Fire-resistant thermoplastic polyester resin compositions and process for rendering polyesters fire-resistant
Assignee: Teijin Ltd
•
Filing: 1975-05-20
•
Granted: 1978-12-26
•
Expires: 1995-05-20
Abstract
Abstract A fire-resistant thermoplastic polyester resin composition having excellent anti-dripping properties which comprises (A) an aromatic polyester resin, (B) a graft copolymer of a butadiene polymer-vinyl monomer in an amount of at least 0.5 parts by weight but less than 25 parts by weight per 100 parts by weight of said polyester resin (A), (c) a fire retardant in an amount of from 0.5 to 35 parts by weight per 100 parts by weight of said polyester resin (A).
Inventors
- 👤 Yoshitsugu Nakamura
- 👤 Takeo Kawamura
- 👤 Noritsugu Saiki
- 👤 Michiyuki Tokashiki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 18:59
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
251 words
A fire-resistant thermoplastic polyester resin composition which consists essentially of (A) an aromatic polyester resin selected from the group consisting of polyethylene terephthalate, polytrimethylene terephthalate, polytetramethylene terephthalate, polyhexamethylene terephthalate and mixtures thereof. (B) a graft copolymer derived from a butadiene polymer having at least 50 mol% of butadiene units and a graft monomer selected from the group consisting of methacrylic acid esters, aromatic monovinyl compounds, vinyl cyanide compounds, and mixtures thereof present in an amount of at least 0.5 parts by weight but less than 25 parts by weight per 100 parts by weight of said polyester resin (A), (c) a fire retardant selected from the group consisting of a compound of the formula ##STR7## in which X represents a halogen atom, n respresents an integer of 1 or 0, and l and m each represents an integer of 1-5, a halogen-substituted cyclopentadiene dimer; an oligomeric polycarbonate of tetrabromobisphenol A, and a combination thereof with antimony oxide, in an amount of from 0.5 to 35 parts by weight per 100 parts by weight of said polyester resin (A), (d) a glass fiber present in an amount less than 120 parts by weight per 100 parts by weight of said polyester resin (A), and (E) at least one additive, in an amount of 0 to 10 parts by weight per 100 parts by weight of said polyester resin (A), selected from the group consisting of stabilizers, coloring agents, mold releasing agents, nucleating agents, lubricants, and inorganic fillers other than said glass fiber.
Claim 2
Dependent Claim
251 words
A fire-resistant thermoplastic polyester resin composition which consists essentially of (A) an aromatic polyester resin selected from the group consisting of polyethylene terephthalate, polytrimethylene terephthalate, polytetramethylene terephthalate, polyhexamethylene terephthalate and mixtures thereof. (B) a graft copolymer derived from a butadiene polymer having at least 50 mol% of butadiene units and a graft monomer selected from the group consisting of methacrylic acid esters, aromatic monovinyl compounds, vinyl cyanide compounds, and mixtures thereof present in an amount of at least 0.5 parts by weight but less than 25 parts by weight per 100 parts by weight of said polyester resin (A), (c) a fire retardant selected from the group consisting of a compound of the formula ##STR7## in which X represents a halogen atom, n respresents an integer of 1 or 0, and l and m each represents an integer of 1-5, a halogen-substituted cyclopentadiene dimer; an oligomeric polycarbonate of tetrabromobisphenol A, and a combination thereof with antimony oxide, in an amount of from 0.5 to 35 parts by weight per 100 parts by weight of said polyester resin (A), (d) a glass fiber present in an amount less than 120 parts by weight per 100 parts by weight of said polyester resin (A), and (E) at least one additive, in an amount of 0 to 10 parts by weight per 100 parts by weight of said polyester resin (A), selected from the group consisting of stabilizers, coloring agents, mold releasing agents, nucleating agents, lubricants, and inorganic fillers other than said glass fiber.
Claim 3
Dependent Claim
21 words
The fire-resistant thermoplastic polyester resin composition of claim 1 wherein said composition is in the form of an injection molded article.
Claim 4
Dependent Claim
59 words
The composition of claim 1 wherein the graft copolymer is present in from about 1 to about 20 parts by weight, the fire retardant is present in from about 3 to about 30 parts by weight, and the glass fiber is present in less than about 100 parts by weight, all per hundred parts by weight of polyester resin.
Claim 5
Dependent Claim
59 words
The composition of claim 1 wherein the graft copolymer is present in from about 2 to about 15 parts by weight, the fire retardant is present in from about 5 to about 25 parts by weight, and the glass fiber is present in less than about 80 parts by weight, all per hundred parts by weight of polyester resin.
Claim 6
Dependent Claim
30 words
The composition of claim 3 wherein the graft copolymer has a grafting ratio of about 15 to 200 percent, and an average particle diameter of less than about 50 microns.
Claim 7
Dependent Claim
28 words
The composition of claim 4 wherein the graft copolymer has a grafting ratio of 30 to 120 percent, and an average particle diameter of less than 10 microns.
Claim 8
Dependent Claim
49 words
The composition of claim 3 wherein the fire retardant is selected from the group consisting of decabromobiphenyl, decabromobiphenyl ether, hexabromobiphenyl ether of the formula ##STR8## an oligomeric polycarbonate of tetrabromobisphenol A having an average polymerization degree of 2-6 and a combination of these with Sb 2 0 3 .
Claim 9
Dependent Claim
122 words
A process for imparting fire-resistant properties to an aromatic polyester resin according to which fire-resistant properties of said resin are improved by blending with a fire retardant which consists essentially of blending with an aromatic polyester resin (A), (B) a graft copolymer of a butadiene polymer-vinyl monomer in an amount of at least 0.5 parts by weight but less than 25 parts by weight per 100 parts by weight of said aromatic polyester resin (A); (C) a fire retardant in an amount of 0.5 to 35 parts by weight per 100 parts by weight of said polyester (A); and (D) a glass fiber present in an amount less than 120 parts by weight per 100 parts by weight of said polyester (A).
Claim 10
Dependent Claim
122 words
A process for imparting fire-resistant properties to an aromatic polyester resin according to which fire-resistant properties of said resin are improved by blending with a fire retardant which consists essentially of blending with an aromatic polyester resin (A), (B) a graft copolymer of a butadiene polymer-vinyl monomer in an amount of at least 0.5 parts by weight but less than 25 parts by weight per 100 parts by weight of said aromatic polyester resin (A); (C) a fire retardant in an amount of 0.5 to 35 parts by weight per 100 parts by weight of said polyester (A); and (D) a glass fiber present in an amount less than 120 parts by weight per 100 parts by weight of said polyester (A).
References Cited (Backward Citations)
US3886231A
Cited
US3564077A
Cited
US3751396A
Cited
US3953394A
Cited
US3953394B1
Cited
US3919353A
Cited
US3864428A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-25 | 1982-06-26 | 1982-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-25 | 1986-06-26 | 1986-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-25 | 1990-06-26 | 1990-12-26 | $7700.00 | Window Closed / Lapsed |