US4132559A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Starting material for high-strength hydrothermally treated objects, and a method of producing such material
Assignee: Advanced Mineral Research AB
•
Filing: 1977-04-26
•
Granted: 1979-01-02
•
Expires: 1997-04-26
Abstract
Abstract A starting material for the manufacture of shaped and hydrothermally hardened products is composed of a binding agent comprising finely-divided olivine having a specific outer surface of at least 25 000 cm 2 /cm 3 , measured according to the permeability method, and finely-divided silica material in a quantity which is at most equal to the solid volume of said olivine and a ballast material in an amount of 50 - 80% by volume of the starting material and comprising particulate ultra-basic rock or slag material having a particle size of 80% smaller than 200 - 1000 μm.
Inventors
- 👤 Per G. Kihlstedt
- 👤 Hedvig E. B. Hassler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:08
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/18; C04B28/184
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
129 words
A starting material for manufacturing shaped and hydrothermally hardened objects, wherein the starting material mainly comprises a mixture of (a) material of the olivine type finely divided to a powdered product having a specific outer surface of at least approximately 25 000 cm 2 /cm 3 , measured in accordance with the permeability method, (b) finely divided silica material in a quantity which is at most equal to the solid volume of said powdered product and having such a small particle size that at least a predominant portion of said silica reacts during the hydrothermal treatment process, (c) ultra-basic rock and/or ultra-basic slag material finely divided to a particle size of 80% smaller than 200-1000 μm and comprising 50 - 80% of the total solid volume of the mixture.
Claim 2
Dependent Claim
129 words
A starting material for manufacturing shaped and hydrothermally hardened objects, wherein the starting material mainly comprises a mixture of (a) material of the olivine type finely divided to a powdered product having a specific outer surface of at least approximately 25 000 cm 2 /cm 3 , measured in accordance with the permeability method, (b) finely divided silica material in a quantity which is at most equal to the solid volume of said powdered product and having such a small particle size that at least a predominant portion of said silica reacts during the hydrothermal treatment process, (c) ultra-basic rock and/or ultra-basic slag material finely divided to a particle size of 80% smaller than 200-1000 μm and comprising 50 - 80% of the total solid volume of the mixture.
Claim 3
Dependent Claim
38 words
A material according to claim 1, wherein at least part of the olivine-type material is finely divided to form a powdered product having a specific outer surface of 50 000 - 200 000 cm 2 /cm 3 .
Claim 4
Dependent Claim
22 words
A material according to claim 1, wherein the silica material comprises 1 - 7%, of the total solid volume of the mixture.
Claim 5
Dependent Claim
30 words
A material according to claim 1, wherein the ultra-basic rock and/or the ultra-basic slag material has a particle size of the order of magnitude of 80% smaller than 500 μm.
Claim 6
Dependent Claim
26 words
A material according to claim 1, wherein the ultra-basic rock and/or the ultra-basic slag material comprises approximately 65% of the total solid volume of the mixture.
Claim 7
Dependent Claim
21 words
A material according to claim 1, wherein the ultra-basic rock and/or the ultra-basic slag material comprises material of the olivine type.
Claim 8
Dependent Claim
29 words
A material according to claim 1 which further comprises a strongly basic substance in a quantity sufficient to increase the pH of the mixture to a value above 10.
Claim 9
Dependent Claim
11 words
A material according to claim 1, wherein the mixture is granulated.
Claim 10
Independent Claim
137 words
A method of producing a starting material for the manufacture of shaped and hydrothermally hardened products, comprising the steps of finely dividing a material of the olivine type to a powdered product having a specific outer surface of at least 25 000 cm 2 /cm 3 , measured according to the permeability method, and mixing said product with finely-divided silica material in a quantity which is at most equal to the solid volume of said powdered product and having a particle size of such fineness that at least a predominant portion of the silica material will react during the hydrothermal treatment process, and with ultra-basic rock and/or ultra-basic slag material finely divided to a particle size of 80% smaller than 200 - 1000 μm and comprising 50 - 80% of the total solid volume of the mixture.
Claim 11
Independent Claim
137 words
A method of producing a starting material for the manufacture of shaped and hydrothermally hardened products, comprising the steps of finely dividing a material of the olivine type to a powdered product having a specific outer surface of at least 25 000 cm 2 /cm 3 , measured according to the permeability method, and mixing said product with finely-divided silica material in a quantity which is at most equal to the solid volume of said powdered product and having a particle size of such fineness that at least a predominant portion of the silica material will react during the hydrothermal treatment process, and with ultra-basic rock and/or ultra-basic slag material finely divided to a particle size of 80% smaller than 200 - 1000 μm and comprising 50 - 80% of the total solid volume of the mixture.
Claim 12
Dependent Claim
30 words
A method according to claim 9, wherein the dividing step comprises the step of conducting at least part of the dividing step in a dry state in a vibration mill.
Claim 13
Dependent Claim
43 words
A method according to claim 9, wherein the dividing step comprises the step of finely dividing at least part of the olivine-type material to a powdered product having a specific outer surface of 50 000 - 200 000 cm 2 /cm 3 .
Claim 14
Dependent Claim
34 words
A method according to claim 9, wherein the mixing step comprises the step of admixing silica material in an amount of from about 1 to 7% of the total solid volume of the mixture.
Claim 15
Dependent Claim
30 words
A method according to claim 9, wherein the ultra-basic rock and/or the ultra-basic slag material has a particle size of the order of magnitude of 80% smaller than 500 μm.
Claim 16
Dependent Claim
41 words
A method according to claim 9, wherein the mixing step comprises the step of admixing the finely divided ultra-basic rock and/or the finely divided ultra-basic slag material in a quantity of approximately 65% of the total solid volume of the mixture.
Claim 17
Dependent Claim
21 words
A method according to claim 9, wherein said ultra-basic rock and/or ultra-basic slag material comprises a material of the olivine type.
Claim 18
Dependent Claim
35 words
A method according to claim 9, further comprising the step of adding to the mixture a strongly basic substance in a quantity sufficient to increase the pH of the mixture to a value above 10.
Claim 19
Dependent Claim
14 words
A method according to claim 9, further comprising the step of granulating the mixture.
Claim 20
Dependent Claim
15 words
Shaped and hydro-thermally hardened objects manufactured from a starting material as claimed in claim 1.
Claim 21
Dependent Claim
19 words
Shaped and hydro-thermally hardened objects manufactured from a starting material produced by the method as claimed in claim 9.
Claim 22
Dependent Claim
21 words
A material according to claim 3, wherein the silica material comprises approximately 3-4% of the total solid volume of the mixture.
Claim 23
Dependent Claim
32 words
The method according to claim 12, wherein the mixing step comprises the step of admixing the silica material in an amount of approximately 3-4% of the total solid volume of the mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |