Method of keeping nozzle bodies or breaker plates clean during extrusion of polymer melts
Assignee: Bayer AG
•
Filing: 1977-06-29
•
Granted: 1978-11-07
•
Expires: 1997-06-29
Abstract
Abstract The invention relates to a method of keeping nozzle bodies or breaker plates clean during extrusion of polymer which can be shaped from the melt which comprises preventing the formation of deposits near the nozzle orifices by gassing these orifices at the point of extrusion of the melt, said gas consisting entirely or partly of vapors of substances which have a depolymerizing action on the deposits formed from the melt at the edge of the nozzle orifice.
Inventors
- 👤 Gerd Wilhelm
- 👤 Artur Jaschke
- 👤 Hans-Jurgen Simon
- 👤 Jens Schmidt
- 👤 Surinder S. Sandhu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:17
CPC Classifications
D; D01; D01D; D01D4/00; D01D4/04; B; B29; B29C; B29C48/00; B29C48/03; B29C48/05; B29C48/25; B29C48/27; B29C48/272; B29C48/30; B29C48/345; B29C48/36; B29C48/50
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
72 words
Method of keeping nozzle bodies or breaker plates clean during extrusion of polymer which can be shaped from the melt which comprises preventing the formation of deposits near the nozzle orifices by gassing these orifices at the point of extrusion of the melt, said gas consisting entirely or partly of vapours of substances which have a depolymerising action on the deposits formed from the melt at the edge of the die orifice.
Claim 2
Dependent Claim
72 words
Method of keeping nozzle bodies or breaker plates clean during extrusion of polymer which can be shaped from the melt which comprises preventing the formation of deposits near the nozzle orifices by gassing these orifices at the point of extrusion of the melt, said gas consisting entirely or partly of vapours of substances which have a depolymerising action on the deposits formed from the melt at the edge of the die orifice.
Claim 3
Dependent Claim
40 words
Method according to claim 1, wherein the gas used for gassing a polycondensate which is beingextruded consists entirely or partly of vapour formed from the liquid of the low molecular weight product of the polycondensation reaction corresponding to the polymer.
Claim 4
Dependent Claim
12 words
Method according to claim 1, wherein the gas used is mainly steam.
Claim 5
Dependent Claim
23 words
Method according to claim 1, wherein traces of highly volatile bases and/or acids are added to the vapours to improve the depolymerising action.
Claim 6
Dependent Claim
96 words
Method of keeping nozzle bodies or breaker plates clean during extrusion of polymer which can be shaped from the melt which comprises preventing the formation of deposits on or near the nozzle orifices by washing or cleaning these orifices at the point of extrusion of the melt by means of a stream of gas consisting at least partly of vapours of a material selected from the group consisting of steam, an amine and an alcohol which have a depolymerising action on the deposits normally formed from the melt at the outer edge of the nozzle orifice.
Claim 7
Dependent Claim
96 words
Method of keeping nozzle bodies or breaker plates clean during extrusion of polymer which can be shaped from the melt which comprises preventing the formation of deposits on or near the nozzle orifices by washing or cleaning these orifices at the point of extrusion of the melt by means of a stream of gas consisting at least partly of vapours of a material selected from the group consisting of steam, an amine and an alcohol which have a depolymerising action on the deposits normally formed from the melt at the outer edge of the nozzle orifice.
Claim 8
Dependent Claim
28 words
The method of claim 5 in which the depolymerising gas is emitted from the nozzle orifices in the same direction and at the same time as the melt.
Claim 9
Dependent Claim
26 words
Method according to claim 5, wherein the polymers which are gassed during extrusion are generally polymeric addition and condensation products such as polyesters, polyamides and polyurethanes.
Claim 10
Dependent Claim
49 words
Method according to claim 5, wherein before the vapours come into contact with the extruded melt, they are at a temperature above the normal boiling point of the liquid, and they are generally not heated to a temperature more than 100° C. higher than that of the extruded melt.
Claim 11
Dependent Claim
56 words
Method according to claim 5, wherein the gas which consists entirely or partly of substances which have a depolymerising effect on the deposits formed from the melt washes the melt on all sides at its exit from the nozzle body and flows down from the nozzle body practically in the same direction as the extruded melt.
Claim 12
Dependent Claim
26 words
Method according to claim 5, wherein at its point of contact with the melt, the gas generally flows at a higher average velocity than the melt.
Claim 13
Dependent Claim
39 words
Method according to claim 5, wherein the quantitative rate of flow of the vapour from the nozzle body is generally not greater than that of the melt, but is preferably between 0.1 and 10% of that of the melt.
References Cited (Backward Citations)
GB901398A
Cited
US3436789A
Cited
US3462522A
Cited
US3502757A
Cited
US3814559A
Cited
US3907957A
Cited
US3975475A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-06 | 1982-05-08 | 1982-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-06 | 1986-05-08 | 1986-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-06 | 1990-05-08 | 1990-11-07 | $7700.00 | Window Closed / Lapsed |