Method of forming dimensionally stable foamed articles of polyvinyl aromatic resins and resultant product
Assignee: Empire Level Manufacturing Corp
•
Filing: 1976-04-06
•
Granted: 1978-11-14
•
Expires: 1996-04-06
Abstract
Abstract A rigid, dimentionally stable, distortion-free article of foamed polyvinyl aromatic resin, having a solid outer skin, is formed by incorporating in a foamable polyvinyl aromatic resin a finely, divided inert solid that has been surface treated to render the solid hydrophobic and then molding the foamable composition under foaming conditions. Foamed polyvinyl aromatic resin articles molded in accordance with the present invention have physical dimensions capable of meeting tolerances in the order of ± 0.002 inches and are suitable for use in the manufacture of precision measuring devices and, particularly, frames for level instruments.
Inventors
- 👤 Siebolt Hettinga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:04
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/34; B; B29; B29C; B29C44/00; B29C44/02; B29C44/04; B29C44/0407; C08J9/009; C08K; C08K9/00; C08K9/04; C08J2325/00; C08J2325/02; C08J2325/04; Y; Y10; Y10S; Y10S264/00; Y10S264/14; Y10S264/17; Y10S264/83
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
175 words
A method for forming a substantially rigid, dimensionally stable, interiorally foamed, polyvinyl aromatic resin article having a substantially non-foamed outer skin, which method comprises: preparing a foamable melt comprised of a polyvinyl aromatic resin and a blowing agent; incorporating in the foamable melt a finely divided inert solid material, the material having been treated to render the solid surface hydrophobic; plasticating the foamable composition and the hydrophobic surface treated solid at an elevated first temperature to prepare a homogeneous charge for injection into a mold having a mold cavity; injecting the homogeneous charge into the mold cavity maintained at a second temperature which is lower than the first temperature and is sufficient to cause solidification of that portion of the mold charge which contacts the walls of the mold cavity to form a solid skin; allowing the charge to expand in the old cavity so as to take on the shape of the mold cavity and then removing the molded foamed article from the mold cavity and allowing the article to cool to room temperature.
Claim 2
Independent Claim
175 words
A method for forming a substantially rigid, dimensionally stable, interiorally foamed, polyvinyl aromatic resin article having a substantially non-foamed outer skin, which method comprises: preparing a foamable melt comprised of a polyvinyl aromatic resin and a blowing agent; incorporating in the foamable melt a finely divided inert solid material, the material having been treated to render the solid surface hydrophobic; plasticating the foamable composition and the hydrophobic surface treated solid at an elevated first temperature to prepare a homogeneous charge for injection into a mold having a mold cavity; injecting the homogeneous charge into the mold cavity maintained at a second temperature which is lower than the first temperature and is sufficient to cause solidification of that portion of the mold charge which contacts the walls of the mold cavity to form a solid skin; allowing the charge to expand in the old cavity so as to take on the shape of the mold cavity and then removing the molded foamed article from the mold cavity and allowing the article to cool to room temperature.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein the polyvinyl aromatic resin is polystyrene.
Claim 4
Dependent Claim
12 words
The method of claim 2 wherein the polystyrene is impact grade polystyrene.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein the solid material is calcium carbonate.
Claim 6
Dependent Claim
20 words
The method of claim 4 wherein the calcium carbonate is surface treated with a wax to render the surface hydrophobic.
Claim 7
Dependent Claim
40 words
The method of claim 1 wherein the solid material is incorporated in the polyvinyl aromatic resin at a concentration of about 0.25 to about 5 percent by volume, based on the violume of 100 pounds of the polyvinyl aromatic resin.
Claim 8
Dependent Claim
23 words
The method of claim 1 wherein the solid material has a particle size in the range of about 1 to about 30 microns.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein the first temperature is about 300° to 450° F and the second temperature is about 140° to about 180° F.
Claim 10
Dependent Claim
39 words
A level frame having a substantially smooth, non-porous outer skin and a foamed interior formed solely of a polyvinyl aromatic resin molded by the method of claim 1 and capable of meeting tolerances in the order of ±0.002 inches.
References Cited (Backward Citations)
CA700613A
Cited
US2728735A
Cited
US3268636A
Cited
US3661810A
Cited
US3950484A
Cited
US3745203A
Cited
US3927159A
Cited
US3921306A
Cited
US3931067A
Cited
US4048208A
Cited
US4048272A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-13 | 1982-05-15 | 1982-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-13 | 1986-05-15 | 1986-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-13 | 1990-05-15 | 1990-11-14 | $7700.00 | Window Closed / Lapsed |