Process for making porous metal heat sink from clad aluminum wire
Assignee: Individual
•
Filing: 1977-05-23
•
Granted: 1978-12-19
•
Expires: 1997-05-23
Abstract
Abstract A method of making porous metal heat sinks from aluminum is described. The sink, in its simplist form, is composed of layers of aluminum wire mesh randomly stacked and brazed together to form a rigid porous metal panel. Devices to be heated (or cooled) are mounted on the panel and forced air passed through the panel creating abundant heat transfer due to large surface area and favorable thermal conductivity of aluminum. Tortuous air passages through the wire mesh create conditions favorable for turbulence which further facilitates heat transfer. Advance in the state-of-the-art is the novel manufacturing method of making a low cost heat sink whose thermal performance is only slightly less than that of higher cost copper wire sinks. A secondary application of the invention is for the formation of metallic filtration material designed for filtering under controlled temperature conditions. Careful selection of wire size, weave, calendering, and layer orientation as well as the brazing process provide the necessary constituents for control of particulate size. The method is in contrast to that disclosed in U.S. Pat. No. 3,999,699 issued to John Chisholm (1976) in which layers of the laminate are fused together by more conventional techniques producing a higher performance and more expensive laminate.
Inventors
- 👤 John Chisholm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:36
CPC Classifications
F; F28; F28F; F28F13/00; F28F13/003; B; B23; B23P; B23P15/00; B23P15/26
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
83 words
The process for making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a tube of brazable aluminum alloy whose melting temperature is slightly below that of the aluminum, extruding the clad billet into wire, weaving the wire into a mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking a plurality of said lamina to form a panel and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 2
Dependent Claim
83 words
The process for making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a tube of brazable aluminum alloy whose melting temperature is slightly below that of the aluminum, extruding the clad billet into wire, weaving the wire into a mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking a plurality of said lamina to form a panel and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 3
Dependent Claim
36 words
The process recited in claim 1 including attaching a piece of solid metal to the surface of the lamina by being included in the brazing process and for the purpose of making attachments to said panel.
Claim 4
Dependent Claim
24 words
The process recited in claim 1 including calendering laminate after brazing to restrict transverse passage of particulate in accordance to a desired particle size.
Claim 5
Dependent Claim
124 words
The process of making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a closed-end tube of brazable aluminum alloy whose melting temperature is slightly below that of the aluminum, extruding the composite billet into wire, weaving the wire into mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking a plurality of said lamina to form a panel including arranging the upper layers of said stacked lamina in a non-coextensive manner with respect to the bottom layer so as to form a channel in the final panel upper surface for the reception of a flame-sprayed deposition, calendering the lamina, and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 6
Dependent Claim
124 words
The process of making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a closed-end tube of brazable aluminum alloy whose melting temperature is slightly below that of the aluminum, extruding the composite billet into wire, weaving the wire into mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking a plurality of said lamina to form a panel including arranging the upper layers of said stacked lamina in a non-coextensive manner with respect to the bottom layer so as to form a channel in the final panel upper surface for the reception of a flame-sprayed deposition, calendering the lamina, and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 7
Dependent Claim
42 words
The process recited in claim 4 including stacking the lamina in a non-coextensive manner with respect to the bottom layer so as to form a channel in the panel upper surface for the reception of a metallic insert retained by the braze.
Claim 8
Dependent Claim
113 words
The process for making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a closed-end tube of brazable aluminum alloy whose melting temperature is slightly below that of aluminum, deforming the composite billet into wire, weaving the wire into mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking at least three of said lamina to form a panel and providing the uppermost layers of the lamina with concentric holes of successively increasing size from the bottom lamina layer for the reception of a flame-sprayed deposition, calendering the lamina, and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 9
Dependent Claim
113 words
The process for making a laminated porous metal panel from clad aluminum wire, said process comprising the steps of encasing a billet of aluminum in a closed-end tube of brazable aluminum alloy whose melting temperature is slightly below that of aluminum, deforming the composite billet into wire, weaving the wire into mesh, calendering the mesh, cleaning the mesh by vapor degreasing, randomly stacking at least three of said lamina to form a panel and providing the uppermost layers of the lamina with concentric holes of successively increasing size from the bottom lamina layer for the reception of a flame-sprayed deposition, calendering the lamina, and brazing the stacked lamina in a controlled atmosphere furnace.
Claim 10
Dependent Claim
55 words
The process recited in claim 6 wherein the concentric holes of successively increasing size from the bottom lamina layer are for the purpose of receiving a stepped metallic insert attached to the successive layers of the lamina by being included in the brazing process and for the purpose of making attachment to the said panel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-18 | 1982-06-19 | 1982-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-18 | 1986-06-19 | 1986-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-18 | 1990-06-19 | 1990-12-19 | $7700.00 | Window Closed / Lapsed |