Manufacture of magnetic discs
Assignee: BASF SE
•
Filing: 1975-12-16
•
Granted: 1979-01-09
•
Expires: 1995-12-16
Abstract
Abstract The invention relates to an improved process for the manufacture of magnetic discs carrying very thin magnetic layers, by applying a fluid dispersion of magnetic materials in a binder mixture to rigid base discs by the spin-coating process. Above the side of the base disc which is to be provided with the magnetic layer, there are arranged means which produce an aerodynamic boundary layer above the discs during rotation of the latter. This avoids the formation of surface irregularities and of coating streaks during production of the layer by spin-coating.
Inventors
- 👤 Eberhard Koester
- 👤 Paul Deigner
- 👤 Roland Falk
- 👤 Karl Uhl
- 👤 Dieter Schaefer
- 👤 Dieter Mayer
- 👤 Herbert Motz
- 👤 Peter Felleisen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:01
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/84; G11B5/842
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
184 words
A process for the production of magnetic layers for magnetic discs which comprises: applying a pourable dispersion of a finely divided magnetic pigment in a solution of an organic binder in a volatile solvent to a rotating base disc, distributing the dispersion to form a thin layer by rotating the base disc, and drying and curing the layer, wherein said process further comprises: rotating along with said base disc and in substantially parallel, axially-spaced relationship thereto, a separate, rigid, generally disc-shaped member having a surface area which is at least equal to that of the base disc and rotates at a distance of up to 20 mm above the surface of the base disc to be coated, so as to define between the surface of said base disc, on which the magnetic layer is to be formed, and the opposing surface of said member a generally cylindrical air space providing on said surface of said disc an aerodynamic boundary layer which rotates in substantially stationary relationship to said surface of said disc, whereby the formation of coating streaks on said layer is substantially avoided.
Claim 2
Dependent Claim
184 words
A process for the production of magnetic layers for magnetic discs which comprises: applying a pourable dispersion of a finely divided magnetic pigment in a solution of an organic binder in a volatile solvent to a rotating base disc, distributing the dispersion to form a thin layer by rotating the base disc, and drying and curing the layer, wherein said process further comprises: rotating along with said base disc and in substantially parallel, axially-spaced relationship thereto, a separate, rigid, generally disc-shaped member having a surface area which is at least equal to that of the base disc and rotates at a distance of up to 20 mm above the surface of the base disc to be coated, so as to define between the surface of said base disc, on which the magnetic layer is to be formed, and the opposing surface of said member a generally cylindrical air space providing on said surface of said disc an aerodynamic boundary layer which rotates in substantially stationary relationship to said surface of said disc, whereby the formation of coating streaks on said layer is substantially avoided.
Claim 3
Dependent Claim
22 words
A process as set forth in claim 1 wherein the dried and cured layer has a thickness of from 1 to 10μ.
Claim 4
Dependent Claim
64 words
A process as set forth in claim 1, wherein two base discs are spaced at a distance of up to 20 mm from one another so as to produce an aerodynamic boundary layer therebetween, the dispersion being simultaneously applied to the two facing disc surfaces and a uniform thin layer being formed on each base disc by effecting rotation of the two base discs.
Claim 5
Dependent Claim
23 words
A process as set forth in claim 1, wherein the finely divided magnetic pigment has a particle size from about 0.2 to 1μ.
Claim 6
Dependent Claim
17 words
A process as set forth in claim 1 wherein the organic binder is a heat curable binder.
Claim 7
Dependent Claim
20 words
A process as set forth in claim 1 wherein the dispersion has a viscosity of from 40 to 200 cp.
Claim 8
Dependent Claim
22 words
A process as set forth in claim 1 wherein the weight ratio of magnetic pigment to binder is from 2 to 10:1.
Claim 9
Dependent Claim
24 words
A process as set forth in claim 1 wherein the dispersion is applied to the rotating disc by pouring or by spraying through nozzles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-08 | 1982-07-10 | 1983-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-08 | 1986-07-10 | 1987-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-08 | 1990-07-10 | 1991-01-09 | $7700.00 | Window Closed / Lapsed |