US4132547A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing self-supporting fully activated iron electrodes by thermal reduction-sintering
Assignee: Northrop Grumman Corp
•
Filing: 1977-05-27
•
Granted: 1979-01-02
•
Expires: 1997-05-27
Abstract
Abstract A self-supporting electrode structure consisting of active material particles is made by: (1) mixing 100 parts of metallic iron particles, with between about 0.5 part to about 5.0 parts of a water soluble metal sulfate selected from MgSO 4 , CdSO 4 , MnSO 4 , ZnSO 4 , BaSO 4 , Cr 2 (SO 4 ) 3 , CuSO 4 , CaSO 4 , Li 2 SO 4 , their hydrates and mixtures, as an electrochemical activator, and an amount of water effective to form a thin coating of metal sulfate on the metallic iron particles, (2) sizing the mixture to between about 10 microns to about 275 microns average particle size, (3) pressing the coated iron particles, and (4) reducing and sintering the coated iron particles at between about 700° C to about 1,000° C, in a reducing atmosphere; to provide an interconnected self-supporting metallic electrode structure consisting solely of fully charged iron active material particles coated with the metal of the additive, said electrode being capable of immediate discharge.
Inventors
- 👤 Edward S. Buzzelli
- 👤 George R. Folser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:25
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/26; H01M4/30; H01M4/36; H01M4/48; H01M4/52; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
226 words
A method of making a self-supporting, fully activated electrode structure consisting of iron active material particles comprising the steps of: (A) mixing 100 parts of metallic iron particles, consisting of essentially pure Fe, with between about 0.5 part to about 5.0 parts of a water soluble metal sulfate additive, effective to activate the iron, selected from the group consisting of MgSO 4 , CdSO 4 , MnSO 4 , ZnSO 4 , BaSO 4 , Cr 2 (SO 4 ) 3 , CuSO 4 , CaSO 4 , Li 2 SO 4 , their hydrates and mixtures thereof, and an amount of water effective to form a thin coating of the metal sulfate on the surface of the metallic iron particles; and then (B) drying the mixture and sizing the mixture to provide particles having an average particle size of between about 10 microns to about 275 microns diameter; and then (C) pressing the coated metallic iron particles to provide a plaque; and then (D) reducing and sintering the plaque consisting of the coated metallic iron particles at between about 700° C to about 1,000° C, in a reducing atmosphere, to provide an interconnected, self-supporting metallic electrode structure consisting solely of fully charged metallic iron particles, consisting of essentially pure Fe, coated with the activator metal of the additive, said electrode being capable of immediate discharge.
Claim 2
Independent Claim
226 words
A method of making a self-supporting, fully activated electrode structure consisting of iron active material particles comprising the steps of: (A) mixing 100 parts of metallic iron particles, consisting of essentially pure Fe, with between about 0.5 part to about 5.0 parts of a water soluble metal sulfate additive, effective to activate the iron, selected from the group consisting of MgSO 4 , CdSO 4 , MnSO 4 , ZnSO 4 , BaSO 4 , Cr 2 (SO 4 ) 3 , CuSO 4 , CaSO 4 , Li 2 SO 4 , their hydrates and mixtures thereof, and an amount of water effective to form a thin coating of the metal sulfate on the surface of the metallic iron particles; and then (B) drying the mixture and sizing the mixture to provide particles having an average particle size of between about 10 microns to about 275 microns diameter; and then (C) pressing the coated metallic iron particles to provide a plaque; and then (D) reducing and sintering the plaque consisting of the coated metallic iron particles at between about 700° C to about 1,000° C, in a reducing atmosphere, to provide an interconnected, self-supporting metallic electrode structure consisting solely of fully charged metallic iron particles, consisting of essentially pure Fe, coated with the activator metal of the additive, said electrode being capable of immediate discharge.
Claim 3
Dependent Claim
88 words
The method of claim 1, wherein the additive is selected from the group consisting of MgSO 4 , 3CdSO 4 ·8H 2 O, MnSO 4 , ZnSO 4 , BaSO 4 , Cr 2 (SO 4 ) 3 ·H 2 O, CuSO 4 ·5H 2 O, CaSO 4 ·2H 2 O, Li 2 SO 4 ·H 2 O and mixtures thereof, and the iron particles are made from Fe 2 O 3 , thermally reduced in H 2 gas at between about 400° C to about 1,000° C.
Claim 4
Dependent Claim
37 words
The method of claim 1, wherein the additive is a mixture of MgSO 4 and 3CdSO 4 ·8H 2 O and the metallic iron particles are mixed with between 0.8 part to 3.0 parts of metal sulfate.
Claim 5
Dependent Claim
39 words
The method of claim 1, wherein the mixture is dried in step (B) for about 30 minutes to 120 minutes at about 25° C to about 75° C, and the reducing atmosphere in step (D) is H 2 gas.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein the electrode is about 50 mil to about 150 mil thick, and about 70% to about 95% porous.
Claim 7
Dependent Claim
27 words
The method of claim 1, where, in step (D), the iron and the metal of the additive undergo a solid state interdiffusion of atoms at their interface.
Claim 8
Dependent Claim
9 words
An electrode made by the method of claim 1.
Claim 9
Independent Claim
201 words
A method of making a self-supporting, fully activated electrode structure consisting of iron active material particles comprising the steps of: (A) mixing 100 parts of metallic iron particles, consisting of essentially pure Fe, with between about 0.8 part to about 3.0 parts of a water soluble metal sulfate additive, effective to activate the iron, selected from the group consisting of MgSO 4 , CdSO 4 , their hydrates and mixtures thereof, and an amount of water effective to form a thin coating of the metal sulfate on the surface of the metallic iron particles; and then (B) drying the mixture and sizing the mixture to provide particles having an average particle size of between about 10 microns to about 275 microns diameter; and then (C) pressing the coated metallic iron particles to provide a plaque; and then (D) reducing and sintering the plaque consisting of the coated metallic iron particles at between about 700° C to about 1,000° C, in a hydrogen gas reducing atmosphere, to provide an interconnected, self-supporting metallic electrode structure consisting solely of fully charged metallic iron particles, consisting of essentially pure Fe, coated with the activator metal of the additive, said electrode being capable of immediate discharge.
Claim 10
Independent Claim
201 words
A method of making a self-supporting, fully activated electrode structure consisting of iron active material particles comprising the steps of: (A) mixing 100 parts of metallic iron particles, consisting of essentially pure Fe, with between about 0.8 part to about 3.0 parts of a water soluble metal sulfate additive, effective to activate the iron, selected from the group consisting of MgSO 4 , CdSO 4 , their hydrates and mixtures thereof, and an amount of water effective to form a thin coating of the metal sulfate on the surface of the metallic iron particles; and then (B) drying the mixture and sizing the mixture to provide particles having an average particle size of between about 10 microns to about 275 microns diameter; and then (C) pressing the coated metallic iron particles to provide a plaque; and then (D) reducing and sintering the plaque consisting of the coated metallic iron particles at between about 700° C to about 1,000° C, in a hydrogen gas reducing atmosphere, to provide an interconnected, self-supporting metallic electrode structure consisting solely of fully charged metallic iron particles, consisting of essentially pure Fe, coated with the activator metal of the additive, said electrode being capable of immediate discharge.
Claim 11
Dependent Claim
26 words
The method of claim 8, wherein the additive is selected from the group consisting of MgSO 4 , 3CdSO 4 ·8H 2 O, and mixtures thereof.
Claim 12
Dependent Claim
27 words
The method of claim 8, where, in step (D), the iron and the metal of the additive undergo a solid state interdiffusion of atoms at their interface.
References Cited (Backward Citations)
US3066178A
Cited
US2871281A
Cited
US3148056A
Cited
US3326676A
Cited
US3453148A
Cited
US3681146A
Cited
US3898098A
Cited
US3992222A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |