Method of making a multiple-density fibrous acoustical panel
Assignee: Allen Industries Inc
•
Filing: 1977-09-28
•
Granted: 1978-12-26
•
Expires: 1997-09-28
Abstract
Abstract An improved acoustical and trim acoustical panel suitable for use in the interior passenger compartments and exterior components of automotive vehicles or the like, comprising a plurality of fibrous layers of controlled different density, integrally united together at their interfaces and optionally provided with a decorative finish on one or both outer face surfaces thereof. The invention is further directed to novel methods for making such trim panels incorporating preselected contours and localized embossments therein to conform to the contour of the structural panels of vehicle bodies over which the trim panels are adapted to be mounted. In accordance with one process embodiment, a fibrous pad is formed incorporating suitable binding agents and a coextensive impervious membrane or film disposed intermediate of the face surfaces thereof. The composite pad is placed in an appropriately contoured mold and pneumatic pressure is applied to one side thereof to effect a densification and molding of the stratum of fibers disposed between the membrane and the mold surface without appreciably compacting the opposite fibrous layer, while simultaneously setting the binding agent to form a contoured shape-retaining pad having a dual-density fibrous structure.
Inventors
- 👤 Thomas A. Flowers
- 👤 Anthony W. Marra
- 👤 Samuel D. Vinch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:43
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/12; B29; B29C; B29C43/00; B29C43/02; B29C43/20; B29C43/203; B29C70/00; B29C70/04; B29C70/28; B32B1/00; B32B27/32; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0854; B32B2307/00; B32B2307/10; B32B2307/102; B32B2307/30; B32B2307/304; B32B2307/70; B32B2307/718; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; B32B2607/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/24992
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
172 words
The method of making an acoustical and thermal insulating fibrous panel which comprises the steps of forming a composite fibrous pad comprising a first fibrous layer and a second fibrous layer disposed in overlying relationship each of substantially uniform thickness and density incorporating a binding agent distributed therethrough and a flexible impervious film disposed between the opposed faces of said first layer and said second layer, positioning said pad with said first layer disposed in overlying relationship adjacent to a mold having a preselected contour, applying a pneumatic pressure through said second layer against said film of a magnitude sufficient to effect a compaction of said first layer between said film and said mold to a desired density and in shape-conforming contact with said mold without effecting any appreciable densification of said second layer, setting said binding agent to retain the fibrous layers in the preselected contoured configuration and said first layer in the densified condition, and thereafter releasing said pneumatic pressure and extracting the contoured dual-density trim panel from said mold.
Claim 2
Independent Claim
172 words
The method of making an acoustical and thermal insulating fibrous panel which comprises the steps of forming a composite fibrous pad comprising a first fibrous layer and a second fibrous layer disposed in overlying relationship each of substantially uniform thickness and density incorporating a binding agent distributed therethrough and a flexible impervious film disposed between the opposed faces of said first layer and said second layer, positioning said pad with said first layer disposed in overlying relationship adjacent to a mold having a preselected contour, applying a pneumatic pressure through said second layer against said film of a magnitude sufficient to effect a compaction of said first layer between said film and said mold to a desired density and in shape-conforming contact with said mold without effecting any appreciable densification of said second layer, setting said binding agent to retain the fibrous layers in the preselected contoured configuration and said first layer in the densified condition, and thereafter releasing said pneumatic pressure and extracting the contoured dual-density trim panel from said mold.
Claim 3
Dependent Claim
32 words
The method as defined in claim 1, in which said film is coextensive with said first and second layer and is of a thickness ranging from about 0.0005 to about 0.025 inch.
Claim 4
Dependent Claim
33 words
The method as defined in claim 2, in which said first and second layer of said composite fibrous pad are of a weight of about 50 to about 500 grams per square foot.
Claim 5
Dependent Claim
22 words
The method as defined in claim 1, in which said film is of a thickness of about 0.001 to about 0.005 inch.
Claim 6
Dependent Claim
33 words
The method as defined in claim 1, in which said first and second layer of said composite fibrous pad are of a weight of about 100 to about 200 grams per square foot.
Claim 7
Dependent Claim
25 words
The method as defined in claim 1, in which said composite fibrous pad is formed to a thickness of about 0.5 to about 5 inches.
Claim 8
Dependent Claim
25 words
The method as defined in claim 1, in which said composite fibrous pad is formed to a thickness of about 1.5 to about 3 inches.
Claim 9
Dependent Claim
34 words
The method as defined in claim 1, in which said binding agent is present in an amount of about 10% to about 45% by weight of the total weight of each of the layers.
Claim 10
Dependent Claim
40 words
The method as defined in claim 1, in which said binding agent is heat-activatable and including the further step of heating said composite pad while in said mold under pneumatic pressure to effect a heat setting of said binding agent.
Claim 11
Dependent Claim
37 words
The method as defined in claim 1, in which the step of applying pneumatic pressure against said film is performed to control the pressure on said film within a range of about 20 to about 50 psig.
Claim 12
Dependent Claim
40 words
The method as defined in claim 1, including the further step of subjecting said composite fibrous pad to a preliminary cure treatment to partially set said binding agent in the stratum adjacent to the outer faces of the fibrous layers.
Claim 13
Dependent Claim
32 words
The method as defined in claim 1, including the further step of applying a porous sheet to at least one exposed face of said composite fibrous pad prior to the molding step.
Claim 14
Dependent Claim
47 words
The method as defined in claim 1, in which the step of forming said composite fibrous pad includes the further steps of separately forming said second layer, applying said film over one face of said second layer, and thereafter applying said first fibrous layer over said film.
Claim 15
Dependent Claim
28 words
The method as defined in claim 13, in which said first layer is separately formed to the desired thickness and density and thereafter is applied over said film.
Claim 16
Dependent Claim
19 words
The method as defined in claim 13, in which said first layer is formed in situ on said film.
Claim 17
Dependent Claim
65 words
The method as defined in claim 1, in which the step of forming said composite fibrous pad includes the further steps of forming an integral fibrous web of the desired thickness and density, slitting said web intermediate of the face surfaces thereof into said first layer and said second layer, and interposing said film between the opposed slit faces of said first and second layer.
Claim 18
Dependent Claim
43 words
The method as defined in claim 1, including the further step of providing said mold with a preselected textured surface over at least a portion of the surface area thereof to impart a corresponding texture to the exposed face of said first layer.
Claim 19
Dependent Claim
30 words
The method as defined in claim 1, including the further step of substantially sealing the peripheral edge of said composite fibrous pad prior to the application of pneumatic pressure thereto.
References Cited (Backward Citations)
US2150458A
Cited
US2851730A
Cited
US2890146A
Cited
GB935961A
Cited
US3825642A
Cited
US3895089A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-25 | 1982-06-26 | 1982-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-25 | 1986-06-26 | 1986-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-25 | 1990-06-26 | 1990-12-26 | $7700.00 | Window Closed / Lapsed |