Double side cooled, pressure mounted semiconductor package and process for the manufacture thereof
Assignee: General Electric Co
•
Filing: 1976-06-17
•
Granted: 1978-12-12
•
Expires: 1996-06-17
Abstract
Abstract Disclosed is a double side cooled, pressure mounted semiconductor package and a method for the manufacture thereof. The package is formed by directly bonding upper and lower metal contact assemblies to an annular ceramic housing. Assembly is simplified if at least one contact assembly comprises two parts applied sequentially. An annular flange having a central opening approximately the size of the central opening in the annular housing and having an outside diameter larger than the outside diameter of the ceramic housing is direct bonded to one end of the housing simultaneously with a lower semiconductor contact. After a conventional semiconductor pellet is positioned in the housing, the second part, a metal contact disc with an outside diameter approximately equaling the outside diameter of the flange, is positioned thereover. Finally, the flange and the disc are welded around their peripheries.
Inventors
- 👤 Dominic A. Cusano
- 👤 James A. Loughran
- 👤 Yen S. E. Sun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:46
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; B; B23; B23K; B23K1/00; B23K1/14; B23K1/18; B23K1/19; B23K31/00; B23K31/02; B23K35/00; B23K35/001; B23K35/22; B23K35/24; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/38; H10; H10W; H10W72/00; H10W72/071; H10W76/00; H10W76/10; H10W76/12; H10W76/13; H10W76/138; H10W76/161; H10W76/40; H10W95/00; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/06; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/40; C04B2237/407; C04B2237/50; C04B2237/54; C04B2237/56; C04B2237/567; C04B2237/70; C04B2237/708; C04B2237/76; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K3/10; H05K3/20; H05K3/202
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
222 words
A method of manufacturing a double side cooled pressure mounted semiconductor package comprising the steps of: providing an annular ceramic housing; providing a metal lower contact disc and a metal upper contact flange; direct bonding said lower metal contact disc to the lower end of said housing and direct bonding said upper contact flange to the upper end of said housing, said direct bonding process being carried out by exposing the interface of the metal and the ceramics to a bonding agent that forms a eutectic alloy with the metal, said eutectic alloy consisting predominately of said metal and having a melting point lower than the melting point of said metal, heating the combination to a temperature between the eutectic temperature and the melting point of the metal for at least a few seconds in an inert atmosphere to form a melt at the interfaces between said metal contact disc, the metal contact flange and said ceramic housing, wherein said steps of exposing and heating are carried out such that said melt is at least ultimately hypoeutectic, and cooling the combination; position a semiconductor pellet subassembly in said housing; positioning an upper metal contact disc on said flange so as to close said package; and welding said upper contact disc and said flange around their peripheries so as to seal said package.
Claim 2
Independent Claim
222 words
A method of manufacturing a double side cooled pressure mounted semiconductor package comprising the steps of: providing an annular ceramic housing; providing a metal lower contact disc and a metal upper contact flange; direct bonding said lower metal contact disc to the lower end of said housing and direct bonding said upper contact flange to the upper end of said housing, said direct bonding process being carried out by exposing the interface of the metal and the ceramics to a bonding agent that forms a eutectic alloy with the metal, said eutectic alloy consisting predominately of said metal and having a melting point lower than the melting point of said metal, heating the combination to a temperature between the eutectic temperature and the melting point of the metal for at least a few seconds in an inert atmosphere to form a melt at the interfaces between said metal contact disc, the metal contact flange and said ceramic housing, wherein said steps of exposing and heating are carried out such that said melt is at least ultimately hypoeutectic, and cooling the combination; position a semiconductor pellet subassembly in said housing; positioning an upper metal contact disc on said flange so as to close said package; and welding said upper contact disc and said flange around their peripheries so as to seal said package.
Claim 3
Dependent Claim
38 words
A method according to claim 1 wherein each of said discs defines a centrally located inwardly facing recess, and each of said recesses receives a massive metal contact plate, and said semiconductor pellet assembly fits between said plates.
Claim 4
Dependent Claim
48 words
A method according to claim 1 wherein said substep of exposing the interface of said metal to said ceramic comprises positioning a preform in each of said interfaces, said preforms being of the same metal as that forming the interface and being heavily prereacted with said bonding agent.
Claim 5
Dependent Claim
30 words
A method according to claim 3 wherein said preforms are sufficiently heavily prereacted that they completely liquefy and fill the interfaces during the substep of heating above the eutectic temperature.
Claim 6
Dependent Claim
24 words
A method according to claim 4 wherein said metal and said preforms are copper, said bonding agent is oxygen, and said ceramic is alumina.
Claim 7
Dependent Claim
33 words
A method according to claim 5 wherein said preforms are in the range of three to five mils in thickness and are oxidized to a total depth of at least about one-quarter mil.
Claim 8
Dependent Claim
24 words
A method according to claim 1 wherein said contact discs and said flange are in the range of ten to twenty mils in thickness.
Claim 9
Dependent Claim
29 words
A method according to claim 1 wherein, prior to heating, said combination is placed in a refractory body and thence a second refractory body is placed on said combination.
Claim 10
Dependent Claim
98 words
A method according to claim 8 wherein said lower contact disc defines a shoulder which mates with the lower end of said housing to keep said disc and said housing concentric and also defines a second shoulder which mates with a shoulder defined by said refractory body to maintain alignment therebetween, and wherein said upper contact flange defines a shoulder which mates with the upper end of said housing to keep said flange and said housing concentric and also defines a second shoulder which mates with a shoulder defined by said second refractory body to maintain alignment therebetween.
Claim 11
Dependent Claim
16 words
A method according to claim 9 wherein a weight is placed on said second refractory body.
Claim 12
Dependent Claim
11 words
A method according to claim 10 wherein said weight is tungsten.
Claim 13
Dependent Claim
23 words
A method according to claim 8 wherein a layer of relatively coarse refractory powder is disposed between said refractory bodies and said metal.
Claim 14
Dependent Claim
25 words
A method according to claim 12 wherein said coarse powder consists of aluminum oxide of a size in the range of 70 to 80 mesh.
Claim 15
Dependent Claim
24 words
A method according to claim 1 wherein said metal is electrolytic tough pitch copper and said bonding agent is the oxygen in said copper.
Claim 16
Dependent Claim
33 words
A method according to claim 1 wherein said lower contact disc and said upper contact flange are copper and said substep of exposing said interface to a bonding agent comprises preoxidizing said copper.
Claim 17
Dependent Claim
26 words
A method according to claim 15 wherein said preoxidation is carried out only on the portions of said copper that are to be in said interfaces.
Claim 18
Dependent Claim
40 words
A method according to claim 1 wherein said substep of exposing said interfaces to a bonding agent comprises disposing on one of the surfaces of each interface a particulate layer of a compound of said metal and said bonding agent.
Claim 19
Dependent Claim
21 words
A method according to claim 1 wherein said metal is copper, said bonding agent is oxygen, and said ceramic is alumina.
References Cited (Backward Citations)
CA545179A
Cited
US3224088A
Cited
US3550254A
Cited
US3751800A
Cited
US3981429A
Cited
US3736650A
Cited
US3766634A
Cited
US3994430A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-11 | 1982-06-12 | 1982-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-11 | 1986-06-12 | 1986-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-11 | 1990-06-12 | 1990-12-12 | $7700.00 | Window Closed / Lapsed |