Molded gypsum product and process for preparing the same
Assignee: Mitsubishi Chemical Corp
•
Filing: 1977-04-19
•
Granted: 1978-11-28
•
Expires: 1997-04-19
Abstract
Abstract A molded gypsum product comprises a matrix of crystalline gypsum and reinforcing fibers of glass fiber and asbestos fiber uniformly distributed in said matrix in a multi-layer structure having at least one higher density layer and at least one lower density layer which is continuously adjacent to said higher density layer and having an average apparent bulk density of 0.3 to 0.9 g/cc.
Inventors
- 👤 Mitsuo Uchida
- 👤 Takeshi Fushiki
- 👤 Mitsuru Awata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:09
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/14
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
196 words
A process for preparing a molded gypsum product containing from 0.1 to 5 wt. % of glass fiber and from 1 to 9 wt.% of asbestos fiber and having an apparent bulk density of from 0.3 to 0.9 g/cc, which comprises the steps of (1) mixing a hydraulic gypsum, water and reinforcing fibers of at least glass fiber and asbestos fiber to obtain a slurry, (2) charging said slurry in a mold of a compression-molding machine, (3) compression molding said slurry under a pressure of from 0.05 to 20 kg/cm 2 G to remove the excess water from the upper and lower surfaces of the mold to form a molded product having a preselected weight ratio of water to hydraulic gypsum, and (4) setting and drying said molded material to form a three-layered structure composed of three continuous layers consisting of two outer layers of higher density having an apparent bulk density of from 0.4 to 1.5 g/cc and one middle layer of lower density having an apparent bulk density of from 0.2 to 0.7 g/cc, wherein the difference in apparent bulk densities of said higher and lower density layers is not less than 0.1 g/cc.
Claim 2
Dependent Claim
196 words
A process for preparing a molded gypsum product containing from 0.1 to 5 wt. % of glass fiber and from 1 to 9 wt.% of asbestos fiber and having an apparent bulk density of from 0.3 to 0.9 g/cc, which comprises the steps of (1) mixing a hydraulic gypsum, water and reinforcing fibers of at least glass fiber and asbestos fiber to obtain a slurry, (2) charging said slurry in a mold of a compression-molding machine, (3) compression molding said slurry under a pressure of from 0.05 to 20 kg/cm 2 G to remove the excess water from the upper and lower surfaces of the mold to form a molded product having a preselected weight ratio of water to hydraulic gypsum, and (4) setting and drying said molded material to form a three-layered structure composed of three continuous layers consisting of two outer layers of higher density having an apparent bulk density of from 0.4 to 1.5 g/cc and one middle layer of lower density having an apparent bulk density of from 0.2 to 0.7 g/cc, wherein the difference in apparent bulk densities of said higher and lower density layers is not less than 0.1 g/cc.
Claim 3
Dependent Claim
24 words
A process for preparing a molded gypsum product according to claim 1 in which an air entraining agent is used in said mixing step.
Claim 4
Dependent Claim
186 words
A process for preparing a molded gypsum product containing from 0.1 to 5 wt.% of glass fiber and from 1 to 9 wt.% of asbestos fiber and having an apparent bulk density of from 0.3 to 0.9 g/cc, which comprises the steps of (1) mixing a hydraulic gypsum, water and reinforcing fibers of at least glass fiber and asbestos fiber to obtain a slurry, (2) charging said slurry in a mold of a compression-molding machine, (3) compression molding said slurry under a pressure of 1-75 kg/cm 2 G to remove water from either the upper surface or the lower surface of the mold to form a molded product having a preselected weight ratio of water to hydraulic gypsum, and (4) setting and drying said molded material to form a two-layered structure composed of two continuous layers consisting of a higher density layer having an apparent bulk density of from 0.4 to 1g/cc and a lower density layer having an apparent bulk density of from 0.2 to 0.7g/cc, wherein the difference in apparent bulk densities of said higher and lower density layers is not less than 0.1g/cc.
Claim 5
Dependent Claim
186 words
A process for preparing a molded gypsum product containing from 0.1 to 5 wt.% of glass fiber and from 1 to 9 wt.% of asbestos fiber and having an apparent bulk density of from 0.3 to 0.9 g/cc, which comprises the steps of (1) mixing a hydraulic gypsum, water and reinforcing fibers of at least glass fiber and asbestos fiber to obtain a slurry, (2) charging said slurry in a mold of a compression-molding machine, (3) compression molding said slurry under a pressure of 1-75 kg/cm 2 G to remove water from either the upper surface or the lower surface of the mold to form a molded product having a preselected weight ratio of water to hydraulic gypsum, and (4) setting and drying said molded material to form a two-layered structure composed of two continuous layers consisting of a higher density layer having an apparent bulk density of from 0.4 to 1g/cc and a lower density layer having an apparent bulk density of from 0.2 to 0.7g/cc, wherein the difference in apparent bulk densities of said higher and lower density layers is not less than 0.1g/cc.
Claim 6
Dependent Claim
24 words
A process for preparing a molded gypsum product according to claim 3 in which an air entraining agent is used in said mixing step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-27 | 1982-05-29 | 1982-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-27 | 1986-05-29 | 1986-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-27 | 1990-05-29 | 1990-11-28 | $7700.00 | Window Closed / Lapsed |