Assignee: OBrien Corp
•
Filing: 1977-02-28
•
Granted: 1978-10-31
•
Expires: 1997-02-28
Abstract
Abstract The present invention relates to curing agents for epoxy resins. More particularly, the present invention relates to water soluble or water-dispersible curing agents which are mixed with water dispersed or water emulsified epoxy resins to form coating compositions which are essentially free of volatile organic solvents or cosolvents and which have extended pot life at room temperature, but which cure under ambient conditions in less than 24 hours.
Inventors
- 👤 Ivar P. Thomassen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:29
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08G59/56; C08G59/58; C08G59/182; C08G59/184; C08G59/62; C08G59/64
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
136 words
A water-dispersible or water-soluble curing agent having a pot-life of between about 2-12 hours for epoxy resins for producing a curing reaction under ambient conditions on a structural surface which curing agent comprises a mixture of water and the hyroxylated amido-poly amine terminated reaction product of an aliphatic polyepoxide, an aliphatic polyamine having at least one primary amine and a polyfunctional carboxylic acid, said amine terminated reaction product having an amine value of from about 150 to about 800, a molecular weight of from about 280 to about 1500, from two to about ten hydroxyl groups per molecule and being essentially free of unreacted carboxylic acid groups and water, said curing agent being substantially free of organic solvents, cosolvents and emulsifiers, said mixture of water and amine terminated reaction product having a pH about about 9.0.
Claim 2
Dependent Claim
136 words
A water-dispersible or water-soluble curing agent having a pot-life of between about 2-12 hours for epoxy resins for producing a curing reaction under ambient conditions on a structural surface which curing agent comprises a mixture of water and the hyroxylated amido-poly amine terminated reaction product of an aliphatic polyepoxide, an aliphatic polyamine having at least one primary amine and a polyfunctional carboxylic acid, said amine terminated reaction product having an amine value of from about 150 to about 800, a molecular weight of from about 280 to about 1500, from two to about ten hydroxyl groups per molecule and being essentially free of unreacted carboxylic acid groups and water, said curing agent being substantially free of organic solvents, cosolvents and emulsifiers, said mixture of water and amine terminated reaction product having a pH about about 9.0.
Claim 3
Dependent Claim
65 words
A curing agent in accordance with claim 1 wherein said reaction product comprises the reaction of at least 2 amine equivalents of said aliphatic polyamine for each epoxy equivalent of said aliphatic polyepoxide and up to 4 carboxylic acid equivalents from said polyfunctional carboxylic acid, the number of said amine equivalents exceeding the number of carboxylic acid equivalents sufficiently to produce an amine terminated product.
Claim 4
Dependent Claim
30 words
A curing agent in accordance with claim 1 wherein said polyfunctional carboxylic acid is reacted with said polyamine as a first step, followed by the reaction with said aliphatic polyepoxide.
Claim 5
Dependent Claim
30 words
A curing agent in accordance with claim 1 wherein said polyamine is reacted with said aliphatic polyepoxide as a first step, followed by the reaction with said polyfunctional carboxylic acid.
Claim 6
Dependent Claim
33 words
A curing agent in accordance with claim 3, wherein at least 2 amine equivalents of the amine-acid reaction product of the first step is reacted with one epoxide equivalent of said aliphatic polyepoxide.
Claim 7
Dependent Claim
32 words
A curing agent in accordance with claim 3, wherein said first step comprises reacting at least 2 amine equivalents of said aliphatic polyamine for each acid equivalent of said polyfunctional carboxylic acid.
Claim 8
Dependent Claim
33 words
A curing agent in accordance with claim 6, wherein at least 2 amine equivalents of the amine-acid reaction product of the first step is reacted with one epoxide equivalent of said aliphatic polyepoxide.
Claim 9
Dependent Claim
32 words
A curing agent in accordance with claim 6, wherein about 2.5 amine equivalents of the amine-acid reaction product of the first step is reacted with one epoxide equivalent of said aliphatic polyepoxide.
Claim 10
Dependent Claim
31 words
A curing agent in accordance with claim 4, wherein said first step comprises reacting at least 2 amine equivalents of said aliphatic polyamine for each epoxide equivalent of said aliphatic polyepoxide.
Claim 11
Dependent Claim
30 words
A curing agent in accordance with claim 4, wherein said first step comprises reacting about 2.5 amine equivalents of said aliphatic polyamine for each epoxide equivalent of said aliphatic polyepoxide.
Claim 12
Dependent Claim
33 words
A curing agent in accordance with claim 9, wherein at least 2 amine equivalents of the reaction product of the first step are reacted with each acid equivalent of the polyfunctional carboxylic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |