Resin coated substrate using a short-set, high-flow melamine-formaldehyde impregnating resin
Assignee: International Paper Co
•
Filing: 1977-03-30
•
Granted: 1978-10-31
•
Expires: 1997-03-30
Abstract
Abstract A substrate is made for use as a top layer in a laminate; the substrate being impregnated with, and having a continuous film on its surface of, a dried, catalyzed, uncured resin, comprising the reaction product of 1 mole of melamine, about 1.8 moles to about 2.7 moles of uninhibited formaldehyde and about 0.05 mole to about 0.40 mole of urea; where the resin content of the substrate is between about 50 wt.% to about 85 wt.%, and the dried, continuous film on the substrate layer will cure within about 30 seconds to about 90 seconds, under pressures of between about 150 psi. to about 500 psi, without the formation of a discontinuous film.
Inventors
- 👤 Harold O. McCaskey, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:28
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/04; B32B21/00; B32B21/10; B32B21/04; B32B21/06; B32B5/00; B32B5/02; C; C08; C08G; C08G12/00; C08G12/02; C08G12/26; C08G12/34; C08G12/36; C08G12/38; C08L; C08L61/00; C08L61/20; C08L61/30; D; D21; D21H; D21H27/00; D21H27/18; D21H27/22; D21H27/26; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; B32B2317/00; B32B2317/12; B32B2317/125; C08L71/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31953; Y10T428/31957; Y10T428/31964; Y10T442/00; Y10T442/20; Y10T442/2738; Y10T442/2746; Y10T442/2754
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
161 words
A resin film coated substrate comprising at least one substrate layer impregnated with resin and having a continuous film on its surface of dried, catalyzed, uncured resin, the resin consisting essentially of the reaction product of 1 mole of melamine, 1.8 moles to 2.7 moles of uninhibited formaldehyde and 0.05 mole to 0.40 mole of urea; the resin, prior to drying, having had a solids content of between about 40 wt.% to about 60 wt.%, a pH of between about 8 to about 10.5 and a water dilutability of between about 85% to about 195%; wherein the resin content of the substrate is between about 50 wt.% to about 85 wt.%, and the dried continuous film on the surface of the substrate layer will cure within about 30 seconds to about 90 seconds, under pressures of between about 150 psi. to about 500 psi., and remain on the surface of the substrate after pressing without the formation of a discontinuous film.
Claim 2
Dependent Claim
161 words
A resin film coated substrate comprising at least one substrate layer impregnated with resin and having a continuous film on its surface of dried, catalyzed, uncured resin, the resin consisting essentially of the reaction product of 1 mole of melamine, 1.8 moles to 2.7 moles of uninhibited formaldehyde and 0.05 mole to 0.40 mole of urea; the resin, prior to drying, having had a solids content of between about 40 wt.% to about 60 wt.%, a pH of between about 8 to about 10.5 and a water dilutability of between about 85% to about 195%; wherein the resin content of the substrate is between about 50 wt.% to about 85 wt.%, and the dried continuous film on the surface of the substrate layer will cure within about 30 seconds to about 90 seconds, under pressures of between about 150 psi. to about 500 psi., and remain on the surface of the substrate after pressing without the formation of a discontinuous film.
Claim 3
Dependent Claim
19 words
The substrate of claim 1, wherein the film thickness is between about 0.0001 inch to about 0.1 inch thick.
Claim 4
Dependent Claim
30 words
The substrate of claim 2, wherein the substrate is material selected from the group consisting of non-woven fabric, woven cloth, glass mat, kraft paper sheet and alpha cellulose paper sheet.
Claim 5
Dependent Claim
48 words
The substrate of claim 2, wherein the reaction product contains about 0.10 wt.% to about 2.0 wt.% based on resin solids of a catalyst effective to increase the rate of cure and about 0.10 wt.% to about 4.0 wt.% of a wetting-agent effective to improve resin impregnating capability.
Claim 6
Dependent Claim
36 words
The substrate of claim 2, wherein the resin coated and impregnated substrate was dried at between about 50° C to about 150° C to a volatile content of between about 5 wt.% to about 15 wt.%.
Claim 7
Dependent Claim
151 words
A resin film coated heat and pressure consolidated laminate, comprising at least one top substrate layer bonded to a porous support; wherein the top substrate layer is impregnated with resin and has a continuous, cured resin film on its top surface, the resin consisting essentially of the cured reaction product of 1 mole of melamine, 1.8 moles to 2.7 moles of uninhibited formaldehyde and 0.05 mole to 0.40 mole of urea; wherein, before curing, the resin content of the substrate layer was between about 50 wt.% to about 85 wt.%, and the resin formed a film on the top surface of the substrate, and wherein the resin was cured during heat and pressure consolidation at between about 150 psi. to about 500 psi. within about 30 seconds to about 90 seconds, and the resin remained on the surface of the substrate after hot pressing without the formation of a discontinuous film.
Claim 8
Dependent Claim
151 words
A resin film coated heat and pressure consolidated laminate, comprising at least one top substrate layer bonded to a porous support; wherein the top substrate layer is impregnated with resin and has a continuous, cured resin film on its top surface, the resin consisting essentially of the cured reaction product of 1 mole of melamine, 1.8 moles to 2.7 moles of uninhibited formaldehyde and 0.05 mole to 0.40 mole of urea; wherein, before curing, the resin content of the substrate layer was between about 50 wt.% to about 85 wt.%, and the resin formed a film on the top surface of the substrate, and wherein the resin was cured during heat and pressure consolidation at between about 150 psi. to about 500 psi. within about 30 seconds to about 90 seconds, and the resin remained on the surface of the substrate after hot pressing without the formation of a discontinuous film.
Claim 9
Dependent Claim
26 words
The laminate of claim 6, wherein the film thickness on the surface of the substrate layer is between about 0.0001 inch to about 0.01 inch thick.
Claim 10
Dependent Claim
32 words
The laminate of claim 7, wherein the substrate layer is a material selected from the group consisting of non-woven fabric, woven cloth, glass mat, kraft paper sheet and alpha cellulose paper sheet.
Claim 11
Dependent Claim
48 words
The laminate of claim 7, wherein the reaction product contains about 0.10 wt.% to about 2.0 wt.% based on resin solids of a catalyst effective to increase the rate of cure and about 0.10 wt.% to about 4.0 wt.% of a wetting-agent effective to improve resin impregnating capability.
Claim 12
Dependent Claim
24 words
The laminate of claim 7 wherein the heat and pressure consolidation was at a temperature of between about 100° C to about 200° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |