Reinforced thermoplastic polyester compositions having improved resistance to heat deflection
Assignee: General Electric Co
•
Filing: 1976-12-06
•
Granted: 1978-10-31
•
Expires: 1996-12-06
Abstract
Abstract Reinforced thermoplastic compositions are provided which comprise a high molecular weight polyester resin and a glass fiber reinforcement wherein the glass fibers have a maximum average standard diameter of about 0.0005 inches. The use of such glass fibers improves resistance to deflection by heat of fibrous glass reinforced compositions in comparison with a reinforced composition including glass fibers having an average standard diameter of greater than about 0.0005 inches.
Inventors
- 👤 Allen D. Wambach
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:32
CPC Classifications
C; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08K3/00; C08K3/34; C08K3/40; C08K5/00; C08K5/49
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
91 words
A reinforced thermoplastic composition having improved retention of heat deflection temperature, said composition comprising: (a) a high molecular weight polyester resin; and (b) a reinforcement therefor comprising glass fibers, said glass fibers having an average standard diameter of no greater than about 0.0005 inches, wherein the glass fibers are present in an amount at least sufficient to provide reinforcement and to improve the resistance to deflection by heat of said composition in comparison with a reinforced composition including glass fibers having an average standard diameter of greater than about 0.0005 inches.
Claim 2
Dependent Claim
91 words
A reinforced thermoplastic composition having improved retention of heat deflection temperature, said composition comprising: (a) a high molecular weight polyester resin; and (b) a reinforcement therefor comprising glass fibers, said glass fibers having an average standard diameter of no greater than about 0.0005 inches, wherein the glass fibers are present in an amount at least sufficient to provide reinforcement and to improve the resistance to deflection by heat of said composition in comparison with a reinforced composition including glass fibers having an average standard diameter of greater than about 0.0005 inches.
Claim 3
Dependent Claim
25 words
A composition as defined in claim 1 wherein said glass fibers have an average standard diameter in the range of 0.00010 to about 0.00040 inches.
Claim 4
Dependent Claim
33 words
A composition as defined in claim 1 wherein said glass fibers are present in an amount of from about 1 to about 60% by weight of the combined weights of (a) and (b).
Claim 5
Dependent Claim
38 words
A composition as defined in claim 1 wherein said polyester has an intrinsic viscosity of at least about 0.4 deciliters per gram when measured in a solution in a 60:40 mixture of phenol and trichloroethane at 30° C.
Claim 6
Dependent Claim
38 words
A composition as defined in claim 4 wherein said polyester has an intrinsic viscosity of at least about 0.7 deciliters per gram when measured in a solution in a 60:40 mixture of phenol and trichloroethane at 30° C.
Claim 7
Dependent Claim
46 words
A composition as defined in claim 1 wherein said polyester is selected from the group consisting of polymeric glycol terephthalate and isophthalate esters having repeating units of the formula: ##STR6## wherein n is a whole number of from 2 to 4, and mixture of such esters.
Claim 8
Dependent Claim
18 words
A composition as defined in claim 6 wherein said polyester resin is in admixture with a homopolycarbonate resin.
Claim 9
Dependent Claim
13 words
A composition as defined in claim 6 wherein said polyester is polyethylene terephthalate.
Claim 10
Dependent Claim
19 words
A composition as defined in claim 6 wherein said polyester is linear poly(1,4-butylene terephthalate) or a branched copolyester thereof.
Claim 11
Dependent Claim
35 words
A composition as defined in claim 6 wherein said branched copolyester is a high melt viscosity poly(1,4-butylene terephthalate) resin which includes a small amount of a branching component containing at least three ester forming groups.
Claim 12
Dependent Claim
20 words
A composition as defined in claim 1 wherein the reinforcement (b) includes a reinforcing amount of a mineral reinforcing filler.
Claim 13
Dependent Claim
14 words
A composition as defined in claim 11 wherein said mineral reinforcing filler is talc.
Claim 14
Dependent Claim
19 words
A composition as defined in claim 1 which also includes a flame retardant amount of a flame retardant additive.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |