Process for the preparation of semi-rigid polyurethane foam having exceptional shock-absorbing properties and vehicle bumpers thereof
Assignee: Nouryon Surface Chemistry AB
•
Filing: 1976-12-27
•
Granted: 1979-01-16
•
Expires: 1996-12-27
Abstract
Abstract A process is provided for producing semi-rigid polyurethane foams having exceptional shock-absorbing properties, even after repeated compression, prepared by the reaction of a polyisocyanate; a polyether polyol having a molecular weight within the range from about 2,000 to about 10,000; from about 1 to about 5% by weight of water per part by weight of polyether polyol; from about 1 to about 6% by weight of urea and/or thiourea per part by weight of polyether polyol; and a cross-linking compound having at least three active hydrogen atoms per molecule that are reactive with isocyanate groups and having a molecular weight below about 1000 in an amount from about 5 to about 25% by weight per part by weight of polyether polyol; the amount of polyisocyanate being selected to give an isocyanate index within the range from about 0.7 to about 1.4. The process provides polyurethane foams that have a cellular structure that remains undamaged under compression as high as 60% at temperatures within the range from about +60° C to about -40° C, and the consequent deformation is less than 1% even after ten compressions of at lest 50% in rapid succession. Accordingly, the invention further provides vehicle bumpers having an impact-receiving layer of this polyurethane foam, and that meet the requirements of FMVSS 215.
Inventors
- 👤 Frank W. Lindewall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 06:21
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/30; C08G18/38; C08G18/3819; C08G18/3823; C08G18/3829; C08G18/3855; C08G18/3857; C08G2110/00; C08G2110/0016; C08G2110/0083; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249991; Y10T428/249992; Y10T428/249993
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
207 words
A process for preparing semi-rigid polyurethane foam having a high shock-absorbent capability that remains substantially undamaged by high compression even after compressions as high as 60% over a wide range of temperatures, and which does not acquire a permanent deformation or deformatcion set in excess of 1% even after rapidly repeated compressions, which comprises reacting a polyisocyanate; a polyether polyol having a molecular weight within the range from about 2,000 to about 10,000; from about 1 to about 5% by weight of water per part by weight of polyether polyol; from about 1 to about 6% by weight of at least one member selected from the group consisting of urea and thiourea per part by weight of polyether polyol; and a cross-linking compound having at least three active hydrogen atoms per molecule that are reactive with isocyanate groups and having a molecular weight below about 1000 in an amount from about 5 to about 25% by weight per part by weight of polyether polyol; the amount of polyisocyanate being selected to give an isocyanate index within the range from about 0.7 to about 1.4 at a temperature at which reaction proceeds within the range from about 30° to about 130° C until a polyurethane foam is produced.
Claim 2
Dependent Claim
207 words
A process for preparing semi-rigid polyurethane foam having a high shock-absorbent capability that remains substantially undamaged by high compression even after compressions as high as 60% over a wide range of temperatures, and which does not acquire a permanent deformation or deformatcion set in excess of 1% even after rapidly repeated compressions, which comprises reacting a polyisocyanate; a polyether polyol having a molecular weight within the range from about 2,000 to about 10,000; from about 1 to about 5% by weight of water per part by weight of polyether polyol; from about 1 to about 6% by weight of at least one member selected from the group consisting of urea and thiourea per part by weight of polyether polyol; and a cross-linking compound having at least three active hydrogen atoms per molecule that are reactive with isocyanate groups and having a molecular weight below about 1000 in an amount from about 5 to about 25% by weight per part by weight of polyether polyol; the amount of polyisocyanate being selected to give an isocyanate index within the range from about 0.7 to about 1.4 at a temperature at which reaction proceeds within the range from about 30° to about 130° C until a polyurethane foam is produced.
Claim 3
Dependent Claim
32 words
A process according to claim 1, which comprises first preparing a prepolymer by reacting the polyether polyol with a stoichiometric excess of the polyisocyanate to form a prepolymer containing isocyanate terminal groups.
Claim 4
Dependent Claim
32 words
A process according to claim 1, which comprises first preparing a prepolymer by reacting the polyisocyanate with a stoichiometric excess of the polyether polyol to form a prepolymer containing hydroxyl terminal groups.
Claim 5
Dependent Claim
12 words
A process according to claim 1 in which the member is urea.
Claim 6
Dependent Claim
12 words
A process according to claim 1 in which the member is thiourea.
Claim 7
Dependent Claim
28 words
A process according to claim 1 in which the cross-linking compound contains the active hydrogens reactive with isocyanate groups attached to nitrogen as a part of amino groups.
Claim 8
Dependent Claim
28 words
A process according to claim 1 in which the cross-linking compound contains the active hydrogens reactive with isocyanate groups attached to oxygen as a part of hydroxyl groups.
Claim 9
Dependent Claim
32 words
A process according to claim 1 in which the cross-linking compound contains the active hydrogens reactive with isocyanate groups attached to nitrogen and oxygen as a mixture of amino and hydroxyl groups.
Claim 10
Dependent Claim
14 words
A process according to claim 1 in which the cross-linking compound is a polyol.
Claim 11
Dependent Claim
24 words
A process according to claim 1 in which the cross-linking compound is a polyoxyalkylene polyol obtained by condensation of an alkylene oxide with polyol.
Claim 12
Dependent Claim
34 words
A process according to claim 1 in which the reaction mixture also contains an amount of a strong base within the range from about 0.001 to about 1% by weight of the polyether polyol.
Claim 13
Dependent Claim
35 words
A proces according to claim 11 in which the base is selected from the group consisting of the alkali metal and alkaline earth metal hydroxides, alkaline-reacting inorganic salts of these metals, and organic amine bases.
Claim 14
Dependent Claim
58 words
A process according to claim 1 in which the polyether polyol is an adduct of an alkylene oxide to a polyol having at least two hydroxyl groups with reactive hydrogen atoms, the alkylene oxide having from two to four carbon atoms and the polyol having from two to six hydroxyl groups and from two to six carbon atoms.
Claim 15
Dependent Claim
38 words
A process according to claim 1 in which the polyether polyol is an adduct of an alkylene oxide to an amine or aminoalcohol having at least one amine and one hydroxyl group or at least two amine groups.
Claim 16
Dependent Claim
38 words
A process according to claim 1 in which the organic polyisocyanate has at least two isocyanate groups and is selected from the group consisting of aliphatic, heterocyclic, cycloaliphatic, and mixed aliphatic aromatic, aliphatic heterocyclic, and aliphatic cycloaliphatic polyisocyanates.
Claim 17
Dependent Claim
13 words
A process according to claim 15, in which the polyisocyanate is toluene diisocyanate.
Claim 18
Dependent Claim
84 words
A process according to claim 15, in which the polyisocyanate has at least two benzene rings, with one isocyanate group per ring, the benzene rings being interconnected by a member selected from the group consisting of ether, sulfone, sulfoxide, methylene, ethylene, propylene, and carbonyl groups, and having the general structure: ##STR3## where Y is a linking group selected from the group consisting of ##STR4## n is a number within the range from about 0.2 to about 1.5 representing an average of the species present.
Claim 19
Dependent Claim
26 words
A process according to claim 1 in which the reaction between the polyisocyanate and the polyether polyol is carried out in the presence of a catalyst.
Claim 20
Dependent Claim
13 words
A process according to claim 18 in which the catalyst is an amine.
Claim 21
Dependent Claim
14 words
A process according to claim 18 in which the catalyst is an organometallic compound.
Claim 22
Dependent Claim
27 words
A process according to claim 1 in which the reaction mixture also includes a blowing agent capable of generating an inert gas under the reaction conditions used.
Claim 23
Dependent Claim
59 words
A polyurethane foam obtained by the process of claim 1, having a cellular structure that remains undamaged by high compression at temperatures within the range from about +60° C to about -40° C, even after compressions as high at 60%, and a consequent deformation of less than 1%, even after ten compressions of at least 50%, in rapid succession.
Claim 24
Dependent Claim
57 words
A vehicle bumper comprising a bumper support, and an impact-absorbing facing layer comprising a polyurethane foam of claim 22, having a density within the range from about 50 to about 150 g/dm 3 and a deformation noted 30 minutes after compression not exceeding 1% over a temperature range of from about +60° C to about -40° C.
References Cited (Backward Citations)
US3108975A
Cited
US3348597A
Cited
US3493257A
Cited
US3728288A
Cited
US3836487A
Cited
US3734557A
Cited
US3801518A
Cited
US3836424A
Cited
US3852150A
Cited
US3939106A
Cited
US3865417A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-15 | 1982-07-17 | 1983-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-15 | 1986-07-17 | 1987-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-15 | 1990-07-17 | 1991-01-16 | $7700.00 | Window Closed / Lapsed |