Photo process for preparing mixtures with building tack which are based on rubber-like copolymers of ethylene
Assignee: Stamicarbon BV
•
Filing: 1975-04-14
•
Granted: 1978-11-28
•
Expires: 1995-04-14
Abstract
Abstract A process for preparing a mixture based on a rubberlike copolymer of ethylene, at least one other alpha - alkene and one or more polyenes and tackifying resins which has good building tack.
Inventors
- 👤 Hendrikus J. G. Paulen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:34
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/28; C08F; C08F210/00; C08F210/16; C08F210/18; C08J2323/00; C08J2323/02; C08J2323/16
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
222 words
A process for preparing mixtures with building tack which are based on ( 1) a rubber-like copolymer of ethylene, at least one other α-alkene, and one or more polyenes, and (2) a tackifying resin, comprising exposing said mixture in the presence of oxygen and a compound effective as a photosensitizer under the conditions of the process to an artificial light source radiating light at a wave length of between 200 and 800 nanometers, and imparting a radiated energy to the mixture of at least 2 microwatts/cm 2 per nanometer; wherein said mixture in the unvulcanized state and prior to said step of exposing, is characterized by an elongation at break of at least 500% and a tensile strength of between 1.5 and 50 kg/cm 2 ; and wherein the copolymer of said mixture contains C═C bonds in the non-linear part of the polymer chain, wherein the carbon atoms of said C═C bonds either (a) have two hydrocarbon groups which are in a vicinal cis relative position to each other and which do not form part of the same system, or (b) have at least three hydrocarbon groups attached thereto; and wherein said copolymer contains 50 to 85 mole % ethylene and 0.1 to 20% by weight of said polyene; whereby said mixture is characterized by building tack after said step of exposing.
Claim 2
Dependent Claim
222 words
A process for preparing mixtures with building tack which are based on ( 1) a rubber-like copolymer of ethylene, at least one other α-alkene, and one or more polyenes, and (2) a tackifying resin, comprising exposing said mixture in the presence of oxygen and a compound effective as a photosensitizer under the conditions of the process to an artificial light source radiating light at a wave length of between 200 and 800 nanometers, and imparting a radiated energy to the mixture of at least 2 microwatts/cm 2 per nanometer; wherein said mixture in the unvulcanized state and prior to said step of exposing, is characterized by an elongation at break of at least 500% and a tensile strength of between 1.5 and 50 kg/cm 2 ; and wherein the copolymer of said mixture contains C═C bonds in the non-linear part of the polymer chain, wherein the carbon atoms of said C═C bonds either (a) have two hydrocarbon groups which are in a vicinal cis relative position to each other and which do not form part of the same system, or (b) have at least three hydrocarbon groups attached thereto; and wherein said copolymer contains 50 to 85 mole % ethylene and 0.1 to 20% by weight of said polyene; whereby said mixture is characterized by building tack after said step of exposing.
Claim 3
Dependent Claim
57 words
The process according to claim 1, wherein as a result of said step of exposing, said mixture is exposed to a total radiated energy of UV light of a wavelength of between 200 and 400 nm which is at most half the total radiated energy of light in the wavelength range of from 200 to 600 nm.
Claim 4
Dependent Claim
57 words
The process according to claim 1, wherein, as a result of said step of exposing, said mixture is exposed to a total radiated energy of UV light of a wavelength of 200 to 400 nm which is at most one fourth of the total radiated energy of light in the wavelength ranging from 200 to 600 nm.
Claim 5
Dependent Claim
51 words
The process according to claim 1, wherein, as a result of said step of exposing, said mixture receives a total radiated energy of UV light of 325 to 400 nm, which is at most one fourth of the total radiated energy of light of wavelength ranging from 325 to 600 nm.
Claim 6
Dependent Claim
57 words
The process according to claim 1, wherein, as a result of said step of exposing, said mixture is exposed to a total radiated energy of UV light of a wavelength of 325 to 400 nm, which is at most one sixth of the total radiated energy of light of the wavelength ranging from 325 to 600 nm.
Claim 7
Dependent Claim
12 words
The process according to claim 1, wherein said light is visible light.
Claim 8
Dependent Claim
16 words
The process according to claim 1, wherein the radiated energy exceeds 30 μW/cm 2 per nm.
Claim 9
Dependent Claim
16 words
The process according to claim 7, wherein said radiated energy exceeds 200 μW/cm 2 per nm.
Claim 10
Dependent Claim
25 words
The process according to claim 1, wherein said mixture is exposed to a total radiated energy which is less than 15 Joules/cm 2 per nm.
