Method of separating ferritic steel or ductile iron from certain nonferrous metals
Assignee: Rolls Royce Corp
•
Filing: 1977-01-28
•
Granted: 1978-10-31
•
Expires: 1997-01-28
Abstract
Abstract A method is disclosed for treating scrap metal chips and turnings containing a valuable metal layer of silver, gold, or copper and a ductile layer of ferritic steel or ductile iron to recover the valuable metal. The chips and turnings are treated by carburization and quenching to embrittle the steel layers and then crushed converting the steel to a small mesh powder which can be screened from larger sized agglomerates of valuable metal insensitive to the embrittling process.
Inventors
- 👤 Dean K. Hanink
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:16
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/78; C22; C22B; C22B1/00; C22B1/005; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
181 words
A method of treating a composite comprising a layered portion of a nonferrous metal taken from the group consisting of silver, silver alloys, gold, gold alloys, copper and copper alloys bonded to a layered portion of iron or low carbon steel wherein the ferrous layer can be through carburized to substantially separate the nonferrous metal from the ferrous metal comprising; heating the composite material in a carburizing environment at a temperature above the austenitic transformation temperature of said ferrous metal portion until sufficient carbon has diffused into the ferrous metal portion to render it through hardenable, quenching the composite from a temperature above the austenitic temperature of the carburized ferrous metal portion to a temperature below the transformation temperature of the ferrous metal portion to convert said portion to martensite, subjecting said composite to a comminuting operation which substantially breaks the hardened ferrous metal portion away from the nonferrous portion reducing the hardened ferrous portion to particles that are smaller in size than comminution products of unhardened nonferrous portion, and separating the ferrous metal particles from the nonferrous metal comminution products.
Claim 2
Independent Claim
181 words
A method of treating a composite comprising a layered portion of a nonferrous metal taken from the group consisting of silver, silver alloys, gold, gold alloys, copper and copper alloys bonded to a layered portion of iron or low carbon steel wherein the ferrous layer can be through carburized to substantially separate the nonferrous metal from the ferrous metal comprising; heating the composite material in a carburizing environment at a temperature above the austenitic transformation temperature of said ferrous metal portion until sufficient carbon has diffused into the ferrous metal portion to render it through hardenable, quenching the composite from a temperature above the austenitic temperature of the carburized ferrous metal portion to a temperature below the transformation temperature of the ferrous metal portion to convert said portion to martensite, subjecting said composite to a comminuting operation which substantially breaks the hardened ferrous metal portion away from the nonferrous portion reducing the hardened ferrous portion to particles that are smaller in size than comminution products of unhardened nonferrous portion, and separating the ferrous metal particles from the nonferrous metal comminution products.
Claim 3
Independent Claim
175 words
A method of treating composite particles comprising scrap chips or turnings that contain a layer of a nonferrous metal taken from the group consisting of silver, silver alloys, gold, gold alloys, copper and copper alloys bonded to a layer of iron or low carbon steel to substantially separate the nonferrous metal from the ferrous metal comprising; heating the particles in a carburizing environment at a temperature above the austenitic transformation temperature of said ferrous metal layers until sufficient carbon has diffused therein to render them through hardenable, quenching the particles from a temperature above the austenitic temperature of the carburized ferrous metal layers to a temperature below the transformation temperature of the ferrous metal layers to convert them to martensite, subjecting said particles to a comminuting operation which substantially breaks the martensitic ferrous metal layers away from the nonferrous layers and reducing the hardened ferrous layers to fine particles and agglomerating the ductile nonferrous layer into particles substantially larger than the ferrous metal particles, and separating the ferrous metal particles from the nonferrous metal particles.
Claim 4
Independent Claim
175 words
A method of treating composite particles comprising scrap chips or turnings that contain a layer of a nonferrous metal taken from the group consisting of silver, silver alloys, gold, gold alloys, copper and copper alloys bonded to a layer of iron or low carbon steel to substantially separate the nonferrous metal from the ferrous metal comprising; heating the particles in a carburizing environment at a temperature above the austenitic transformation temperature of said ferrous metal layers until sufficient carbon has diffused therein to render them through hardenable, quenching the particles from a temperature above the austenitic temperature of the carburized ferrous metal layers to a temperature below the transformation temperature of the ferrous metal layers to convert them to martensite, subjecting said particles to a comminuting operation which substantially breaks the martensitic ferrous metal layers away from the nonferrous layers and reducing the hardened ferrous layers to fine particles and agglomerating the ductile nonferrous layer into particles substantially larger than the ferrous metal particles, and separating the ferrous metal particles from the nonferrous metal particles.
Claim 5
Independent Claim
160 words
A method of treating particles that contain a silver portion bonded to a steel portion such as are produced as offal in the manufacture of steel backed silver bearings to substantially separate the silver from the steel comprising; heating the particles in a gas carburizing environment at a temperature above the austenitic transformation temperature of the steel portions until sufficient carbon has diffused into the steel portions of said particles to render the steel portions through hardenable, quenching the particles from a temperature above the austenitic temperature of the carburized ferrous metal portions to a temperature below the transformation temperature of the steel portions to convert said steel portions to martensite, subjecting said particles to a comminuting operation which substantially breaks the martensitic steel portions away from the nonferrous portions reducing the steel portions to fine particles and agglomerating the ductile nonferrous portions into particles substantially larger than the steel particles, and separating the steel particles from the silver particles.
Claim 6
Independent Claim
160 words
A method of treating particles that contain a silver portion bonded to a steel portion such as are produced as offal in the manufacture of steel backed silver bearings to substantially separate the silver from the steel comprising; heating the particles in a gas carburizing environment at a temperature above the austenitic transformation temperature of the steel portions until sufficient carbon has diffused into the steel portions of said particles to render the steel portions through hardenable, quenching the particles from a temperature above the austenitic temperature of the carburized ferrous metal portions to a temperature below the transformation temperature of the steel portions to convert said steel portions to martensite, subjecting said particles to a comminuting operation which substantially breaks the martensitic steel portions away from the nonferrous portions reducing the steel portions to fine particles and agglomerating the ductile nonferrous portions into particles substantially larger than the steel particles, and separating the steel particles from the silver particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |