the products of steps (b) and (c) either separately or together, in an aqueous slurry, depositing the comminuted products on a solid, macrosize carrier, and drying the resulting composite.
Claim 22
Independent Claim
132 words
A method of manufacturing a composition having a water-insoluble catalytically-promoting component thereon, which method consists essentially of the steps of (a) mixing an aqueous solution of a water-soluble, catalytically-promoting metal component and finely-divided, high surface area, refractory oxide which is sufficiently dry to absorb essentially all of said solution, (b) converting said catalytically-promoting metal component in the resulting composite to water-insoluble form while said composite remains essentially devoid of free liquid, (c) repeating steps (a) and (b) while using a different catalytically-promoting metal and a separate portion of a finely-divided, high surface area, refractory oxide than used in steps (a) and (b), comminuting the products of steps (b) and (c) either separately or together, in an aqueous slurry, depositing the comminuted products on a solid, macrosize carrier, and drying the resulting composite.
Claim 23
Dependent Claim
28 words
The method of claim 19 wherein said slurry is acidic and the macrosize carrier has a total surface area of less than about 5 square meters per gram.
Claim 24
Dependent Claim
13 words
The method of claim 20 wherein said refractory oxide is comprised of alumina.
Claim 25
Dependent Claim
28 words
The method of claim 21 in which one of said catalytically-promoting metal components is comprised of base metal component and another is comprised of platinum group metal component.
Claim 26
Dependent Claim
16 words
The method of claim 22 in which said base metal component is comprised of nickel oxide.
Claim 27
Dependent Claim
12 words
A method of claim 1 in which said resulting composite is calcined.
Claim 28
Dependent Claim
12 words
A method of claim 6 in which said resulting composite is calcined.
Claim 29
Dependent Claim
12 words
A method of claim 11 in which said resulting composite is calcined.
Claim 30
Dependent Claim
12 words
A method of claim 15 in which said resulting composite is calcined.
Claim 31
Dependent Claim
12 words
A method of claim 17 in which said resulting composite is calcined.
Claim 32
Dependent Claim
21 words
A method of claim 24 in which said resulting composite is calcined at a temperature of at least about 250° C.
Claim 33
Dependent Claim
21 words
A method of claim 25 in which said resulting composite is calcined at a temperature of at least about 250° C.
Claim 34
Dependent Claim
21 words
A method of claim 26 in which said resulting composite is calcined at a temperature of at least about 250° C.
Claim 35
Dependent Claim
21 words
A method of claim 27 in which said resulting composite is calcined at a temperature of at least about 250° C.
Claim 36
Dependent Claim
21 words
A method of claim 28 in which said resulting composite is calcined at a temperature of at least about 250° C.
Claim 37
Dependent Claim
12 words
A method of claim 19 in which said resulting composite is calcined.
Claim 38
Dependent Claim
20 words
A method of claim 34 in which said resulting composite is calcined at a temperature of at least 250° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-15 | 1982-07-17 | 1983-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-15 | 1986-07-17 | 1987-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-15 | 1990-07-17 | 1991-01-16 | $7700.00 | Window Closed / Lapsed |