Method of making bent laminated glass windshields with drilled apertures

Claim 1

A method of making a bent, laminated, safety glass windshield comprising a pair of glass sheets laminated to a layer of plastic interlayer material and having at least one aperture extending through the thickness of said laminated windshield in spaced relation to a marginal portion thereof comprising performing the following steps in sequence: (a) drilling at least one aperture through the thickness of a first flat glass sheet, (b) drilling at least one corresponding aperture through the thickness of a second flat glass sheet in such a position that it will be aligned with said corresponding aperture of said first flat glass sheet after said two sheets are aligned in superimposed position and bent simultaneously, (c) assembling said flat glass sheets in superimposed aligned position over one another and mounting said assembly so formed over an outline bending mold of the gravity sagging type having an upward facing shaping surface conforming to the shape desired for said glass sheets, (d) heating said glass sheet assembly to at least the deformation temperature of the glass and not above 1150° F. (677° C.) in the vicinity of said aperture whereby the glass sheets sag to form shaped glass sheets having controlled shapes corresponding to the shaping surface of said bending mold, (e) cooling said shaped glass sheets, controlling said cooling in the range from about 1100° F. (593° C.) to about 900° F. (482° C.) to a rate of cooling of between 1° F. (0.5° C.) and 3° F. (1.7° C.) per second, thereby establishing a compression stress in the periphery of said holes while avoiding the establishment of temporary tension stresses in said hole periphery that would cause the glass to break in the vicinity thereof, and (f) laminating said shaped glass sheets to an interlayer composed of polyurethane or polyvinyl acetal.

Claim 2

A method of making a bent, laminated, safety glass windshield comprising a pair of glass sheets laminated to a layer of plastic interlayer material and having at least one aperture extending through the thickness of said laminated windshield in spaced relation to a marginal portion thereof comprising performing the following steps in sequence: (a) drilling at least one aperture through the thickness of a first flat glass sheet, (b) drilling at least one corresponding aperture through the thickness of a second flat glass sheet in such a position that it will be aligned with said corresponding aperture of said first flat glass sheet after said two sheets are aligned in superimposed position and bent simultaneously, (c) assembling said flat glass sheets in superimposed aligned position over one another and mounting said assembly so formed over an outline bending mold of the gravity sagging type having an upward facing shaping surface conforming to the shape desired for said glass sheets, (d) heating said glass sheet assembly to at least the deformation temperature of the glass and not above 1150° F. (677° C.) in the vicinity of said aperture whereby the glass sheets sag to form shaped glass sheets having controlled shapes corresponding to the shaping surface of said bending mold, (e) cooling said shaped glass sheets, controlling said cooling in the range from about 1100° F. (593° C.) to about 900° F. (482° C.) to a rate of cooling of between 1° F. (0.5° C.) and 3° F. (1.7° C.) per second, thereby establishing a compression stress in the periphery of said holes while avoiding the establishment of temporary tension stresses in said hole periphery that would cause the glass to break in the vicinity thereof, and (f) laminating said shaped glass sheets to an interlayer composed of polyurethane or polyvinyl acetal.

Claim 8

A method of making a bent, laminated safety glass windshield having at least one aperture extending through the entire thickness of said windshield comprising a pair of bent glass sheets having aligned apertures and a layer of plastic interlayer material apertured in alignment with the aligned apertures in said apertured glass sheets comprising (1) drilling an aperture through a first flat glass sheet to be bent and laminated, (2) drilling a corresponding aperture through a second flat glass sheet to be bent and laminated, said aperture being in such a position that it is aligned with the corresponding aperture of said first flat glass sheet after said glass sheets are bent, (3) assembling said glass sheets with said apertures aligned in shaping relation to an outline bending mold of the gravity-sag type, (4) heating said assembled glass sheets to a temperature sufficient to sag said glass sheets simultaneously to conform to the shape of said mold but insufficient in the vicinity of said apertures to heal the more severe fissures formed during said drilling, whereby said sheets conform to the shape of said mold and said unhealed fissures in said apertured portion of the glass sheets remain susceptible of developing into vents, (5) cooling said shaped glass sheets at a controlled rate of cooling at a sufficiently slow and uniform rate through a temperature range from above to below the annealing range of the glass to avoid establishing temporary tension stresses that would cause said unhealed fissures to develop into vents, yet at a rate through said temperature range sufficient to establish a compression stress layer in the surface of said apertured portion, and laminating said shaped, apertured glass sheets to an interlayer composed of polyurethane or polyvinyl acetal.

Claim 9

A method of making a bent, laminated safety glass windshield having at least one aperture extending through the entire thickness of said windshield comprising a pair of bent glass sheets having aligned apertures and a layer of plastic interlayer material apertured in alignment with the aligned apertures in said apertured glass sheets comprising (1) drilling an aperture through a first flat glass sheet to be bent and laminated, (2) drilling a corresponding aperture through a second flat glass sheet to be bent and laminated, said aperture being in such a position that it is aligned with the corresponding aperture of said first flat glass sheet after said glass sheets are bent, (3) assembling said glass sheets with said apertures aligned in shaping relation to an outline bending mold of the gravity-sag type, (4) heating said assembled glass sheets to a temperature sufficient to sag said glass sheets simultaneously to conform to the shape of said mold but insufficient in the vicinity of said apertures to heal the more severe fissures formed during said drilling, whereby said sheets conform to the shape of said mold and said unhealed fissures in said apertured portion of the glass sheets remain susceptible of developing into vents, (5) cooling said shaped glass sheets at a controlled rate of cooling at a sufficiently slow and uniform rate through a temperature range from above to below the annealing range of the glass to avoid establishing temporary tension stresses that would cause said unhealed fissures to develop into vents, yet at a rate through said temperature range sufficient to establish a compression stress layer in the surface of said apertured portion, and laminating said shaped, apertured glass sheets to an interlayer composed of polyurethane or polyvinyl acetal.