Claim 11
Dependent Claim
21 words
The process according to claim 1, wherein the tensile strength of said mixture ranges between 2 and 30 kg/cm 2 .
Claim 12
Dependent Claim
18 words
The process according to claim 1, wherein said tensile strength ranges between 3 and 25 kg/cm 2 .
Claim 13
Dependent Claim
20 words
The process according to claim 1, wherein said tensile strength of said mixture is less than 15 kg/cm 2 .
Claim 14
Dependent Claim
16 words
The process according to claim 1, wherein said elongation at break of said mixture exceeds 800%.
Claim 15
Dependent Claim
16 words
The process according to claim 13, wherein said elongation at break of said mixture exceeds 1700%.
Claim 16
Dependent Claim
16 words
The process according to claim 1 wherein said copolymer contains 55 to 80 mole % ethylene.
Claim 17
Dependent Claim
17 words
The process according to claim 15, wherein said ethylene content is between 60 and 77.5 mole %.
Claim 18
Dependent Claim
54 words
The process according to claim 16, wherein said copolymer shows a peak at a temperature of between -7° and 11° C., in a thermogram recorded by means of differential scanning calorimetry at a cooling rate of 8° C. per minute, in which the heat of crystallization is plotted as a function of the temperature.
Claim 19
Dependent Claim
15 words
The process according to claim 17, wherein the peak occurs between -3° and +8° C.
Claim 20
Dependent Claim
15 words
The process according to claim 17, wherein the peak occurs between 0° and +6° C.
Claim 21
Dependent Claim
22 words
The process according to claim 17, characterized in that the copolymer is prepared with the aid of the catalyst-combination vanadiumoxytrichloride and alkylaluminiumsesquichloride.
Claim 22
Dependent Claim
38 words
The process according to claim 1, wherein said tackifying resin is prepared from an alkyl phenol and formaldehyde, said resin having a molecular weight of between 200 and 3000, said alkyl group having 1 to 30 carbon atoms.
Claim 23
Dependent Claim
39 words
The process according to claim 1, wherein said tackifying resin is prepared from alkyl phenol and formaldehyde, said tackifying resin having a molecular weight of between 200 and 3000 and said alkyl group having 8 to 12 carbon atoms.
Claim 24
Dependent Claim
22 words
The process according to claim 1, wherein the amount of photosensitizer ranges between 0.001 to 1% by weight based on said copolymer.
Claim 25
Dependent Claim
18 words
The process according to claim 23, wherein said quantity of photosensitizer ranges between 0.01 to 0.5% by weight.
Claim 26
Dependent Claim
22 words
The process according to claim 1, wherein said sensitizer comprises one or more polynuclear aromatic compounds of 3 to 50 aromatic nuclei.
Claim 27
Dependent Claim
45 words
The process according to claim 1, wherein said photosensitizer is an aromatic oil, the aromatic content of which exceeds 40% by weight, said aromatic oil having a transmission of less than 95% if 74 mg of said oil are dissolved in 100 ml of n-hexane.
Claim 28
Dependent Claim
88 words
The process according to claim 1, wherein said mixture comprises (i) and (ii) wherein (i) is a copolymer of ethylene, at least one other α-alkene and one or more polyenes, said copolymer having a tensile strength of at least 10 kg/cm 2 and an ethylene content lying between 50 and 80 weight %, and (ii) is a copolymer of ethylene, at least one other α-alkene and one or more polyenes with a tensile strength lower than 10 kg/cm 2 and an ethylene content lower than 65 weight %.
Claim 29
Dependent Claim
36 words
The process according to claim 27, wherein the ethylene content of the copolymer of (i) lies between 62 and 75 weight % and wherein the ethylene content of (ii) lies between 50 and 63 weight %.
Claim 30
Dependent Claim
23 words
The process according to claim 27, wherein each of (i) and (ii) has a Mooney viscosity ML(1 + 4)125° of at least 20.
Claim 31
Dependent Claim
23 words
The process according to claim 28, wherein each of (i) and (ii) has a Mooney viscosity ML(1 + 4)125° of at least 30.
Claim 32
Dependent Claim
9 words
A mixture prepared by the process of claim 1.
Claim 33
Dependent Claim
10 words
The process of claim 1, wherein said polyene is ethylidenenorbornene.
Claim 34
Dependent Claim
10 words
The process of claim 15, wherein said polyene is ethylidenenorbornene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-27 | 1982-05-29 | 1982-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-27 | 1986-05-29 | 1986-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-27 | 1990-05-29 | 1990-11-28 | $7700.00 | Window Closed / Lapsed |