Preparation of liquid epoxy resins from bisphenols
Assignee: Societa Italiana Resine SpA SIR
•
Filing: 1976-12-07
•
Granted: 1979-01-02
•
Expires: 1996-12-07
Abstract
Abstract A liquid epoxy resin is produced by gradually feeding an aqueous solution of alkali metal hydroxide into a solution of bisphenol-A in epichlorohydrin, while maintaining the reaction medium at boiling point, distilling off water in the form of an azeotrope with epichlorohydrin and recycling the latter, and maintaining a water content of from 0.1 to 0.7 wt.% and a pH value between 7 and 9 in said reaction medium. The liquid epoxy resins thus obtained have low values of the viscosity, epoxy equivalent and hydrolyzable chlorine content.
Inventors
- 👤 Silvio Vargiu
- 👤 Mario Pitzalis
- 👤 Giancarlo Crespolini
- 👤 Gino Giuliani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:06
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/02; C08G59/04; C08G59/06; C08G59/063
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
215 words
A method for the preparation of a low viscosity, low hydrolyzable chlorine content liquid epoxy resin corresponding to the general formula: ##STR2## wherein R is the bisphenyl radical of bisphenol-A and n has an average value of from 0 to about 0.07 by reaction of epichlorohydrin with bisphenol-A in the presence of an alkali metal hydroxide, with comprises: (a) gradually feeding an aqueous solution of alkali metal hydroxide into a mixture of epichlorohydrin and bisphenol-A in a molar ratio of at least 10:1, until the ratio between the moles of alkali metal hydroxide fed in and the number of phenolic hydroxyl groups in said mixture is from 1:1 to 1.05:1, while maintaining the reaction medium at boiling point, distilling off water in the form of an azeotropic mixture with epichlorohydrin and recycling the distilled epichlorohydrin into the reaction medium, the addition of alkali metal hydroxide and the distillation conditions being so adjusted as to maintain in the reaction medium a content of liquid water of from 0.1 to 0.7 wt.% and a pH value between 7 and 9, wherein the reaction medium is boiled at a temperature of from 70° to 90° C. and at a pressure of from 150 to 350 mm Hg; and (b) recovering the liquid epoxy resin from the reaction products.
Claim 2
Independent Claim
215 words
A method for the preparation of a low viscosity, low hydrolyzable chlorine content liquid epoxy resin corresponding to the general formula: ##STR2## wherein R is the bisphenyl radical of bisphenol-A and n has an average value of from 0 to about 0.07 by reaction of epichlorohydrin with bisphenol-A in the presence of an alkali metal hydroxide, with comprises: (a) gradually feeding an aqueous solution of alkali metal hydroxide into a mixture of epichlorohydrin and bisphenol-A in a molar ratio of at least 10:1, until the ratio between the moles of alkali metal hydroxide fed in and the number of phenolic hydroxyl groups in said mixture is from 1:1 to 1.05:1, while maintaining the reaction medium at boiling point, distilling off water in the form of an azeotropic mixture with epichlorohydrin and recycling the distilled epichlorohydrin into the reaction medium, the addition of alkali metal hydroxide and the distillation conditions being so adjusted as to maintain in the reaction medium a content of liquid water of from 0.1 to 0.7 wt.% and a pH value between 7 and 9, wherein the reaction medium is boiled at a temperature of from 70° to 90° C. and at a pressure of from 150 to 350 mm Hg; and (b) recovering the liquid epoxy resin from the reaction products.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said molar ratio between epichlorohydrin and bisphenol-A does not exceed 15:1.
Claim 4
Dependent Claim
18 words
The method of claim 1, wherein said molar ratio between epichlorohydrin and bisphenol-A is from 12:1 to 13:1.
Claim 5
Dependent Claim
21 words
The method of claim 1, wherein said alkali metal hydroxide is selected from the group consisting of sodium and potassium hydroxides.
Claim 6
Dependent Claim
19 words
The method of claim 1, wherein said aqueous solution contains from 40 to 50 wt.% of alkali metal hydroxide.
Claim 7
Dependent Claim
30 words
The method of claim 1, wherein said water content is maintained at a value of from 0.4 to 0.6 wt.% and said pH at a value between 7 and 8.
Claim 8
Dependent Claim
20 words
The method of claim 1, wherein said aqueous solution is added for a period of from 3 to 6 hours.
Claim 9
Dependent Claim
39 words
The method of claim 1, wherein the reaction medium is kept boiling for a period of from 10 to 20 minutes upon completion of the alkali metal hydroxide addition, thus distilling off the residual water present in said medium.
Claim 10
Dependent Claim
38 words
The method of claim 1, wherein during said addition the reaction medium is continuously circulated through a self-cleansing filter or a centrifuge, thereby to substantially remove the alkali metal chloride which forms as a by-product of the reaction.
Claim 11
Dependent Claim
14 words
The method of claim 1, wherein said water is continuously removed throughout the process.
Claim 12
Dependent Claim
23 words
The method of claim 1, wherein said liquid epoxy resin has a viscosity of from 6,000 about 8,000 cps, measured at 25° C.
Claim 13
Dependent Claim
9 words
The method of claim 1, wherein n is 0.
Claim 14
Dependent Claim
48 words
The method of claim 11, wherein said alkali metal hydroxide is sodium hydroxide and wherein said liquid epoxy resin has a hydrolizable chlorine content of from 0.1 to 0.02% by weight, the molar amount of said sodium hydroxide being up to 5% in excess of the stoichiometric amount.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |