Poly (oxyalkylene) glycol based polyurethane with improved paint adhesion properties
Assignee: Olin Corp
•
Filing: 1977-08-29
•
Granted: 1978-11-07
•
Expires: 1997-08-29
Abstract
Abstract Flexible polyurethane elastomers suitable for use as automotive exterior body parts are disclosed. The elastomers which are produced from select polymeric diols having a polyoxypropylene block capped with a random poly (oxyethylene-oxypropylene) structure, feature enhanced paint adhesion properties.
Inventors
- 👤 Frank J. Preston
- 👤 David R. MacFarland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:10
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08G18/485
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
94 words
A polyurethane elastomer with improved paint adhesion properties comprising the reaction product of an organic diisocyanate, a chain extender and a polyether polyol having a molecular weight of about 1,500 to about 3,000 prepared by oxyalkylation of (a) a poly (oxypropylene) glycol precursor which precursor is the condensation product of propylene oxide and a difunctional active hydrogen-containing initiator with (b) a random capping mixture of ethylene oxide and about 3 to about 15 percent by weight propylene oxide to produce a polyether polyol including about 30 to about 60 percent by weight oxyethylene content.
Claim 2
Dependent Claim
94 words
A polyurethane elastomer with improved paint adhesion properties comprising the reaction product of an organic diisocyanate, a chain extender and a polyether polyol having a molecular weight of about 1,500 to about 3,000 prepared by oxyalkylation of (a) a poly (oxypropylene) glycol precursor which precursor is the condensation product of propylene oxide and a difunctional active hydrogen-containing initiator with (b) a random capping mixture of ethylene oxide and about 3 to about 15 percent by weight propylene oxide to produce a polyether polyol including about 30 to about 60 percent by weight oxyethylene content.
Claim 3
Dependent Claim
20 words
The polyurethane elastomer of claim 1 wherein the molecular weight of the polyol ranges from about 1,750 to about 2,500.
Claim 4
Dependent Claim
16 words
The polyurethane elastomer of claim 2 wherein the molecular weight of the polyol is about 2,000.
Claim 5
Dependent Claim
34 words
The polyurethane elastomer of claim 1 wherein the polyol is prepared by random oxyalkylation of a poly (oxypropylene) glycol with a mixture of ethylene oxide and about 5 to about 10 percent propylene oxide.
Claim 6
Dependent Claim
27 words
The polyurethane elastomer of claim 4 wherein the polyol is a poly (oxypropylene) glycol oxyalkylated with a mixture of ethylene oxide and about 5 percent propylene oxide.
Claim 7
Dependent Claim
19 words
The polyurethane elastomer of claim 1 wherein the polyol comprises about 40 to about 50 percent by weight oxyethylene.
Claim 8
Dependent Claim
14 words
The polyurethane elastomer of claim 6 wherein the polyol comprises about 45 percent oxyethylene.
Claim 9
Dependent Claim
31 words
The polyurethane elastomer of claim 1 wherein the organic diisocyanate reactant is selected from the group consisting of tolylene diisocyanate, methylene bis (phenyl isocyanate), bidenzyl diisocyanate, phenylene diisocyanate, and hexamethylene diisocyanate.
Claim 10
Dependent Claim
25 words
The polyurethane elastomer of claim 8 wherein the organic diisocyanate reactant is selected from the group consisting of tolylene diisocyanate and methylene bis (phenyl isocyanate).
Claim 11
Dependent Claim
16 words
The polyurethane elastomer of claim 9 wherein the organic diisocyanate reactant is 4,4'-methylene bis (phenyl isocyanate).
Claim 12
Dependent Claim
32 words
The polyurethane elastomer of claim 1 wherein the chain extender reactant is an aliphatic diol selected from the group consisting of ethylene glycol, propylene glycol, butane diol, pentane diol, and hexane diol.
Claim 13
Dependent Claim
13 words
The polyurethane elastomer of claim 11 wherein the chain extender is 1,4-butane diol.
Claim 14
Dependent Claim
45 words
The polyurethane elastomer of claim 1 wherein the polyol reactant is prepared by random oxyalkylation of a poly (oxypropylene) glycol based on a glycol initiator selected from the group consisting of water, propylene glycol, dipropylene glycol, tripropylene glycol, ethylene glycol, butylene glycol, and butane diol.
Claim 15
Dependent Claim
25 words
The polyurethane elastomer of claim 13 wherein the polyol is prepared by random oxyalkylation of a poly (oxypropylene) glycol based on a dipropylene glycol initiator.
Claim 16
Dependent Claim
72 words
The polyurethane elastomer of claim 1 comprising the reaction product of an organic diisocyanate, a chain extender, and a poly (oxyalkylene) glycol having a molecular weight of about 1,750 to about 2,500, prepared by random oxyalkylation of a poly (oxypropylene) glycol precursor with a mixture of ethylene oxide and about 5 to about 10 percent propylene oxide to produce a polyol including about 40 to about 50 percent by weight oxyethylene content.
Claim 17
Dependent Claim
48 words
The polyurethane elastomer of claim 15 comprising the reaction product of 4,4'-methylene bis (phenyl isocyanate), 1,4-butane diol, and a poly (oxyalkylene) glycol having a molecular weight of about 2,000, prepared by random oxyalkylation of poly (oxypropylene) to produce a polyol comprising about 45 percent by weight oxyethylene content.
Claim 18
Dependent Claim
19 words
The polyurethane elastomer of claim 16 wherein the poly (oxypropylene) glycol reactant is based on a dipropylene glycol initiator.
Claim 19
Dependent Claim
32 words
In a process of fabricating flexible automotive body parts from polyurethane elastomers, the improvement characterized by using the polyurethane elastomer of claim 1 to produce a part with improved paint adhesion properties.
Claim 20
Dependent Claim
32 words
In a process of fabricating flexible automotive body parts from polyurethane elastomers, the improvement characterized by using the polyurethane elastomer of claim 15 to produce a part with improved paint adhesion properties.
Claim 21
Dependent Claim
32 words
In a process of fabricating flexible automotive body parts from polyurethane elastomers, the improvement characterized by using the polyurethane elastomer of claim 16 to produce a part with improved paint adhesion properties.
Claim 22
Dependent Claim
32 words
In a process of fabricating flexible automotive body parts from polyurethane elastomers, the improvement characterized by using the polyurethane elastomer of claim 17 to produce a part with improved paint adhesion properties.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-06 | 1982-05-08 | 1982-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-06 | 1986-05-08 | 1986-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-06 | 1990-05-08 | 1990-11-07 | $7700.00 | Window Closed / Lapsed |