Molded plastic article and method of making the same
Assignee: Individual
•
Filing: 1977-09-06
•
Granted: 1978-10-31
•
Expires: 1997-09-06
Abstract
Abstract A composite molded article composed of a backing layer of fiber-reinforced thermosetting resin and an outer layer of a thermoplastic resin which is mechanically interlocked to the backing layer through the fiber reinforcement. In fabrication, a layer of fibrous material impregnated with an uncured thermosetting resin is placed in a mold and a molten thermoplastic resin is injected into the mold. The heat of the thermoplastic resin serves to cure the thermosetting resin and the resulting composite article has a rigid, high strength backing formed of the reinforced thermosetting resin and has a smooth thermoplastic outer surface which is receptive to surface finishes.
Inventors
- 👤 David E. Lawson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:29
CPC Classifications
B; B29; B29C; B29C37/00; B29C37/0078; B29C37/0082; B29C35/00; B29C35/02; B29C37/0025; B29C37/0028; B29C45/00; B29C45/14; B29C45/14778; B29C45/14786; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B29C45/14836; B29C2045/14844; B29K; B29K2101/00; B29K2101/10; B29K2101/12; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0854; B29K2105/12; B29K2105/128; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31786
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
104 words
A method of making a molded composite structure, comprising the steps of placing in a mold cavity a fibrous material impregnated with an uncured thermosetting resin system capable of being cured by the application of heat, and injecting a molten thermoplastic resin into the mold cavity under pressure and at a temperature above the temperature required to cure the thermosetting resin system, the sensible heat of the thermoplastic resin providing heat required to cause the thermosetting resin system to cure to provide a composite structure having a cured thermosetting resin backing layer and a smooth thermoplastic resin outer surface bonded to the backing layer.
Claim 2
Independent Claim
104 words
A method of making a molded composite structure, comprising the steps of placing in a mold cavity a fibrous material impregnated with an uncured thermosetting resin system capable of being cured by the application of heat, and injecting a molten thermoplastic resin into the mold cavity under pressure and at a temperature above the temperature required to cure the thermosetting resin system, the sensible heat of the thermoplastic resin providing heat required to cause the thermosetting resin system to cure to provide a composite structure having a cured thermosetting resin backing layer and a smooth thermoplastic resin outer surface bonded to the backing layer.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein the thermoplastic resin is at a pressure above 10,000 psi.
Claim 4
Dependent Claim
60 words
The method of claim 1, wherein the step of injecting the resin comprises introducing the molten thermoplastic resin into the mold cavity under a first pressure sufficiently low to prevent disruption of the fibrous material to fill the cavity, and thereafter applying a second pressure to the molten thermoplastic resin, said second pressure being substantially greater than the first pressure.
Claim 5
Dependent Claim
74 words
The method of claim 1, wherein the fibrous material comprises a plurality of randomly arranged fibers, and said method includes the step of applying a layer of woven cloth on the exposed surface of the fibrous material prior to injecting the thermoplastic resin into said cavity, said layer serving to protect the fibrous material from the fluid surge of the thermoplastic resin being injected into said cavity and preventing disruption of the fibrous material.
Claim 6
Dependent Claim
34 words
The method of claim 1, wherein said thermosetting resin system is a polyester resin system including a monomer having a boiling point above the temperature of the thermoplastic resin being injected into said mold.
Claim 7
Dependent Claim
15 words
The method of claim 2, wherein said monomer has a boiling point above 250° F.
Claim 8
Dependent Claim
20 words
The method of claim 2, wherein said monomer is selected from the group consisting of diallyl phthalate and divinyl benzene.
Claim 9
Independent Claim
138 words
A method of making a composite structure, comprising the steps of placing in a mold cavity a mass of fibrous material impregnated with an uncured polyester resin system capable of being fully cured by the application of heat, said mass being spaced from a wall of said cavity to produce a space, injecting a heated molten thermoplastic resin into the space in the mold cavity and into contact with said mass, maintaining the temperature of the molten thermoplastic resin at a value below the volatilizing temperature of the components of the resin system, the heated thermoplastic resin being the sole source of heat to effect curing of the polyester resin system and provide a composite structure having a rigid polyester resin backing member and a smooth thermoplastic outer layer, and removing the composite structure from the mold cavity.
Claim 10
Independent Claim
138 words
A method of making a composite structure, comprising the steps of placing in a mold cavity a mass of fibrous material impregnated with an uncured polyester resin system capable of being fully cured by the application of heat, said mass being spaced from a wall of said cavity to produce a space, injecting a heated molten thermoplastic resin into the space in the mold cavity and into contact with said mass, maintaining the temperature of the molten thermoplastic resin at a value below the volatilizing temperature of the components of the resin system, the heated thermoplastic resin being the sole source of heat to effect curing of the polyester resin system and provide a composite structure having a rigid polyester resin backing member and a smooth thermoplastic outer layer, and removing the composite structure from the mold cavity.
Claim 11
Dependent Claim
27 words
The method of claim 8, wherein said fibrous material comprises glass fibers and said monomer is selected from the group consisting of diallyl phthalate and divinyl benzene.
Claim 12
Dependent Claim
21 words
The method of claim 8, including the step of applying a finish coating to the outer surface of the thermoplastic layer.
Claim 13
Dependent Claim
13 words
The method of claim 10, wherein said mass comprises a sheet molding compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |