Method for making ceramic electric resistor

Claim 2

A process for the production of a ceramic electric resistor comprising: the steps of obtaining a ceramic body which consists of material having a Peronskite structure with semiconducting doping with alien-lattice ions, applying a palladium (II)-chloride solution to the surface of the ceramic body at points to be contacted, stoving in the palladium (II)-chloride solution at temperatures between 300° to 500° C. after it has been applied to the ceramic body, currentless nickel-plating the resulting palladium (II)-chloride layer to produce a second layer and tempering the resulting resistor.

Claim 3

A process in accordance with claim 1 wherein a 0.01 to 0.2% by weight PdCl 2 solution is used to produce the first layer.

Claim 4

A process in accordance with claim 2 wherein the first layer is stoved-in at temperatures of between 300° and 550° C. or 10 to 60 minutes.

Claim 5

A process in accordance with claim 1 wherein a nickel bath of the following composition is used for the production of the second layer: 3% by weight NiCl 2 . 6H 2 O 1% by weight NaH 2 PO 2 . H 2 O 3 to 7% by weight Na 3 C 6 H 5 O 7 . 2H 2 O 89 to 93% by weight H 2 O.

Claim 6

A process in accordance with claim 4 wherein the currentless nickel-plating is carried out at bath temperatures of 65° to 95° C. during 1 to 60 minutes.

Claim 7

A process in accordance with claim 5 wherein the tempering is carried out at temperatures from 200° to 300° C. in 2 to 15 hours.

Claim 8

Method for producing a ceramic electric resistor having a positive temperature coefficient of resistance and including an oxidizing stoved body consisting of a material possessing Perovskite structure and being semiconducting by means of doping with alien-lattice ions, said body being provided with contact platings free of blocking layers, said contact platings including at least two layers of different materials, the first of said two layers being of palladium and the second layer situated on the first layer being of a nickel-phosphorous alloy including the steps of applying a palladium (II) chloride solution with 0.01 to 0.2% by weight PdCl 2 to the surface of the ceramic body at areas to be contacted, stoving the palladium (II) chloride layer at temperatures between 300° C. and 550° C. for a time between 10 and 60 minutes, immersing the resulting stoved layer in a nickel bath having the following composition: 3% by weight NiCl 2 . 6H 2 O 1% by weight NaH 2 PO 2 . H 2 O 3-7% by weight Na 3 C 6 H 5 O 7 . 2H 2 O currentless nickel plating in said bath at temperatures of 65° C. to 95° C. for a time between 1 and 60 minutes, and tempering the resulting resistor for 2 to 15 hours at temperatures from 200° C. to 300° C.

Claim 9

Method for producing a ceramic electric resistor having a positive temperature coefficient of resistance and including an oxidizing stoved body consisting of a material possessing Perovskite structure and being semiconducting by means of doping with alien-lattice ions, said body being provided with contact platings free of blocking layers, said contact platings including at least two layers of different materials, the first of said two layers being of palladium and the second layer situated on the first layer being of a nickel-phosphorous alloy including the steps of applying a palladium (II) chloride solution with 0.01 to 0.2% by weight PdCl 2 to the surface of the ceramic body at areas to be contacted, stoving the palladium (II) chloride layer at temperatures between 300° C. and 550° C. for a time between 10 and 60 minutes, immersing the resulting stoved layer in a nickel bath having the following composition: 3% by weight NiCl 2 . 6H 2 O 1% by weight NaH 2 PO 2 . H 2 O 3-7% by weight Na 3 C 6 H 5 O 7 . 2H 2 O currentless nickel plating in said bath at temperatures of 65° C. to 95° C. for a time between 1 and 60 minutes, and tempering the resulting resistor for 2 to 15 hours at temperatures from 200° C. to 300° C.