US4129543A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermosetting molding resin compositions
Assignee: Hi-Tech Industries Inc
•
Filing: 1976-06-18
•
Granted: 1978-12-12
•
Expires: 1996-06-18
Abstract
Abstract This invention provides, in a first aspect, means for obtaining a liquid thermosetting polyester resin composition which is degassed without the loss of volatile component, by the presence of a dimethyl polysiloxane ingredient in the resin composition. The second aspect of the invention provides for mold lubrication and parting without substantial surface problems in the finished product by the presence of a mixture of an alkyl phosphate ester parting agent in combination with an alkylene bis-alkamide material.
Inventors
- 👤 Neil Kaplan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:42
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08K; C08K3/00; C08K3/18; C08K3/34; C08K3/36; C08K5/00; C08K5/16; C08K5/20; C08K5/49; C08K5/51; C08K5/52; C08L83/00; C08L83/04
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
160 words
In a polymerizable thermosetting liquid resin composition which is designed and adapted for use in an injection molding process, the composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-linked thermoset polymer, and a particulate filler material in an amount of at least about 100 parts per 100 parts by weight of the resin and cross-linking monomer, the improvement comprising a dimethylpolysiloxane, having a viscosity of at least 100 centistokes when measured at 25° C in a Brookfield viscometer, RV series, and converted to centistokes according to the formula viscosity(centistokes) = viscosity(centipoise)/density; dimethylpolysiloxane being present in an amount of from about 0.02 to about 3 parts per 100 parts of the combined resin, whereby the polymerizable resin composition is rendered substantially free of incondensible gases to that voids are not formed in a product injection molded from said polymerizable resin composition.
Claim 2
Dependent Claim
160 words
In a polymerizable thermosetting liquid resin composition which is designed and adapted for use in an injection molding process, the composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-linked thermoset polymer, and a particulate filler material in an amount of at least about 100 parts per 100 parts by weight of the resin and cross-linking monomer, the improvement comprising a dimethylpolysiloxane, having a viscosity of at least 100 centistokes when measured at 25° C in a Brookfield viscometer, RV series, and converted to centistokes according to the formula viscosity(centistokes) = viscosity(centipoise)/density; dimethylpolysiloxane being present in an amount of from about 0.02 to about 3 parts per 100 parts of the combined resin, whereby the polymerizable resin composition is rendered substantially free of incondensible gases to that voids are not formed in a product injection molded from said polymerizable resin composition.
Claim 3
Dependent Claim
15 words
The polymerizable thermosetting liquid resin composition of claim 1, wherein the cross-linking monomer is styrene.
Claim 4
Dependent Claim
22 words
The polymerizable thermosetting liquid resin composition of claim 1, comprising in addition initiators and catalysts suitable for use in injection molding operations.
Claim 5
Dependent Claim
26 words
In the resin composition of claim 1, where the dimethyl polysiloxane is a liquid having a viscosity not greater than about 60,000 cs at 25° C.
Claim 6
Dependent Claim
30 words
The resin composition of claim 1, wherein the particulate filler material is a granular filler having a particle size in the range of from about 5 to about 60 microns.
Claim 7
Dependent Claim
24 words
The resin composition of claim 5, wherein the granular particulate filler contains at least one metal oxide and at least one amorphous silica material.
Claim 8
Dependent Claim
59 words
The resin composition of claim 6, wherein the metal oxide particles are present in an amount of from about 90 to about 180 parts by weight per 100 parts of the resin composition and wherein the amorphous silica is present in an amount from about 15 parts by weight to about 35 parts by weight of the resin composition.
Claim 9
Dependent Claim
87 words
The resin composition of claim 1, wherein the improvement comprises, in addition, the combination of an alkyl phosphate ester and an alkylene bisalkamide, the quantity of alkyl phosphate ester being not substantially greater than 0.4 parts per 100 parts by weight of resin, the combination being present in an amount sufficient to impart satisfactory mold-release qualities to the resin such that a thermoset molded resin product formed therefrom releases cleanly from an injection mold without the formation of spew on the surface of the final molded product.
