Production of plaster molds by microwave treatment
Assignee: Valentine Match Plate Co
•
Filing: 1977-03-22
•
Granted: 1978-11-21
•
Expires: 1997-03-22
Abstract
Abstract Metal casting components, e.g. molds and cores, are produced from a compacted mass of plaster by microwave treatment while shielded by a heat insulating medium, e.g. glass fiber matting, which freely transmits microwave radiation as well as water vapor and steam. A casting component dried by this method is completely calcined, and the resulting component will promote cast reproduction of its surface pattern with maximum fidelity of detail.
Inventors
- 👤 James M. Valentine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:33
CPC Classifications
H; H05; H05B; H05B6/00; B; B22; B22C; B22C9/00; B22C9/12
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
139 words
The method of fabricating from gypsum-containing plaster, a foundry casting component which is to be used in casting a metal part from molten casting metal at a temperature above the boiling point of water, and from which the water must be substantially completely eliminated to prevent its turning to steam upon contact with the molten metal, which method comprises the steps of, (a) forming a moldable suspension of the plaster and water, (b) molding a mass of said suspension into a predetermined configuration, (c) shielding said molded mass against radiation of heat therefrom by heat insulating means pervious to microwave radiation and to water vapor and steam; and (d) subjecting said insulated mass to electromagnetic wave energy at microwave frequency until the internal temperature of said mass exceeds the calcining temperature of gypsum but does not reach 600° F.
Claim 2
Independent Claim
139 words
The method of fabricating from gypsum-containing plaster, a foundry casting component which is to be used in casting a metal part from molten casting metal at a temperature above the boiling point of water, and from which the water must be substantially completely eliminated to prevent its turning to steam upon contact with the molten metal, which method comprises the steps of, (a) forming a moldable suspension of the plaster and water, (b) molding a mass of said suspension into a predetermined configuration, (c) shielding said molded mass against radiation of heat therefrom by heat insulating means pervious to microwave radiation and to water vapor and steam; and (d) subjecting said insulated mass to electromagnetic wave energy at microwave frequency until the internal temperature of said mass exceeds the calcining temperature of gypsum but does not reach 600° F.
Claim 3
Dependent Claim
13 words
The method defined in claim 1 wherein said calcining temperature is 270° F.
Claim 4
Dependent Claim
28 words
The method defined in claim 1 wherein said subjecting step (d) is continued until the internal temperature of said mass is in the range of approximately 350°-400° F.
Claim 5
Dependent Claim
14 words
The method defined in claim 1 wherein said insulating means comprises glass fiber matting.
Claim 6
Dependent Claim
32 words
The method defined in claim 1 comprising the further step of controlling said subjecting step (d) by measuring with infrared radiation the temperature of the surface of a cavity in said mass.
Claim 7
Dependent Claim
33 words
The method defined in claim 5 wherein said mass is a multiple-part mold having a sprue hole leading to a cavity therein and said measuring action is carried out through said sprue hole.
Claim 8
Dependent Claim
20 words
The method defined in claim 5 wherein said cavity is a blind hole in the outer surface of said mass.
Claim 9
Dependent Claim
47 words
A method defined in claim 1 wherein said insulating means comprises solid members of refractory material located in closely spaced relation with said mass to leave a narrow slot therebetween for escape of water vapor of steam while reflecting heat back into the surface of said mass.
References Cited (Backward Citations)
US3585258A
Cited
US3732048A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |