Steel article having a nitrided and partly oxidized surface and method for producing same
Assignee: Nissan Motor Co Ltd
•
Filing: 1977-04-06
•
Granted: 1978-12-26
•
Expires: 1997-04-06
Abstract
Abstract Surface-hardening of a steel article which is to be mated with a separate article so as to make a sliding or rolling face-to-face contact is accomplished by heating the steel article in ammonia gas containing from 1 to 10% by volume of air. The treated article has an oxidized layer as an outmost part of a nitride layer. The oxidized layer abrades more readily than the nitride layer, so that the article has the property of smoothly fitting a separate article practically from the start of use and exhibits a good wear resistance during subsequent use.
Inventors
- 👤 Shingi Fushimi
- 👤 Takeshi Miyata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:22
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/06; C23C8/28; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12583; Y10T428/1259
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
115 words
A method of hardening a steel article which is to be mated with a separate article so as to make face-to-face contact, said article having good wear resistance and smoothly fitting the separate article substantially from the start of use, the method comprising: a. heating said steel article in an ammonia gas atmosphere containing less than 1% by volume of oxygen; b. continuing heating of the steel article at a temperature of 450 to 650° in an ammonia gas atmosphere containing from 1 to 10% by volume of oxygen so that a surface region of the steel article is nitrided, with the formation of an oxidized layer as an outermost part of the nitrided layer.
Claim 2
Independent Claim
115 words
A method of hardening a steel article which is to be mated with a separate article so as to make face-to-face contact, said article having good wear resistance and smoothly fitting the separate article substantially from the start of use, the method comprising: a. heating said steel article in an ammonia gas atmosphere containing less than 1% by volume of oxygen; b. continuing heating of the steel article at a temperature of 450 to 650° in an ammonia gas atmosphere containing from 1 to 10% by volume of oxygen so that a surface region of the steel article is nitrided, with the formation of an oxidized layer as an outermost part of the nitrided layer.
Claim 3
Dependent Claim
33 words
A method as claimed in claim 1, wherein said ammonia gas atmosphere used in said second ammonia treatment contains from 5 to 50% by volume of air as the source of said oxygen.
Claim 4
Dependent Claim
29 words
A method as claimed in claim 1, wherein the two heating steps are performed successively without interrupting the heating and the contact of the steel article with ammonia gas.
Claim 5
Dependent Claim
31 words
A method as claimed in claim 1, wherein the two heating steps are preformed with an interval therebetween, so that the steel article is once cooled and isolated from ammonia gas.
Claim 6
Dependent Claim
32 words
A method as claimed in claim 1 wherein the heating continues until the oxidized layer is from 1 to 10 μm in depth as measured from the surface of the steel sheet.
References Cited (Backward Citations)
US2513302A
Cited
US3802933A
Cited
US3748195A
Cited
US4017336A
Cited
DE2508907A1
Cited
US3943010A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-25 | 1982-06-26 | 1982-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-25 | 1986-06-26 | 1986-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-25 | 1990-06-26 | 1990-12-26 | $7700.00 | Window Closed / Lapsed |