Assignee: NATIONAL REFRACTORIES & MINERALS Corp A CORP OF
•
Filing: 1977-09-15
•
Granted: 1978-11-21
•
Expires: 1997-09-15
Abstract
Abstract {PG,1 A magnesium aluminate spinel-bonded refractory can be formed which does not exhibit undue expansion (due to the reaction of magnesia and alumina to form magnesium aluminate spinel) between the raw, compacted state and the fired, ceramically bonded state when fired to a temperature of 1400{20 {0 C if a very finely divided alumina with dense particles is used. More specifically, the alumina used has an average particle size of less than 5, preferably less than 2, microns, and a specific surface of less than 30 m{hu 2{l /g, preferably about 5 m{hu 2{l /g (i.e., the small crystallites or particles are dense and do not have a high surface area, as do finely divided active aluminas).
Inventors
- 👤 Ralph B. Videtto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:51
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/44; C04B35/443; C04B35/03; C04B35/04; C04B35/043; C04B35/047; C04B35/0473
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
169 words
A refractory shape having 16 vol % or less porosity in either the fired or unfired form consisting essentially of from 60 to 80 percent magnesia refractory aggregate coarser than 44 microns and sized for good brickmaking to achieve maximum density and from 40 to 20 percent refractory matrix material finer than 44 microns, said matrix material being adapted to form magnesium aluminate spinel upon heating to a temperature of at least 800° C. and consisting essentially of from 15 to 25 percent magnesia containing at least 95% MgO and having a specific surface of at least 5,000 cm 2 /g, and from 4 to 15 percent alumina having a specific surface of from 2 to 30 m 2 /g and an average particle size of less than 5 microns, all percentages being by weight and based on the total weight of aggregate and matrix material, said refractory exhibiting no expansion, as compared with its formed but unfired state, after having been heated to a temperature of 1400° C.
Claim 2
Dependent Claim
169 words
A refractory shape having 16 vol % or less porosity in either the fired or unfired form consisting essentially of from 60 to 80 percent magnesia refractory aggregate coarser than 44 microns and sized for good brickmaking to achieve maximum density and from 40 to 20 percent refractory matrix material finer than 44 microns, said matrix material being adapted to form magnesium aluminate spinel upon heating to a temperature of at least 800° C. and consisting essentially of from 15 to 25 percent magnesia containing at least 95% MgO and having a specific surface of at least 5,000 cm 2 /g, and from 4 to 15 percent alumina having a specific surface of from 2 to 30 m 2 /g and an average particle size of less than 5 microns, all percentages being by weight and based on the total weight of aggregate and matrix material, said refractory exhibiting no expansion, as compared with its formed but unfired state, after having been heated to a temperature of 1400° C.
Claim 3
Dependent Claim
16 words
Refractory composition according to claim 1 wherein the fine magnesia contains at least about 98% MgO.
Claim 4
Dependent Claim
13 words
Refractory composition according to claim 2 which contains about 8 percent fine alumina.
Claim 5
Dependent Claim
183 words
Method of making a magnesium aluminate spinel bonded refractory comprising: (a) admixing from 60 to 80 percent magnesia refractory aggregate coarser than 44 microns and sized for good brickmaking to achieve maximum density with from 40 to 20 percent refractory matrix material finer than 44 microns, said matrix material being adapted to form magnesium aluminate spinel upon heating to a temperature of at least 800° C. and consisting essentially of from 15 to 25% magnesia containing at least 95% MgO and having a specific surface of at least 5,000 cm 2 /g and from 4 to 15% alumina having a specific surface of from 2 to 30 m 2 /g and an average particle size less than 5 microns; (b) compacting the admixture to a porosity of 16 vol % or less; and (c) heating the compacted admixture to at least 800° C.; all percentages being by weight and based on the total weight of aggregate and matrix material, and said refractory exhibiting no expansion, as compared with its formed but unfired state, after having been heated to a temperature of 1400° C.
Claim 6
Dependent Claim
183 words
Method of making a magnesium aluminate spinel bonded refractory comprising: (a) admixing from 60 to 80 percent magnesia refractory aggregate coarser than 44 microns and sized for good brickmaking to achieve maximum density with from 40 to 20 percent refractory matrix material finer than 44 microns, said matrix material being adapted to form magnesium aluminate spinel upon heating to a temperature of at least 800° C. and consisting essentially of from 15 to 25% magnesia containing at least 95% MgO and having a specific surface of at least 5,000 cm 2 /g and from 4 to 15% alumina having a specific surface of from 2 to 30 m 2 /g and an average particle size less than 5 microns; (b) compacting the admixture to a porosity of 16 vol % or less; and (c) heating the compacted admixture to at least 800° C.; all percentages being by weight and based on the total weight of aggregate and matrix material, and said refractory exhibiting no expansion, as compared with its formed but unfired state, after having been heated to a temperature of 1400° C.
Claim 7
Dependent Claim
16 words
Method according to claim 4 wherein the compacted material is heated to at least 1400° C.
Claim 8
Dependent Claim
16 words
Method according to claim 4 wherein the compacted material is heated to at least 1600° C.
Claim 9
Dependent Claim
28 words
Method according to claim 4 wherein the alumina has a specific surface of about 5 m 2 /g and an average particle size of less than 2 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |