Method of treating steel strip and sheet surfaces, in sulfur-bearing atmosphere, for metallic coating
Assignee: Armco Inc
•
Filing: 1976-12-23
•
Granted: 1978-10-31
•
Expires: 1996-12-23
Abstract
Abstract A method of preparing the surfaces of steel strip and sheet stock for fluxless hot dip coating with molten metal by passing the stock through a first heating zone containing the hot gaseous products of combustion of a sulfur-bearing gaseous fuel with air, continuing the heating in a further heating zone, and cooling the stock approximately to the temperature of the molten coating metal in a reducing atmosphere. The radiant energy absorptivity of the stock is increased by forming a visible sulfur and oxygen rich layer thereon in the first heating zone and preserving the layer throughout the further heating zone. Coke oven gas may be used as fuel in the first heating zone.
Inventors
- 👤 Jerry L. Arnold
- 👤 Frank C. Dunbar
- 👤 Alan F. Gibson
- 👤 Marvin B. Pierson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:52
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/34; C23C2/36; C23C2/38
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
219 words
A method of preparing the sufaces of steel strip and sheet stock for fluxless hot dip coating with molten metal, comprising the steps of passing the stock through a furnace heated by direct combustion with air of gaseous fuel containing sulfur compounds ranging from about 5 to about 1600 grains of sulfur per 100 cubic feet of fuel to produce an atmosphere of gaseous products of combustion containing sulfur and from about 2% free oxygen by volume to about 2% by volume excess combustibles in the form of carbon monoxide and hydrogen in which atmosphere said stock is heated to about 540° to about 705° C., thereby causing the formation of a visible sulfur and oxygen rich layer on the stock surfaces, continuing the heating of said stock in a further heating zone isolated from said furnace in an atmosphere consisting of a gas inert to said sulfur and oxygen rich layer and less than 5% hydrogen by volume, thereby preserving said layer, and cooling said stock approximately to the temperature of the molten coating metal in a cooling zone isolated from said heating zones, said cooling zone containing a reducing atmosphere comprising at least 10% hydrogen by volume, whereby to reduce said sulfur and oxygen rich layer completely to a metallic iron surface wettable by said coating metal.
Claim 2
Independent Claim
219 words
A method of preparing the sufaces of steel strip and sheet stock for fluxless hot dip coating with molten metal, comprising the steps of passing the stock through a furnace heated by direct combustion with air of gaseous fuel containing sulfur compounds ranging from about 5 to about 1600 grains of sulfur per 100 cubic feet of fuel to produce an atmosphere of gaseous products of combustion containing sulfur and from about 2% free oxygen by volume to about 2% by volume excess combustibles in the form of carbon monoxide and hydrogen in which atmosphere said stock is heated to about 540° to about 705° C., thereby causing the formation of a visible sulfur and oxygen rich layer on the stock surfaces, continuing the heating of said stock in a further heating zone isolated from said furnace in an atmosphere consisting of a gas inert to said sulfur and oxygen rich layer and less than 5% hydrogen by volume, thereby preserving said layer, and cooling said stock approximately to the temperature of the molten coating metal in a cooling zone isolated from said heating zones, said cooling zone containing a reducing atmosphere comprising at least 10% hydrogen by volume, whereby to reduce said sulfur and oxygen rich layer completely to a metallic iron surface wettable by said coating metal.
Claim 3
Dependent Claim
22 words
The method claimed in claim 1, wherein said stock is heated to about 675° to 925° C. in said further heating zone.
Claim 4
Dependent Claim
16 words
The method claimed in claim 1, wherein said further heating zone is a radiant tube furnace.
Claim 5
Dependent Claim
14 words
The method claimed in claim 1, wherein said gaseous fuel is coke oven gas.
Claim 6
Dependent Claim
48 words
The method claimed in claim 1, including the step of holding said stock at a selected lower temperature in a control zone in a reducing atmosphere containing at least 10% hydrogen by volume after passing through said further heating zone and prior to the cooling of said stock.
Claim 7
Independent Claim
225 words
A method of preparing the surfaces of steel strip and sheet stock for fluxless hot dip coating with molten coating metal, comprising the steps of passing the stock through a furnace heated by direct combustion with air of gaseous fuel containing sulfur compounds ranging from about 5 to about 1600 grains of sulfur per 100 cubic feet of fuel to produce an atmosphere of gaseous products of combustion containing sulfur and from about 2% free oxygen by volume to about 2% by volume excess combustibles in the form of carbon monoxide and hydrogen in which atmosphere said stock is heated to about 370° to 485° C., passing said stock into outside atmosphere, thereby causing the formation of a visible sulfur and oxygen rich layer on the stock surfaces, continuing the heating of said stock in a further heating zone isolated from said furnace in an atmosphere consisting of a gas inert to said sulfur and oxygen rich layer and less than 5% hydrogen by volume, thereby preserving said layer, and cooling said stock approximately to the temperature of the molten coating metal in a cooling zone isolated from said heating zones, said cooling zone containing a reducing atmosphere comprising at least 10% hydrogen by volume, whereby to reduce said sulfur and oxygen rich layer completely to a metallic iron surface wettable by said coating metal.
Claim 8
Independent Claim
225 words
A method of preparing the surfaces of steel strip and sheet stock for fluxless hot dip coating with molten coating metal, comprising the steps of passing the stock through a furnace heated by direct combustion with air of gaseous fuel containing sulfur compounds ranging from about 5 to about 1600 grains of sulfur per 100 cubic feet of fuel to produce an atmosphere of gaseous products of combustion containing sulfur and from about 2% free oxygen by volume to about 2% by volume excess combustibles in the form of carbon monoxide and hydrogen in which atmosphere said stock is heated to about 370° to 485° C., passing said stock into outside atmosphere, thereby causing the formation of a visible sulfur and oxygen rich layer on the stock surfaces, continuing the heating of said stock in a further heating zone isolated from said furnace in an atmosphere consisting of a gas inert to said sulfur and oxygen rich layer and less than 5% hydrogen by volume, thereby preserving said layer, and cooling said stock approximately to the temperature of the molten coating metal in a cooling zone isolated from said heating zones, said cooling zone containing a reducing atmosphere comprising at least 10% hydrogen by volume, whereby to reduce said sulfur and oxygen rich layer completely to a metallic iron surface wettable by said coating metal.
Claim 9
Dependent Claim
22 words
The method claimed in claim 6, wherein said stock is heated to about 735° to 925° C. in said further heating zone.
Claim 10
Dependent Claim
173 words
In a method of preparing the surfaces of steel strip and sheet stock for fluxless hot dip coating with molten metal, including the steps of passing the stock through a first heating zone under conditions which form a visible iron oxide layer on the stock surfaces, continuing the heating of said stock in a further heating zone in a reducing atmosphere to reduce said oxide layer to a metallic iron surface, and cooling said stock approximately to the temperature of the molten coating metal in a protective reducing atmosphere to maintain said iron surface, the improvement which comprises forming a visible sulfur and oxygen rich layer on said stock surfaces in said first-mentioned heating zone to increase the radiant energy absorptivity of said stock, preserving said layer throughout said further heating zone by maintaining thereon an atmosphere inert to said layer, and thereafter reducing said layer to a metallic iron surface wettable by said coating metal in a reducing atmosphere containing at least 10% by volume hydrogen during said cooling of said stock.
Claim 11
Dependent Claim
173 words
In a method of preparing the surfaces of steel strip and sheet stock for fluxless hot dip coating with molten metal, including the steps of passing the stock through a first heating zone under conditions which form a visible iron oxide layer on the stock surfaces, continuing the heating of said stock in a further heating zone in a reducing atmosphere to reduce said oxide layer to a metallic iron surface, and cooling said stock approximately to the temperature of the molten coating metal in a protective reducing atmosphere to maintain said iron surface, the improvement which comprises forming a visible sulfur and oxygen rich layer on said stock surfaces in said first-mentioned heating zone to increase the radiant energy absorptivity of said stock, preserving said layer throughout said further heating zone by maintaining thereon an atmosphere inert to said layer, and thereafter reducing said layer to a metallic iron surface wettable by said coating metal in a reducing atmosphere containing at least 10% by volume hydrogen during said cooling of said stock.
Claim 12
Dependent Claim
29 words
The improvement claimed in claim 8, including the step of holding said stock at a selected lower temperature after said further heating zone and prior to the cooling thereof.
References Cited (Backward Citations)
US1141770A
Cited
US1672180A
Cited
US2110893A
Cited
US2197622A
Cited
GB701685A
Cited
US3936543A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |