US4123299A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing silicon-iron sheet materal, and product
Assignee: General Electric Co
•
Filing: 1978-09-29
•
Granted: 1978-10-31
•
Expires: 1998-09-29
Abstract
Abstract The magnetic properties of silicon-iron are improved by adding tin, and by both adding tin and lowering the sulfur content the weld brittleness is reduced in addition to improving the magnetic properties.
Inventors
- 👤 Howard C. Fiedler
- 👤 Joseph T. Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:34
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; C; C22; C22C; C22C38/00; C22C38/02; H01F1/14783
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
129 words
The method of producing grain oriented silicon-iron sheet which comprises the steps of providing a silicon-iron melt containing 2.2 to 4.5 percent silicon, between about three and 35 parts per million boron, between about 30 and 75 parts per million nitrogen in the ratio to boron of 1 to 15 parts per part of boron, from 0.02 to 0.05 percent manganese, 0.005 to 0.025 percent sulfur and tin in amounts ranging from 0.01 to 0.10 percent, casting the melt and hot rolling the resulting billet to form an elongated sheet-like body, cold rolling the hot rolled body to provide a sheet of final gauge thickness, and subjecting the resulting cold-rolled sheet to a final heat treatment to decarburize it and to develop (110) [001] secondary recrystallization texture in it.
Claim 2
Independent Claim
129 words
The method of producing grain oriented silicon-iron sheet which comprises the steps of providing a silicon-iron melt containing 2.2 to 4.5 percent silicon, between about three and 35 parts per million boron, between about 30 and 75 parts per million nitrogen in the ratio to boron of 1 to 15 parts per part of boron, from 0.02 to 0.05 percent manganese, 0.005 to 0.025 percent sulfur and tin in amounts ranging from 0.01 to 0.10 percent, casting the melt and hot rolling the resulting billet to form an elongated sheet-like body, cold rolling the hot rolled body to provide a sheet of final gauge thickness, and subjecting the resulting cold-rolled sheet to a final heat treatment to decarburize it and to develop (110) [001] secondary recrystallization texture in it.
Claim 3
Dependent Claim
41 words
The method of claim 1 in which the manganese content of the melt is about 0.025 percent, the sulfur content of the melt is about 0.012 percent and the tin content of the melt is between about 0.010 and 0.050 percent.
Claim 4
Dependent Claim
32 words
The method of claim 1 in which the melt contains between about 0.02 and 0.03 percent manganese, between about 0.009 and 0.014 percent sulfur and between about 0.020 and 0.050 percent tin.
Claim 5
Dependent Claim
31 words
The method of claim 1 in which the melt contains between about 0.030 and 0.040 percent manganese, between about 0.013 and 0.019 percent sulfur and between 0.020 and 0.050 percent tin.
Claim 6
Dependent Claim
60 words
The method of claim 1 in which the melt contains about 0.026 percent manganese, about 0.013 percent sulfur and about 0.02 percent tin, and in which in preparation for the final heat treatment step the cold-rolled silicon-iron sheet is provided with an electrically-insulating adherent coating containing about 15 parts per million boron on the basis of the said silicon-iron sheet.
Claim 7
Dependent Claim
60 words
The method of claim 1 in which the melt contains about 0.024 percent manganese, about 0.008 percent sulfur and about 0.097 percent tin, and in which in preparation for the final heat treatment step the cold-rolled silicon-iron sheet is provided with an electrically-insulating adherent coating containing about 12 parts per million boron on the basis of the said silicon-iron sheet.
Claim 8
Dependent Claim
64 words
A cold-rolled silicon-iron sheet product containing 2.2 to 4.5 percent silicon, between about three and 35 parts per million boron, between about 30 and 75 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, from 0.02 to 0.05 percent manganese, 0.005 to 0.025 percent sulfur and tin in amounts ranging from 0.010 to 0.10 percent.
Claim 9
Dependent Claim
64 words
A cold-rolled silicon-iron sheet product containing 2.2 to 4.5 percent silicon, between about three and 35 parts per million boron, between about 30 and 75 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, from 0.02 to 0.05 percent manganese, 0.005 to 0.025 percent sulfur and tin in amounts ranging from 0.010 to 0.10 percent.
Claim 10
Dependent Claim
30 words
The cold-rolled sheet of claim 7 in which the manganese content is about 0.025 percent, the sulfur content is about 0.013 percent, and the tin content is about 0.05 percent.
Claim 11
Dependent Claim
30 words
The cold-rolled sheet of claim 7 in which the manganese content is about 0.035 percent, the sulfur content is about 0.017 percent and the tin content is about 0.05 percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |