Assignee: Alkor GmbH Kunstoffverkauf
•
Filing: 1976-11-15
•
Granted: 1978-11-21
•
Expires: 1996-11-15
Abstract
Abstract A lacquer consisting essentially of a uniform dispersion or solution of 8% to 16% polymerized lower alkyl acrylate and/or methacrylate having 1% to 20% free carboxyl groups, 2.5% to 10% polymethyl or polyethylmethacrylate, 5% to 10% water-soluable, thermosetting melamine resin, the balance being a volatile medium consisting essentially of water and a lower alkanol when deposited on a plastic film and cured at a temperature at least sufficient to volatilize the solvent, forms a transparent, abrasion-resistant coating.
Inventors
- 👤 Victor Peters
- 👤 Franz Krammer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:40
CPC Classifications
C; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C09D133/08; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; C08J2433/00; C08L; C08L33/00; C08L33/04; C08L33/06; C08L33/10; C08L33/12; C08L61/00; C08L61/20; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31627; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
130 words
A lacquer suitable for protecting the surface of plastic film against abrasion consisting essentially of: (a) 8 to 16 parts by weight of an acrylic polymer consisting essentially of repeating units selected from the group consisting of C 2 H 3 COOR and C 3 H 6 COOR, R being hydrogen, methyl, or ethyl, at least 1% and not more than 20% of said R being hydrogen; (b) 2.5 to 10 parts by weight of methyl or ethyl ester of polymethacrylic acid; (c) 5 to 10 parts by weight of a water-soluble, thermosetting melamine resin; and (d) a volatile liquid medium consisting essentially of a mixture of water and an alkanol having up to three carbon atoms, said polymer, said ester, and said resin being uniformly dispersed in said medium.
Claim 2
Dependent Claim
130 words
A lacquer suitable for protecting the surface of plastic film against abrasion consisting essentially of: (a) 8 to 16 parts by weight of an acrylic polymer consisting essentially of repeating units selected from the group consisting of C 2 H 3 COOR and C 3 H 6 COOR, R being hydrogen, methyl, or ethyl, at least 1% and not more than 20% of said R being hydrogen; (b) 2.5 to 10 parts by weight of methyl or ethyl ester of polymethacrylic acid; (c) 5 to 10 parts by weight of a water-soluble, thermosetting melamine resin; and (d) a volatile liquid medium consisting essentially of a mixture of water and an alkanol having up to three carbon atoms, said polymer, said ester, and said resin being uniformly dispersed in said medium.
Claim 3
Dependent Claim
44 words
A lacquer as set forth in claim 1, further comprising an amount of catalyst capable of accelerating the setting of said resin in the absence of said polymer and said ester at a temperature of approximately 150° C, said catalyst being a strong acid.
Claim 4
Dependent Claim
22 words
A lacquer as set forth in claim 2, wherein said catalyst consists of 1.2 to 2.5 parts by weight of p-toluenesulfonic acid.
Claim 5
Dependent Claim
28 words
A lacquer as set forth in claim 2, further comprising an amount of ammonia or an amine sufficient to make the pH of said lacquer 7.5 to 8.5.
Claim 6
Dependent Claim
14 words
A lacquer as set forth in claim 1, wherein said resin is hexamethoxymethyl melamine.
Claim 7
Dependent Claim
23 words
A lacquer as set forth in claim 1, wherein the amount of alkanol in said mixture is not less than 50% by weight.
Claim 8
Dependent Claim
40 words
A lacquer as set forth in claim 5, further comprising 1.2 to 3.5 parts p-toluenesulfonic acid, and an amount of ammonia or an amine sufficient to make the pH of said lacquer 7.5 to 8.5, said resin being hexamethoxymethyl melamine.
Claim 9
Dependent Claim
60 words
A method of protecting the surface of a plastic film against abrasion which comprises coating said surface with the lacquer set forth in claim 7, said medium being inert to said surface, and heating said lacquer until said medium is substantially completely volatilized and said polymer, said ester, and said resin jointly form a substantially transparent layer on said surface.
Claim 10
Dependent Claim
60 words
A method of protecting the surface of a plastic film against abrasion, which comprises coating said surface with the lacquer set forth in claim 1, said medium being inert to said surface, and heating said lacquer until said medium is substantially completely volatilized and said polymer, said ester, and said resin jointly form a substantially transparent layer on said surface.
Claim 11
Dependent Claim
21 words
A method as set forth in claim 9, wherein said lacquer is heated to a temperature of 140° to 160° C.
Claim 12
Dependent Claim
30 words
A lacquer as set forth in claim 1, further comprising at least one member of the group of matting agents consisting of silicon dioxide and polyolefines of lower molecular weight.
Claim 13
Dependent Claim
13 words
A lacquer as set forth in claim 6, wherein said alkanol is ethanol.
Claim 14
Dependent Claim
32 words
A method as set forth in claim 9, wherein said plastic film consists essentially of at least one member of the group consisting of polyvinyl chloride, polyester, polyolefin, acrylic resin, and polyurethane.
Claim 15
Dependent Claim
22 words
A method as set forth in claim 13, wherein the amount of alkanol in said mixture is at least 50% by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |