Method for forming a polyethylene layer on a substrate
Assignee: CORDOTEX
•
Filing: 1977-03-16
•
Granted: 1979-01-09
•
Expires: 1997-03-16
Abstract
Abstract Adhesion between extruded polyethylene film and a substrate consisting of paper or paper lined metal foil is improved when the substrate and film are pressed together by passing through rollers which also cool the film to below its softening temperature, wherein at least one of said rolls which is brought into contact with the polyethylene coating is moistened on its rolling surface with a liquid having a critical surface tension below 73 dyne/cm, a boiling point below 100° C and consisting of a mixture of water and between 10% and 50% ethyl alcohol.
Inventors
- 👤 Erwin W. Wartenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:34
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/10; B05; B05D; B05D1/00; B05D1/26; B32B27/32; B32B37/00; B32B37/08; B05D2203/00; B05D2203/22; B05D2252/00; B05D2252/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
156 words
A process for the coating of a substrate, consisting of paper or paper lined with a metal foil, with polyethylene in which the polyethylene is extruded to a thin film which, while it is still warm, is brought into contact with the substrate and, with simultaneous cooling to a temperature below the softening temperature of the polyethylene, is pressed together with the substrate by passing the substrate and the extruded polyethylene film through cooperating rolls wherein at least one roll which is brought into contact with the polyethylene coating is a metal chill roll which is moistened on its rolling surface with a liquid having a critical surface tension below 73 dyne/cm and a boiling point below 100° C., and consisting of a mixture of water and between about 10% and about 50% ethyl alcohol, whereby an uninterrupted liquid layer is applied to the whole contact surface of the roll or rolls with the polyethylene coating.
Claim 2
Dependent Claim
156 words
A process for the coating of a substrate, consisting of paper or paper lined with a metal foil, with polyethylene in which the polyethylene is extruded to a thin film which, while it is still warm, is brought into contact with the substrate and, with simultaneous cooling to a temperature below the softening temperature of the polyethylene, is pressed together with the substrate by passing the substrate and the extruded polyethylene film through cooperating rolls wherein at least one roll which is brought into contact with the polyethylene coating is a metal chill roll which is moistened on its rolling surface with a liquid having a critical surface tension below 73 dyne/cm and a boiling point below 100° C., and consisting of a mixture of water and between about 10% and about 50% ethyl alcohol, whereby an uninterrupted liquid layer is applied to the whole contact surface of the roll or rolls with the polyethylene coating.
Claim 3
Dependent Claim
22 words
A process according to claim 1, wherein the amount of ethyl alcohol in the liquid is between about 10% and about 35%.
Claim 4
Dependent Claim
18 words
A process according to claim 1, wherein the amount of ethyl alcohol in the liquid is about 25%.
Claim 5
Dependent Claim
20 words
A process according to claim 1, wherein the liquid is applied to the roll or rolls by a spraying process.
Claim 6
Dependent Claim
31 words
A process according to claim 1, wherein the liquid is fed to said roll by dipping parts of the roll into a vessel below the roll, which vessel contains the liquid.
Claim 7
Dependent Claim
30 words
A process according to claim 1, wherein the application of said liquid to the said roll is made by means of a coating device that is contacted with the roll.
Claim 8
Dependent Claim
42 words
A process according to claim 1, wherein the critical surface tension of said liquid is adjusted by admixture of sufficient ethyl alcohol to reduce the surface tension to a value approximately corresponding to the critical surface tension of the polyethylene thermoplastic material.
References Cited (Backward Citations)
US2877140A
Cited
US3013900A
Cited
US3075868A
Cited
US3215578A
Cited
US3392076A
Cited
US3640788A
Cited
US3448000A
Cited
US3589975A
Cited
US3498865A
Cited
US3700525A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-08 | 1982-07-10 | 1983-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-08 | 1986-07-10 | 1987-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-08 | 1990-07-10 | 1991-01-09 | $7700.00 | Window Closed / Lapsed |