Grafted polymeric material and process for preparing
Assignee: Spectrum Brands Inc
•
Filing: 1977-03-23
•
Granted: 1978-12-26
•
Expires: 1997-03-23
Abstract
Abstract A process for preparing a polymeric material grafted throughout its bulk is provided. A polymer having finely divided particles is blended with silica and maintained in a fluidized bed. The polymer is activated by passing ozone uniformly through the blend to initiate incipient labile sites in the molecular structure of the polymer. The polymer is then reacted with an ethylenically unsaturated ionogenic monomer to graft polymerize the monomer onto the polymer. The grafted polymer may then be converted to a salt form by reacting with alkaline compounds. The resultant powders can be fused into any desired shape by conventional polymer plastic processes.
Inventors
- 👤 Philip Bernstein
- 👤 James P. Coffey
- 👤 Alan E. Varker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:01
CPC Classifications
C; C08; C08F; C08F259/00; C08F259/02; C08F259/04; C08F255/00; C08F255/02
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
128 words
A grafted polymeric composition formed by the process of: (a) suspending and agitating a quantity of finely divided polymeric material selected from the group consisting of polyethylene, polypropylene, and polyvinylchloride, wherein the polymeric material is comprised of particles having a particle size of about 15 to 25 microns; and wherein the polymeric material is blended with 0.5-5%, by weight of the polymeric material, silica, and wherein the suspending and agitating is in a fluidized bed at ambient temperature; (b) introducing ozone into said fluidized bed, at ambient temperature, for activating said material by initiating incipient labile sites in the molecular structure of said material; and (c) reacting the activating material with an ethylenically unsaturated ionogenic monomer, at an elevated temperature, to graft polymerize the monomer onto said material.
Claim 2
Dependent Claim
128 words
A grafted polymeric composition formed by the process of: (a) suspending and agitating a quantity of finely divided polymeric material selected from the group consisting of polyethylene, polypropylene, and polyvinylchloride, wherein the polymeric material is comprised of particles having a particle size of about 15 to 25 microns; and wherein the polymeric material is blended with 0.5-5%, by weight of the polymeric material, silica, and wherein the suspending and agitating is in a fluidized bed at ambient temperature; (b) introducing ozone into said fluidized bed, at ambient temperature, for activating said material by initiating incipient labile sites in the molecular structure of said material; and (c) reacting the activating material with an ethylenically unsaturated ionogenic monomer, at an elevated temperature, to graft polymerize the monomer onto said material.
Claim 3
Dependent Claim
35 words
The grafted polymeric composition according to claim 1, wherein the process of forming said composition further comprises the step of converting the grafted material into salt form by reacting the grafted material with alkalie compound.
Claim 4
Dependent Claim
16 words
The composition of claim 1, wherein the finely divided polymer material is polyethylene, polypropylene, or polyvinylchloride.
Claim 5
Dependent Claim
20 words
The composition of claim 3, wherein the polymer has particles of an average diameter of about 5 to 50 microns.
Claim 6
Dependent Claim
17 words
The composition of claim 1, wherein the ethylenically unsaturated ionogenic monomer is methacrylic acid or acrylic acid.
Claim 7
Dependent Claim
93 words
A grafted polymeric composition formed by the process of: (a) suspending and agitating a quantity of polyethylene having a particle size of about 15 to 25 microns blended with 0.5-5% by weight based on the weight of the polyethylene fumed silica in a fluidized bed; (b) introducing ozone into the fluidized bed maintain at ambient temperature until the amount of ozone absorbed is approximately 500-600 milligrams per 100 grams of polyethylene; (c) reacting the ozonated material with methacrylic acid until the graft polymerization is from 30 to 440° by weight of the polyethylene.
Claim 8
Dependent Claim
93 words
A grafted polymeric composition formed by the process of: (a) suspending and agitating a quantity of polyethylene having a particle size of about 15 to 25 microns blended with 0.5-5% by weight based on the weight of the polyethylene fumed silica in a fluidized bed; (b) introducing ozone into the fluidized bed maintain at ambient temperature until the amount of ozone absorbed is approximately 500-600 milligrams per 100 grams of polyethylene; (c) reacting the ozonated material with methacrylic acid until the graft polymerization is from 30 to 440° by weight of the polyethylene.
Claim 9
Dependent Claim
137 words
A process for obtaining a grafted polymeric composition comprising the steps of: (a) suspending and agitating a quantity of finely divided polymeric material selected from the group consisting of polyethylene, polypropylene, and polyvinylchloride, wherein the polymeric material is comprised of particles having a particle size of about 15 to 25 microns; and wherein the polymeric material is blended with 0.5-5%, by weight of the polymeric material, silica, and wherein the suspending and agitating is in a fluidized bed at ambient temperature; (b) introducing ozone into said fluidized bed at ambient temperature for activitating the material of step A by initiating incipient labile sites in the molecular structure of the material; and (c) reacting the activated material of step B with an ethylenically unsaturated ionogenic monomer, at an elevated temperature, to graft polymerize the monomer onto the material.
Claim 10
Dependent Claim
137 words
A process for obtaining a grafted polymeric composition comprising the steps of: (a) suspending and agitating a quantity of finely divided polymeric material selected from the group consisting of polyethylene, polypropylene, and polyvinylchloride, wherein the polymeric material is comprised of particles having a particle size of about 15 to 25 microns; and wherein the polymeric material is blended with 0.5-5%, by weight of the polymeric material, silica, and wherein the suspending and agitating is in a fluidized bed at ambient temperature; (b) introducing ozone into said fluidized bed at ambient temperature for activitating the material of step A by initiating incipient labile sites in the molecular structure of the material; and (c) reacting the activated material of step B with an ethylenically unsaturated ionogenic monomer, at an elevated temperature, to graft polymerize the monomer onto the material.
Claim 11
Dependent Claim
16 words
The process of claim 7 wherein the finely divided polymer material is polyethylene, polypropylene or polyvinylchloride.
Claim 12
Dependent Claim
33 words
The process of claim 7 wherein the finely divided polymer material is polyethylene having particles of an average diameter of about 5 to 50 microns, and the ethylenically unsaturated monomer is methacrylic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-25 | 1982-06-26 | 1982-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-25 | 1986-06-26 | 1986-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-25 | 1990-06-26 | 1990-12-26 | $7700.00 | Window Closed / Lapsed |