Claim 10
Dependent Claim
99 words
In a polymerizable thermosetting composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-link thermoset polymer, the improvement comprising the dispersion in the resin composition of the combination of an alkyl phosphate ester and alkylene bisalkamide, the alkyl phosphate ester being present in a quantity not substantially greater than 0.4 parts per 100 parts by weight of resin, the combination providing satisfactory mold-release activity for the resin composition following polymerization and curing in the mold but without any surface spew.
Claim 11
Dependent Claim
99 words
In a polymerizable thermosetting composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-link thermoset polymer, the improvement comprising the dispersion in the resin composition of the combination of an alkyl phosphate ester and alkylene bisalkamide, the alkyl phosphate ester being present in a quantity not substantially greater than 0.4 parts per 100 parts by weight of resin, the combination providing satisfactory mold-release activity for the resin composition following polymerization and curing in the mold but without any surface spew.
Claim 12
Dependent Claim
31 words
The resin composition of claim 9, wherein the alkyl phosphate ester is a dialkyl phosphate ester and wherein the alkyl groups each contain from about 6 to about 32 carbon atoms.
Claim 13
Dependent Claim
21 words
The polymerizable resin composition of claim 10, wherein the alkyl groups each contain from about 8 to about 24 carbon atoms.
Claim 14
Dependent Claim
35 words
The resin composition of claim 11, wherein the alkylene bis alkamide has an alkylene group containing not more than about 8 carbon atoms and an alkamide group containing not more than about 32 carbon atoms.
Claim 15
Dependent Claim
39 words
The resin composition of claim 12, wherein the alkylene group contains not more than about 5 carbon atoms and the alkamide group contains from about 6 to about 24 carbon atoms, the alkylene bis alkamide being a waxy solid.
Claim 16
Dependent Claim
61 words
The resin composition of claim 11, wherein the alkyl phosphate ester is present in an amount of from about 0.1 part to about 0.4 part per 100 parts by weight of resin composition and the alkylene bis alkamide is present in an amount of from about 0.09 part to about 0.3 part per 100 parts by weight of the resin composition.
Claim 17
Dependent Claim
156 words
In a polymerizable thermosetting composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-linked thermoset polymer, the improvement comprising the dispersion of a dimethyl polysiloxane having a viscosity in the range of from about 600 to about 1,000 cs. at 25° C as measured by in an amount of from about 0.02 part to about 3 parts by weight per 100 parts by weight of the resin composition, ethylene bis stearamide in an amount of from about 0.09 to about 0.3 parts by weight per 100 parts by weight of resin composition and a dialkyl phosphate ester wherein each alkyl group contains from about 8 to about 24 carbon atoms and wherein the alkyl phosphate ester is present in an amount of from about 0.1 to about 0.4 part per 100 parts by weight of resin composition.
Claim 18
Dependent Claim
156 words
In a polymerizable thermosetting composition comprising an unsaturated polyester resin capable of cross-linking to form a thermoset polymer and a cross-linking monomer capable of copolymerizing with the polyester resin to form a cross-linked thermoset polymer, the improvement comprising the dispersion of a dimethyl polysiloxane having a viscosity in the range of from about 600 to about 1,000 cs. at 25° C as measured by in an amount of from about 0.02 part to about 3 parts by weight per 100 parts by weight of the resin composition, ethylene bis stearamide in an amount of from about 0.09 to about 0.3 parts by weight per 100 parts by weight of resin composition and a dialkyl phosphate ester wherein each alkyl group contains from about 8 to about 24 carbon atoms and wherein the alkyl phosphate ester is present in an amount of from about 0.1 to about 0.4 part per 100 parts by weight of resin composition.
Claim 19
Dependent Claim
31 words
The polymerizable resin composition of claim 9, comprising in addition, particulate filler material in an amount of at least about 100 parts per 100 parts by weight of the resin composition.
Claim 20
Dependent Claim
26 words
In the resin composition of claim 1, where the dimethyl polysiloxane is a liquid having a viscosity not greater than about 5,000 cs. at 25° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-11 | 1982-06-12 | 1982-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-11 | 1986-06-12 | 1986-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-11 | 1990-06-12 | 1990-12-12 | $7700.00 | Window Closed / Lapsed |